Sealant material

Patent metadata

Field	Value
Publication number	US-11618841-B2
Application number	US-201916387081-A
Country	US
Kind code	B2
Filing date	Apr 17, 2019
Priority date	Oct 24, 2016
Publication date	Apr 4, 2023
Grant date	Apr 4, 2023

Abstract

A sealant material for sealing joints between male and female mating parts comprising:
(a) an elongate flexible thread suitable for wrapping around at least one of the parts, and (b) a joint sealing composition comprising an anaerobically curable composition in solid form,

the flexible thread being coated with the anaerobically curable composition. This provides a reactive composition on the thread for sealing joints.

First claim

What is claimed is:

1. A sealant material for sealing joints between male and female mating parts comprising:
(a) an elongate flexible thread suitable for wrapping around at least one of the parts, and
(b) an anaerobically curable joint sealing composition in solid form, the flexible thread being coated with the anaerobically curable joint sealing composition in solid form.

2. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable component and optionally has at least one functional group selected from acrylates and methacrylates, and combinations thereof.

3. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises:
(a) an anaerobically curable component; and
(b) a curing component for curing the anaerobically curable component;

wherein the anaerobically curable joint sealing composition has a melting point in the range from about 30° C. to about 100° C.

4. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition is in solid tack-free form.

5. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition has a melting point from about 40° C. to about 100° C.

6. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition has a melting point from about 50° C. to about 100° C.

7. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable component which comprises an anaerobically curable monomer.

8. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable component which comprises an anaerobically curable monomer and a resin component.

9. A sealant material according to claim 8 wherein the resin component is anaerobically curable.

10. A sealant material according to claim 8 wherein the resin component and the anaerobically curable monomer are each a solid, each with a melting point in the range from about 30° C. to about 100° C.

11. A sealant material according to claim 8 wherein the anaerobically curable joint sealing composition comprises a first part comprising the resin component and a second part comprising the anaerobically curable monomer.

12. A sealant material according to claim 8 wherein the anaerobically curable component includes the product formed by melting the resin component and the anaerobically curable monomer and blending them and forming a solid blended product.

13. A sealant material according to claim 8 wherein the resin component is present in an amount of from about 10 to about 60% by weight based on the total weight of the composition.

14. A sealant material according to claim 8 wherein the resin component is selected from: (meth) acrylated polyurethane resins with a molecular weight of about 2,000 g/mol or higher; novolac resins with a molecular weight of about 2,000 g/mol or higher; (meth)acrylated polyester resins with a molecular weight of about 2,000 g/mol or higher; and combinations thereof.

15. A sealant material according to claim 8 wherein the anaerobically curable monomer is present in an amount of from about 40 to about 90% by weight based on the total weight of the composition.

16. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable component in which the anaerobically curable component is present in an amount of from about 80% to about 99% by weight of the total composition.

17. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable monomer which comprises at least one acrylate or methacrylate ester group.

18. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition comprises an anaerobically curable component that includes at least one of: (meth)acrylated polyurethane resin with a molecular weight of less than about 1000 g/mol, (meth)acrylate monomers, encapsulated (meth)acrylate monomers; and combinations thereof.

19. A sealant material according to claim 1 including a curing component that is present in an amount of from about 0.1 to about 10% by weight based on the total weight of the composition, and/or wherein the curing component comprises an encapsulated peroxide.

20. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition contains less than 1% solvent by weight based on the total weight of composition and wherein the solvent is organic solvent or water.

21. A sealant material according to claim 1 wherein the anaerobically curable joint sealing composition has a re-solidification point in the range from about 30 to about 50° C.

22. A sealant material according to claim 1 comprising joint sealing composition present in an amount from:
about 5 to about 90% w/w, and wherein the elongate flexible thread is present in an amount from about 10 to about 95% w/w of elongate flexible thread.

23. A sealant material according to claim 1 wherein the thread is made from one or more of the following materials: a polyamide, polypropylene, polyester, PTFE, polyphenylene sulfide or cotton and combinations thereof.

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Ledwith Deirdre
• Vaissaud Laura
• Doherty Michael
• Houlihan James
• Kneafsey Brendan

Classifications

• C10M1/00

  Liquid compositions essentially based on mineral lubricating oils or fatty oils; Their use as lubricants · CPC title

• C09K2200/0655

  Polyesters · CPC title

• C09K2003/1065

  Anaerobically hardenable materials · CPC title

• C09K2200/0441

  Carboxylic acids, salts, anhydrides or esters thereof · CPC title

• C09J175/14 Primary

  Polyurethanes having carbon-to-carbon unsaturated bonds · CPC title