Method for producing a sintered component

Patent metadata

Field	Value
Publication number	US-11590571-B2
Application number	US-202017060271-A
Country	US
Kind code	B2
Filing date	Oct 1, 2020
Priority date	Oct 25, 2019
Publication date	Feb 28, 2023
Grant date	Feb 28, 2023

Abstract

The invention relates to a method for producing a sintered component comprising the steps: providing a metallic powder; filling the powder into a powder press; pressing the powder to form a green compact; removing the green compact from the powder press; sintering the green compact into a sintered component with pores; optional redensification of the sintered component; hardening of the sintered component, wherein the pores of the sintered component, prior to hardening at least in that region of the surface of the sintered component which is subjected to a hardening, are at least partially filled with a filling agent.

First claim

The invention claimed is:

1. A method for producing a sintered component comprising the steps:
providing an iron-based powder consisting of between 0.1 wt. % and 0.9 wt. % of C, between 0 wt. % and 5.0 wt. % of Ni, between 0 wt. % and 2 wt. % of Mo, between 0 wt. % and 1 wt. % of Mn and between 0.1 wt. % and 3 wt. % of copper, the remainder being iron;
filling the powder into a powder press;
pressing the powder to form a green compact;
removing the green compact from the powder press;
sintering the green compact into a sintered component with pores;
optionally redensifying the sintered component;
hardening of the sintered component;

wherein the pores of the sintered component, prior to hardening at least in a region of a surface of the sintered component which is subjected to hardening, are at least partially filled with a filling agent.

2. A method for producing a sintered component, comprising the steps:
adding a filling agent to an iron-based powder consisting of between 0.1 wt. % and 0.9 wt. % of C, between 0 wt. % and 5.0 wt. % of Ni, between 0 wt. % and 2 wt. % of Mo, between 0 wt. % and 1 wt. % of Mn and between 0.1 wt. % and 3 wt. % of copper, the remainder being iron;
filling the powder into a powder press;
pressing the powder to form a green compact;
removing the green compact from the powder press;
sintering the green compact into a sintered component with pores;
optionally redensifying the sintered component;
hardening of the sintered component;

wherein the pores of the sintered component, prior to hardening at least in a region of a surface of the sintered component which is subjected to hardening, are at least partially filled with the filling agent.

3. The method according to claim 1 , wherein the filling agent is added during and/or after sintering of the green compact.

4. The method according to claim 1 , wherein a metal or a metal alloy is used as the filling agent.

5. The method according to claim 1 , wherein the sintered component is case-hardened.

6. The method according to claim 1 , wherein the hardening is carried out by carburization and subsequent quenching or by sinter hardening and subsequent quenching or by inductive hardening.

7. The method according to claim 6 , wherein the carburization is carried out by means of low-pressure carburizing or carbonitriding.

Assignees

• Miba Sinter Austria Gmbh

Inventors

• Neto Jose Correa
• Hellein Robert
• Rodrigues Daniel Napoleao

Classifications

• C23C8/20

  Carburising · CPC title

• C21D1/06

  Surface hardening · CPC title

• C22C38/16

  containing copper · CPC title

• B22F3/26 Primary

  Impregnating {(making ferrous alloys by impregnation C22C33/0242)} · CPC title

• C23C8/32

  of ferrous surfaces · CPC title