Grafted polyvinyl alcohol polymer, formulations containing the same, and creping methods

Patent metadata

Field	Value
Publication number	US-11560443-B2
Application number	US-202017010858-A
Country	US
Kind code	B2
Filing date	Sep 3, 2020
Priority date	Sep 11, 2019
Publication date	Jan 24, 2023
Grant date	Jan 24, 2023

Abstract

A grafted polyvinyl alcohol polymer includes a polyvinyl alcohol main chain and a plurality of side chains grafted to the polyvinyl alcohol main chain. One or more of the side chains from the plurality of side chains include one or more units selected from: an aliphatic carboxylic acid, an aliphatic amide, an amino alkyl (meth)acrylate, a hydroxylated alkyl (meth)acrylate, or any combinations thereof. The grafted polyvinyl alcohol polymer can be included in a formulation that also includes water, and the formulation can be used as an adhesive in a creping process.

First claim

What is claimed is:

1. A grafted polyvinyl alcohol polymer comprising a polyvinyl alcohol main chain and a plurality of side chains grafted to the polyvinyl alcohol main chain,
wherein one or more of said side chains from the plurality of side chains comprise i) units of an aliphatic carboxylic acid or units of an aliphatic amide or both, and ii) units of an amino alkyl (meth)acrylate or units of a hydroxylated alkyl (meth)acrylate, or both, and
wherein said grafted polyvinyl alcohol polymer has each of the following properties:
a) the grafted polyvinyl alcohol polymer is a latex;
b) the grafted polyvinyl alcohol polymer is completely dispersible in water at an amount of from 1 wt % to 25 wt % at a pH of 2 to 5;
c) the grafted polyvinyl alcohol polymer is not an irreversible gel at any pH;
d) the grafted polyvinyl alcohol polymer is gel-free at a pH of 8 and
e) the grafted polyvinyl alcohol polymer has a first glass transition temperature of from −40° C. to 60° C., and a second glass transition temperature of from 70° C. to 90° C.

2. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise: units of the aliphatic carboxylic acid, units of the aliphatic amide, units of the amino alkyl (meth)acrylate, and units of the hydroxylated alkyl (meth)acrylate.

3. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise units of the aliphatic carboxylic acid.

4. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise units of the aliphatic amide.

5. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise units of the hydroxylated alkyl (meth)acrylate.

6. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise: units of the aliphatic carboxylic acid and units of the aliphatic amide.

7. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise: units of the aliphatic carboxylic acid and units of the hydroxylated alkyl (meth)acrylate.

8. The grafted polyvinyl alcohol polymer of claim 1 , wherein the one or more of said side chains from the plurality of side chains comprise: units of the aliphatic amide and units of the hydroxylated alkyl (meth)acrylate.

9. The grafted polyvinyl alcohol polymer of claim 1 , wherein a) said grafted polyvinyl alcohol polymer has a viscosity of less than 500 cP⋅s when present in an aqueous dispersion having a pH of 3, at a concentration of 22.5 to 25 wt %, at 25° C. and 1 atmosphere orb) said grafted polyvinyl alcohol polymer has a viscosity of less than 100 cPs when present in an aqueous solution having a pH of 3, at a concentration of 2.5 to 10 wt %, at 25° C. and 1 atmosphere or c) said grafted polyvinyl alcohol polymer is capable of being dispersed in an aqueous solution at a concentration of from 10 wt % to 40 wt %.

10. The grafted polyvinyl alcohol polymer of claim 1 , wherein said grafted polyvinyl alcohol polymer is capable of being in condensed form when present in an aqueous solution having a pH of from about 2 to about 5, and is capable of being in semi-condensed form when present in an aqueous solution having a pH of from about 4 to about 5.5, and is capable of being in amorphous form when present in an aqueous solution having a pH of from about 5.5 to about 8.

11. The grafted polyvinyl alcohol polymer of claim 1 , wherein a) the grafted polyvinyl alcohol polymer has a weight-average molecular weight of from 5,000 Daltons to about 1,500,000 Daltons or b) the grafted polyvinyl alcohol polymer has a number-average molecular weight of from 1,000 Daltons to about 50,000 Daltons, or c) said grafted polyvinyl alcohol polymer has a polydispersity, Mw/Mn, of at least 1.5 .

12. The grafted polyvinyl alcohol polymer of claim 1 , wherein a) the polyvinyl alcohol main chain, in unreacted form, has a weight-average molecular weight of from about 5,000 Daltons to about 1,500,000 Daltons or b) the polyvinyl alcohol main chain, in unreacted form, has a number-average molecular weight of from about 1,000 Daltons to about 50,000 Daltons or c) the polyvinyl alcohol main chain, in unreacted form, has a polydispersity, Mw/Mn, of from 2 to 7 or d) the polyvinyl alcohol main chain has a degree of hydrolysis of from about 74 mol % to about 95 mol %.

13. The grafted polyvinyl alcohol polymer of claim 1 ,
wherein the aliphatic carboxylic acid is present and comprises at least one of acrylic acid and methacrylic acid,
wherein the aliphatic amide is present and comprises at least one of acrylamide, methacrylamide, dimethyl acrylamide, diethyl acrylamide, dipropyl acrylamide and N-t-butylacrylamide, and
wherein the hydroxylated alkyl (meth)acrylate is present and comprises at least one of 2-hydroxyethyl methacrylate and hydroxy propyl methacrylate.

14. The grafted polyvinyl alcohol polymer of claim 1 , which includes a structure (I):
—[CH 2 —CH(OH)] a —[CH 2 —CH(R])] b −  (I)

wherein a total weight percent of (a) units is from 74% to 95% based on the total weight of the grafted polyvinyl alcohol polymer,
wherein a total weight percent of (b) units is from 5% to 26% based on the total weight of the grafted polyvinyl alcohol polymer,
wherein each R is acetate or a side chain from the plurality of side chains.

15. A formulation comprising:
an aqueous phase; and
the grafted polyvinyl alcohol polymer of claim 1 .

16. The formulation of claim 15 , wherein said formulation comprises:
100 parts by weight of the aqueous phase; and
from 10 parts by weight to 40 parts by weight of the grafted polyvinyl alcohol polymer, wherein
the grafted polyvinyl alcohol polymer is dispersed in the aqueous phase.

17. The formulation of claim 15 , wherein a) said formulation has a pH of from about 2 to about 5, and wherein the grafted polyvinyl alcohol polymer is in condensed form or b) said formulation has a pH of from about 4 to about 5.5, and wherein the grafted polyvinyl alcohol polymer is in semi-condensed form or c) said formulation has a pH of from about 5.5 to about 8, and wherein the grafted polyvinyl alcohol polymer is in an amorphously-dissolved form.

18. The formulation of claim 15 , wherein said formulation contains less than 1 wt % of surfactant.

19. A method of making a grafted polyvinyl alcohol polymer of claim 1 , the method comprising:
polymerizing, via free-radical polymerization, at least one of an aliphatic carboxylic acid, an aliphatic amide, an amino alkyl (meth)acrylate and a hydroxylated alkyl (meth)acrylate in the presence of a free polyvinyl alcohol.

20. A method of making an aqueous solution of a grafted polyvinyl alcohol polymer of claim 1 , the method comprising:
adding alkali to a dispersion, to thereby increase the pH of the dispersion to be from 4 to 8 and form an aqueous solution of the grafted polyvinyl alcohol polymer, wherein
the dispersion comprises:
an aqueous phase; and
the grafted polyvinyl alcohol polymer, which is dispersed in the aqueous phase, wherein the dispersion has a pH of from 2 to 5 prior to said adding.

21. A process for creping a fiber web, comprising:
providing a rotating cylindrical dryer, including a dryer surface,
applying a formulation comprising the gr

Assignees

• Buckman Laboratories Int Inc

Inventors

• Moustafa Ahmed
• Glover Daniel

Classifications

• C08F261/04 Primary

  on to polymers of vinyl alcohol · CPC title

• B29C41/26

  by depositing flowable material on a rotating drum · CPC title

• B29K2029/04

  PVOH, i.e. polyvinyl alcohol (B29K2031/04 takes precedence) · CPC title

• B29C67/0011

  for shaping plates or sheets · CPC title

• B29C69/02

  of moulding techniques only · CPC title