Multilayer mixed oxide supported catalyst for oxidative coupling of methane

Patent metadata

Field	Value
Publication number	US-11633721-B2
Application number	US-202017769879-A
Country	US
Kind code	B2
Filing date	Sep 21, 2020
Priority date	Oct 22, 2019
Publication date	Apr 25, 2023
Grant date	Apr 25, 2023

Abstract

A multilayer supported oxidative coupling of methane (OCM) catalyst composition (support, first single oxide layer, one or more mixed oxide layers, optional second single oxide layer) characterized by formula A a Z b E c D d O x /support; A is alkaline earth metal; Z is first rare earth element; E is second rare earth element; D is redox agent/third rare earth element; the first, second, third rare earth element are not the same; a=1.0; b=0.1-10.0; c=0.1-10.0; d=0-10.0; x balances oxidation states; first single oxide layer (Z b1 O x1 , b1=0.1-10.0; x1 balances oxidation states) contacts support and one or more mixed oxide layers; one or more mixed oxide layers (A a2 Z b2 E c2 D d2 O x2 , a2=1.0; b2=0.1-10.0; c2=0.1-10.0; d2=0-10.0; x2 balances oxidation states; A a Z b E c D d O x and A a2 Z b2 E c2 D d2 O x2 are different) contacts first single oxide layer and optionally second single oxide layer, and second single oxide layer (AO), when present, contacts one or more mixed oxide layers and optionally first single oxide layer.

First claim

What is claimed is:

1. A multilayer supported oxidative coupling of methane (OCM) catalyst composition characterized by the general formula A a Z b E c D d O x /support, wherein the multilayer supported OCM catalyst composition comprises a support, a first single oxide layer, one or more mixed oxide layers, and an optional second single oxide layer;
wherein A is an alkaline earth metal; wherein Z is a first rare earth element; wherein E is a second rare earth element; wherein D is a redox agent or a third rare earth element; wherein the first rare earth element, the second rare earth element, and the third rare earth element, when present, are not the same; wherein a is 1.0; wherein b is from about 0.1 to about 10.0; wherein c is from about 0.1 to about 10.0; wherein d is from about 0 to about 10.0; wherein x balances the oxidation states;
wherein the first single oxide layer contacts the support and the one or more mixed oxide layers, wherein the first single oxide layer is characterized by the general formula Z b1 O x1 , wherein b1 is from about 0.1 to about 10.0; and wherein x1 balances the oxidation states;
wherein the one or more mixed oxide layers contacts the first single oxide layer and optionally the second single oxide layer, wherein the one or more mixed oxide layers is characterized by the general formula A a2 Z b2 E c2 D d2 O x2 , wherein a2 is 1.0; wherein b2 is from about 0.1 to about 10.0; wherein c2 is from about 0.1 to about 10.0; wherein d2 is from about 0 to about 10.0; wherein x2 balances the oxidation states; wherein the general formula A a Z b E c D d O x and the general formula A a2 Z b2 E c2 D d2 O x2 are different;
wherein the second single oxide layer, when present, contacts the one or more mixed oxide layers and optionally the first single oxide layer, and wherein the second single oxide layer is characterized by the general formula AO.

2. The multilayer supported OCM catalyst composition of claim 1 , wherein the alkaline earth metal is selected from the group consisting of magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), and combinations thereof.

3. The multilayer supported OCM catalyst composition of claim 1 , wherein the first rare earth element, the second rare earth element, and the third rare earth element can each independently be selected from the group consisting of lanthanum (La), scandium (Sc), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), yttrium (Y), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), lutetium (Lu), and combinations thereof.

4. The multilayer supported OCM catalyst composition of claim 1 , wherein the redox agent is selected from the group consisting of manganese (Mn), tungsten (W), bismuth (Bi), antimony (Sb), tin (Sn), cerium (Ce), praseodymium (Pr), and combinations thereof.

5. The multilayer supported OCM catalyst composition of claim 1 , wherein the first single oxide layer comprises La 2 O 3 .

6. The multilayer supported OCM catalyst composition of claim 1 , wherein the second single oxide layer comprises SrO.

7. The multilayer supported OCM catalyst composition of claim 1 , wherein the one or more mixed oxide layers has the general formula Sr a2 La b2 Yb c2 Nd d2 O x2 ; wherein a2 is 1.0; wherein b2 is from about 0.1 to about 10.0; wherein c2 is from about 0.1 to about 10.0; wherein d2 is from about 0 to about 10.0; and wherein x2 balances the oxidation states.

8. The multilayer supported OCM catalyst composition of claim 1 , wherein the support is selected from the group consisting of alumina (Al 2 O 3 ), silica (SiO 2 ), silica (SiO 2 )-alumina (Al 2 O 3 ), silicon carbide (SiC), zirconia (ZrO 2 ), titania (TiO 2 ), magnesium oxide (MgO), zeolites, transition metal oxides, alkali metal oxides, alkaline earth metal oxides, lanthanide oxides, actinide oxides, carbon, and combinations thereof.

9. The multilayer supported OCM catalyst composition of claim 1 , wherein the support has a surface area in a range of from greater than 0 m 2 /g and less than about 20.0 m 2 /g, as determined by measuring nitrogen adsorption according to the Brunauer, Emmett and Teller (BET) method.

10. The multilayer supported OCM catalyst composition of claim 1 , wherein the support has a total pore volume in a range of from about 0.1 cc/g to about 1.0 cc/g, as determined by measuring nitrogen adsorption according to the BET method.

11. The multilayer supported OCM catalyst composition of claim 1 , wherein the support has a pore size distribution in a range of from about 0.01 microns to about 500 microns, as determined by measuring nitrogen adsorption according to the BET method.

12. The multilayer supported OCM catalyst composition of claim 1 , wherein the weight ratio of A a Z b E c D d O x to the support is in a range of from about 0.01 to about 5.0.

13. The multilayer supported OCM catalyst composition of claim 1 , wherein (1) the first single oxide layer is characterized by a thickness of from about 0.001 μm to about 100 μm, (2) the one or more mixed oxide layers is characterized by a thickness of from about 0.002 μm to about 250 μm, (3) the second single oxide layer is characterized by a thickness of from about 0.001 μm to about 50 μm, or (4) any combinations of (1)-(3).

14. A method of making a multilayer supported oxidative coupling of methane (OCM) catalyst composition comprising:
(a) contacting a support with a first OCM catalyst precursor mixture to form a first supported OCM catalyst precursor, wherein the first OCM catalyst precursor mixture comprises one or more compounds comprising a first rare earth element cation (Z);
(b) calcining at least a portion of the first supported OCM catalyst precursor at a temperature of equal to or greater than about 500° C. to form a first calcined supported OCM catalyst precursor, wherein the first calcined supported OCM catalyst precursor comprises the support and a first single oxide layer, wherein the first single oxide layer contacts the support, wherein the first single oxide layer is characterized by the general formula Z b1 O x1 , and wherein b1 is from about 0.1 to about 10.0; and wherein x1 balances the oxidation states;
(c) contacting at least a portion of the first calcined supported OCM catalyst precursor with a second OCM catalyst precursor mixture to form a second supported OCM catalyst precursor, wherein the second OCM catalyst precursor mixture comprises one or more compounds comprising an alkaline earth metal cation, one or more compounds comprising the first rare earth element cation (Z), one or more compounds comprising a second rare earth element cation (E), and one or more compounds comprising a redox agent cation or a third rare earth element cation (D); wherein the first rare earth element cation, the second rare earth element cation, and the third rare earth element cation, when present, are not the same; wherein the second OCM catalyst precursor mixture is characterized by a molar ratio of first rare earth element to alkaline earth metal of b2:1, wherein b2 is from about 0.1 to about 10.0; wherein the second OCM catalyst precursor mixture is characterized by a molar ratio of second rare earth element to alkaline earth metal of c2:1, wherein c2 is from about 0.1 to about 10.0; and wherein the second OCM catalyst precursor mixture is characterized by a molar ratio of redox agent or third rare earth element to alkaline earth metal of d2:1, wherein d2 is from about 0 to about 10.0; and
(d) calcining at least a portion of the second supported OCM catalyst precursor at a temperature of equal to or greater than about 500° C. to form the

Assignees

• Sabic Global Technologies Bv

Inventors

• Liang Wugeng
• Li Luanyi
• Perez Hector
• Gautam Pankaj
• West David

Classifications

• Y02P20/52

  using catalysts, e.g. selective catalysts · CPC title

• C07C2521/12

  Silica and alumina · CPC title

• B01J2523/00

  Constitutive chemical elements of heterogeneous catalysts · CPC title

• B01J23/10 Primary

  of rare earths · CPC title

• C07C2523/10

  of rare earths · CPC title