Moisture-curable adhesive composition and a method for mounting tiles on wall surfaces

Patent metadata

Field	Value
Publication number	US-11624014-B2
Application number	US-201816483196-A
Country	US
Kind code	B2
Filing date	Feb 5, 2018
Priority date	Feb 6, 2017
Publication date	Apr 11, 2023
Grant date	Apr 11, 2023

Abstract

A moisture-curable adhesive composition comprises a polymer component selected from a silane-terminated polyalkylene oxide and/or a polyurethane; a plurality of amino-silane modified wollastonite fibers having an average aspect ratio of from about 1.5:1 to about 12:1 and an average fiber length of from about 6 μm to about 825 μm; at least two fillers, wherein one of said fillers is untreated and a second of said fillers is treated with a modifier selected from the group consisting of a fatty acid derivative, a silane, a titanate, and mixtures thereof wherein at least one of said fillers is irregularly shaped; and a rheology modifier. The composition preferably further comprises a plurality of irregularly-shaped crumb rubber particles having an average particle size of between about 0.5 to 1.5 mm. The composition is useful for adhering tiles to surfaces, especially large format tiles to substantially vertically-extending wall surfaces.

First claim

What is claimed:

1. A moisture-curable adhesive composition comprising:
a) a polymer component selected from a silane-terminated polyalkylene oxide and/or a polyurethane;
b) a plurality of amino-silane modified wollastonite fibers having an average aspect ratio of from about 1.5:1 to about 12:1 and an average fiber length of from about 6 μm to about 825 μm;
c) a first filler comprising stearate-treated ground calcium carbonate particles and having a mean particle size between about 1.5 μm and about 10 μm, wherein said first filler is present in the composition in an amount of about 1 to about 27% by weight; a second filler comprising untreated ground calcium carbonate particles and having a mean particle size between about 1.5 μm and about 10 μm, wherein said second filler is present in the composition in an amount of about 1 to about 34% by weight; and a third filler comprising stearate-treated ground calcium carbonate particles and having a mean particle size between about 0.1 μm and about 1.3 μm, wherein said third filler is present in the composition in an amount of about 1 to about 20% by weight; wherein at least one of said fillers is irregularly shaped;
d) a rheology modifier.

2. The composition of claim 1 , wherein the polymer component is the silane-terminated polyalkylene oxide and is present in an amount of about 5 to about 40% by weight.

3. The composition of claim 2 , wherein:
the silane-terminated polyalkylene oxide is present in an amount of about 10 to about 30% by weight;
the plurality of amino-silane modified wollastonite fibers is present in an amount of about 3 to about 15% by weight, and the amino-silane loading is about 1 to about 35% by weight of the fibers;
the first filler, the second filler, and the third filler are present in total amount of about 30 to about 70% by weight; and
the composition further comprises a plasticizer in an amount of about 2 to about 40% by weight.

4. The composition of claim 3 , wherein:
the silane-terminated polyalkylene oxide is present in an amount of about 12 to about 24% by weight;
the plurality of amino-silane modified wollastonite fibers is present in an amount of about 5 to about 10% by weight, and the amino-silane loading is about 2 to about 20% by weight of the fibers;
the first filler, the second filler, and the third filler are present in total amount of about 40 to about 60% by weight; and
the plasticizer is present in an amount of about 10 to about 30% by weight.

5. The composition of claim 4 , wherein:
the silane-terminated polyalkylene oxide is present in an amount of about 15 to about 20% by weight;
the plurality of amino-silane modified wollastonite fibers is present in an amount of about 6 to about 8% by weight, and the amino-silane loading is about 4 to about 10% by weight of the fibers;
the first filler, the second filler, and the third filler are present in total amount of about 42 to about 50% by weight; and
the plasticizer is present in an amount of about 18 to about 24% by weight.

6. The composition of claim 1 further comprising a plurality of irregularly-shaped crumb rubber particles having an average particle size of between about 0.5 to 1.5 mm.

7. The composition of claim 6 , wherein the plurality of irregularly-shaped crumb rubber particles is present in an amount of about 0.5 to about 10%.

8. The composition of claim 1 further comprising a dehydrating agent, an adhesion promoter, and a catalyst.

9. The composition of claim 1 , wherein the silane-terminated polyalkylene oxide comprises:
a first silane-terminated polyalkylene oxide comprising a methoxysilyl chain polymer and having a branched polyether backbone; and
a second silane-terminated polyalkylene oxide comprising a methoxysilyl chain polymer and having a linear polyether backbone.

10. The composition of claim 9 , wherein:
the first silane-terminated polyalkylene oxide is present in an amount of between about 5 to about 30% by weight; and
the second silane-terminated polyalkylene oxide is present in an amount of between about 0.5 to about 5% by weight.

11. The composition of claim 1 , wherein:
the first filler is present in the composition in an amount of between about 7 to about 19% by weight;
the second filler is present in the composition in an amount of between about 14 to about 28% by weight; and
the third filler is present in the composition in an amount of between about 5 to about 15% by weight.

12. The composition of claim 1 , wherein the average aspect ratio of the plurality of the amino-silane modified wollastonite fibers is from about 2:1 to about 8:1 and the average fiber length of the amino-silane modified wollastonite fibers is from about 10 to about 40 μm.

13. The composition of claim 12 , wherein the average aspect ratio of the plurality of the amino-silane modified wollastonite fibers is from about 2:1 to about 5:1 and the average fiber length of the amino-silane modified wollastonite fibers is from about 12 μm to about 25 μm.

14. The composition of claim 1 , wherein the untreated filler has an average particle size of about 3 μm and the third filler has an average particle size of about 0.7 μm.

15. The composition of claim 1 , wherein the rheology modifier is the fatty acid derivative.

16. The composition of claim 1 , wherein the fatty acid derivative comprises stearic acid.

17. The composition of claim 1 , wherein the polymer component is the polyurethane and the polyurethane comprises a silane-modified polyurethane.

Assignees

• Bostik Inc
• Bistik Inc

Inventors

• Porter Todd V
• Bulen Chad P
• Oztemiz Serhan
• Devlin Liam P

Classifications

• C08K9/02

  Ingredients treated with inorganic substances · CPC title

• C08G65/336

  containing silicon · CPC title

• C08L21/00

  Compositions of unspecified rubbers · CPC title

• C08K7/08

  Oxygen-containing compounds · CPC title

• C08G18/837 Primary

  by silicon containing compounds · CPC title