Peroxide-cured halogenated elastomers having a silicon-containing superficial layer

Patent metadata

Field	Value
Publication number	US-11597816-B2
Application number	US-201816955170-A
Country	US
Kind code	B2
Filing date	Dec 19, 2018
Priority date	Dec 22, 2017
Publication date	Mar 7, 2023
Grant date	Mar 7, 2023

Abstract

Described herein is curable composition comprising a partially halogenated elastomeric gum comprising a plurality of cure sites selected from at least one of iodine, bromine, and nitrile; a silicon-containing compound; a dehydrohalogenation agent; and a peroxide cure system. Upon curing, a silicon-containing superficial layer forms, which can provide good chemical stability, increased durability, non-tackiness, and a matte finish to the cured elastomer.

First claim

What is claimed is:

1. A curable partially halogenated elastomeric gum composition comprising:
(a) a partially halogenated elastomeric gum comprising (i) at least 25% halogen by weight, wherein the halogen is at least one of fluorine and chlorine and (ii) a plurality of cure sites wherein the cure sites are selected from at least one of iodine, bromine, or nitrile;
(b) at least 0.01 parts by mass of a silicon-containing compound per 100 parts by mass of the partially halogenated elastomeric gum;
(c) at least 1 mmol and at most 10 mmol of a dehydrohalogenation agent per 100 parts by mass of the partially halogenated elastomeric gum; and
(d) a curing system, wherein the curing system consists of a peroxide and a coagent.

2. The composition of claim 1 , wherein the partially halogenated elastomeric gum is a fluorinated amorphous polymer or a chlorinated amorphous polymer.

3. The composition of claim 2 , wherein fluorinated amorphous polymer comprises interpolymerized vinylidene fluoride monomeric units.

4. The composition of claim 2 , wherein the partially halogenated elastomer gum comprises a fluorinated amorphous polymer, the fluorinated amorphous polymer comprises at least one of: (i) a copolymer comprising tetrafluoroethylene, vinylidene fluoride, and hexafluoropropylene monomeric units; (ii) a copolymer comprising tetrafluoroethylene, and propylene monomeric units; (iii) a copolymer comprising tetrafluoroethylene, vinylidene fluoride, and propylene monomeric units; (iv) a copolymer comprising vinylidene fluoride, perfluoro (methyl vinyl) ether, and hexafluoropropylene monomeric units; or (v) a copolymer comprising vinylidene fluoride, and hexafluoropropylene monomeric units.

5. The composition of claim 1 , wherein the partially halogenated elastomeric gum is a block copolymer comprising at least one A block and at least one B block.

6. The composition of claim 5 , wherein the A block comprises 30-85 wt % TFE; 5-40 wt % HFP; and 5-55 wt % VDF; and the B block comprises 25-65 wt % VDF and 15-60 wt % HFP; or even 35-60 wt % VDF and 25-50 wt % HFP based on the weight of the fluorinated elastomeric gum.

7. The composition of claim 1 , wherein the composition comprises less than 5 parts by weight of the silicon-containing compound per 100 parts by weight of the partially halogenated elastomeric gum.

8. The composition of claim 1 , wherein the silicon-containing compound is a tetraalkoxysilane.

9. The composition of claim 1 , wherein the composition comprises at least 0.1 and at most 5 parts by weight of the peroxide per 100 parts by weight of the partially halogenated elastomeric gum.

10. The composition of claim 1 , wherein the composition comprises from 0.1 to 10 parts by weight of the coagent per 100 parts by weight of the partially halogenated elastomeric gum.

11. An article comprising the cured composition according to claim 1 .

12. A method of making a partially halogenated elastomer having a superficial layer comprising silicon, the method comprising:
(a) obtaining the composition of claim 1 ; and
(b) heating the composition in an unrestrained fashion at a temperature of at least 160° C. for at least 15 min.

13. The composition of claim 1 , wherein the composition is substantially free of an acid acceptor.

14. The composition of claim 1 , wherein the silicon-containing compound is inorganic.

15. The composition of claim 1 , wherein the silicon-containing compound is organic.

16. The composition of claim 1 , wherein the silicon-containing compound is a particle.

17. The composition of claim 1 , wherein the silicon-containing compound is a liquid.

18. The article of claim 11 , wherein the article is at least one of a seal, o-ring, gasket, or wearable device.

19. The composition of claim 1 , comprising at least 1.5 mmol and at most 10 mmol of a dehydrohalogenation agent per 100 parts by mass of the partially halogenated elastomeric gum.

Assignees

• 3M Innovative Properties Company

Inventors

• Fukushi Tatsuo
• Nguyen Tho Q
• Sohlo Allen M

Classifications

• C08K3/34

  Silicon-containing compounds · CPC title

• C08K5/50

  Phosphorus bound to carbon only · CPC title

• C08K13/02

  Organic and inorganic ingredients · CPC title

• C08K5/5415 Primary

  containing at least one Si—O bond · CPC title

• C08K5/14

  Peroxides · CPC title