Processes for producing optical effects layers

Patent metadata

Field	Value
Publication number	US-11577273-B2
Application number	US-201917264229-A
Country	US
Kind code	B2
Filing date	Jun 18, 2019
Priority date	Jul 30, 2018
Publication date	Feb 14, 2023
Grant date	Feb 14, 2023

Abstract

The invention relates to the field of the protection of security documents such as for example banknotes and identity documents against counterfeit and illegal reproduction. In particular, the present invention provides processes for optical effect layers (OEL) exhibiting two or more nested indicia using a magnetic assembly comprising i) a soft magnetic plate (x31) comprising a) one or more voids (V) and b) one or more indentations (I) and/or one or more protrusions (P), and ii) one or more dipole magnets (x32).

First claim

The invention claimed is:

1. A process for producing an optical effect layer exhibiting two or more nested indicia on a substrate, said process comprising the steps of:
a) applying onto a substrate surface a coating composition comprising i) platelet-shaped magnetic or magnetizable pigment particles and ii) a binder material so as to form a coating layer on said substrate, said coating composition being in a first liquid state;
b) exposing the coating layer to a magnetic field of a magnetic assembly comprising
i) a soft magnetic plate comprising one or more soft magnetic metals, alloys or compounds having magnetic permeability or made of a composite comprising from 25 wt-% to 95 wt-% of soft magnetic particles dispersed in a non-magnetic material, the weight percents being based on a total weight of the magnetic plate,
wherein the soft magnetic plate comprises one or more voids for receiving one or more dipole magnets,
wherein the soft magnetic plate comprises one or more indentations and/or one or more protrusions, each of said one or more indentations and/or one or more protrusions comprising one or more continuous loop-shaped indicia and/or one or more discontinuous loop-shaped indicia, and
wherein the one or more voids are surrounded by the one or more indentations and/or one or more protrusions comprising the one or more continuous loop-shaped indicia and/or the one or more voids are surrounded by one or more indentations and/or one or more protrusions comprising the one or more discontinuous loop-shaped indicia,

ii) the one or more dipole magnets, each of said one or more dipole magnets having its magnetic axis substantially perpendicular to the substrate surface and all of said one or more dipole magnets having a same magnetic direction, wherein said one or more dipole magnets are disposed within the one or more voids;

and
c) hardening the coating composition to a second state so as to fix the platelet-shaped magnetic or magnetizable pigment particles in their adopted positions and orientations.

2. The process according to claim 1 , wherein the soft magnetic plate comprises the one or more indentations and wherein a top surface of the one or more dipole magnets, is flush with the top surface of the soft magnetic plate.

3. The process according to claim 1 , wherein the soft magnetic plate comprises the one or more protrusions and wherein a top surface of the one or more dipole magnets, is flush with the top surface of the soft magnetic plate.

4. The process according to claim 1 , further comprising a step of exposing the coating layer to a dynamic magnetic field of a device so as to bi-axially orient at least a part of the platelet-shaped magnetic or magnetizable pigment particles, said step occurring prior to or simultaneously with step b) and before step c).

5. The process according to claim 1 , wherein the soft magnetic plate is made a composite comprising from 25 wt-% to 95 wt-% of soft magnetic particles dispersed in a non-magnetic material being a polymeric matrix comprising or consisting of either thermoplastic materials selected from the group consisting of polyamides, co-polyamides, polyphtalimides, polyolefins, polyesters, polytetrafluoroethylenes, polyacrylates, polymethacrylates, polyimides, polyetherimides, polyetheretherketones, polyaryletherketones, polyphenylene sulfides, liquid crystal polymers, polycarbonates and mixtures thereof or a thermosetting material selected from the group consisting of epoxy resins, phenolic resins, polyimide resins, silicon resins and mixtures thereof.

6. The process according to claim 5 , wherein the one or more voids have a depth between 5% and 100% in comparison with a thickness of the soft magnetic plate, and/or the one or more indentations have a depth between 5% and 100%, in comparison with a thickness of the soft magnetic plate and/or the one or more protrusions have a height between 5% and 100% in comparison with a thickness of the soft magnetic plate.

7. The process according to claim 1 , wherein the soft magnetic particles are selected from the group consisting of carbonyl iron, carbonyl nickel, cobalt and combinations thereof.

8. The process according to claim 1 , wherein the soft magnetic particles have a d50 between 0.5 μm and 100 μm.

9. The process according to claim 1 , wherein a diameter of the one or more dipole magnets is smaller than a size of the one or more voids.

10. The process according to claim 1 , wherein the step c) of hardening the coating composition is carried out partially simultaneously with the step b).

11. The process according to claim 1 , wherein the platelet-shaped magnetic or magnetizable pigment particles are platelet-shaped optically variable magnetic or magnetizable pigment particles selected from the group consisting of platelet-shaped magnetic thin-film interference pigment particles, platelet-shaped magnetic cholesteric liquid crystal pigment particles, platelet-shaped interference coated pigment particles comprising a magnetic material and mixtures of two or more thereof.

12. The process according to claim 1 , wherein the one or more voids have a depth between 5% and 90%, in comparison with a thickness of the soft magnetic plate.

13. A process for producing an optical effect layer exhibiting two or more nested indicia on a substrate, said process comprising the steps of:
a) applying onto a substrate surface a coating composition comprising i) platelet-shaped magnetic or magnetizable pigment particles and ii) a binder material so as to form a coating layer on said substrate, said coating composition being in a first liquid state;
b) exposing the coating layer to a magnetic field of a magnetic assembly comprising
i) a soft magnetic plate comprising one or more soft magnetic metals, alloys or compounds having magnetic permeability or made of a composite comprising from 25 wt-% to 95 wt-% of soft magnetic particles dispersed in a non-magnetic material, the weight percents being based on a total weight of the magnetic plate,
wherein the soft magnetic plate comprises one or more voids for receiving one or more dipole magnets,
wherein the soft magnetic plate comprises one or more indentations and/or one or more protrusions, each of said one or more indentations and/or one or more protrusions one or more continuous loop-shaped indicia and/or one or more discontinuous loop-shaped indicia, and
wherein the one or more voids are surrounded by the one or more continuous loop-shaped indicia and/or the one or more voids are surrounded by the one or more discontinuous loop-shaped indicia,

ii) the one or more dipole magnets, each of said one or more dipole magnets having its magnetic axis substantially perpendicular to the substrate surface and all of said one or more dipole magnets having a same magnetic direction, wherein said one or more dipole magnets are disposed within the one or more voids, wherein a top surface of the one or more dipole magnets, is flush with the top surface of the soft magnetic plate;

and
c) hardening the coating composition to a second state so as to fix the platelet-shaped magnetic or magnetizable pigment particles in their adopted positions and orientations.

Assignees

• Sicpa Holding Sa

Inventors

• Nikseresht Ghanepour Neda
• Mueller Edgar
• Schmid Mathieu
• Despland Claude-Alain

Classifications

• B05D3/0254

  After-treatment · CPC title

• B05D3/067

  Curing or cross-linking the coating · CPC title

• B42D25/23

  Identity cards · CPC title

• B05D3/207 Primary

  post-treatment by magnetic fields · CPC title

• H01F1/14

  metals or alloys · CPC title