Method for preparing unbleached biomechanical pulp from straw

Patent metadata

Field	Value
Publication number	US-11624154-B2
Application number	US-201916954275-A
Country	US
Kind code	B2
Filing date	Apr 29, 2019
Priority date	Dec 29, 2018
Publication date	Apr 11, 2023
Grant date	Apr 11, 2023

Abstract

A method for preparing unbleached biomechanical pulp from straw. A straw is used as a raw material, which is treated with alkaline biological enzymes, heated with hot alkali steam, refined, and washed. The mechanical pulp prepared by the method of the present invention has significantly improved ring-crush strength, can be used to prepare corrugated paper or cardboard paper, and can significantly improve the compressive strength of the carton.

First claim

What is claimed is:

1. A method for preparing an unbleached biomechanical pulp from straw, comprising the following steps:
(1) cutting physically selected dedusted air-dried straw into 3-6 cm long pieces of straw;
(2) transferring the straw cut in Step (1) to a treatment vessel or reactor, and treating with one or more compound enzymes having activity under alkaline conditions at a solid/liquid ratio of 1:4-1:8 W/V, wherein during the treatment with the one or more compound enzymes, alkali is added so that the straw is controlled to pH 7-10, and the treatment time is controlled to 30-90 min;
(3) removing the straw treated in Step (2) and further treating with steam under alkaline conditions at a temperature of 100-120° C.;
(4) refining the straw treated in Step (3) in one or more stages so that a beating degree is 25-55° SR;
(5) washing with water after the refining to obtain a biomechanical pulp, after the washing, a filtrate containing the water is treated with a multi-purpose evaporator, and optionally (1) solid residue is recovered for incineration in a boiler and (2) heat energy is recovered for use in forming heated water or steam; and
(6) defibrating the biomechanical pulp by a defibrater and evenly mixing.

2. The method according to claim 1 , wherein the one or more compound enzymes used in Step (2) include a compound enzyme of alkaline xylanase, alkaline cellulase, and alkaline pectinase, wherein a ratio of enzyme activity of the alkaline xylanase, alkaline cellulase and alkaline pectinase is 8-12:3-5:1.5-3.

3. The method according to claim 1 , wherein the amount of alkali added in Step (2) is 0.5%-3% by weight of a content of the treatment vessel or reactor.

4. The method according to claim 1 , wherein the alkali is NaOH or KOH.

5. The method according to claim 1 , wherein the treatment temperature in Step (2) is 45-60° C.

6. The method according to claim 1 , wherein the treatment time with the steam in Step (3) is 10-60 min.

7. The method according to claim 1 , wherein in the treatment with the steam in Step (3), the pH is 9-14.

8. The method according to claim 1 , wherein the physically selected dedusted air-dried straw is physically selected dedusted air-dried wheat straw.

Assignees

• Univ Qilu Technology

Inventors

• Chen Jiachuan
• Ji Xingxiang
• Yang Guihua
• Tian Zhongjian
• Wang Ruiming
• Guo Yuqian

Classifications

• D21C1/02

  with water or steam · CPC title

• D21D1/00

  Methods of beating or refining; Beaters of the Hollander type (knotter screens D21F) · CPC title

• D21C1/06

  with alkaline reacting compounds · CPC title

• D21B1/16

  in the presence of chemical agents · CPC title

• D21H11/12 Primary

  Pulp from non-woody plants or crops, e.g. cotton, flax, straw, bagasse · CPC title