Preparation method and application of zero-valent aluminum/iron-bearing clay composite for catalyzing persulfate to oxidize organics

Patent metadata

Field	Value
Publication number	US-11534738-B1
Application number	US-202217870781-A
Country	US
Kind code	B1
Filing date	Jul 21, 2022
Priority date	Oct 28, 2021
Publication date	Dec 27, 2022
Grant date	Dec 27, 2022

Abstract

A preparation method and application of a zero-valent aluminum/iron-bearing clay composite for catalyzing a persulfate to oxidize organics are provided, which belongs to the field of water environmental treatment. A novel catalyst is prepared by an iron-bearing clay and a zero-valent aluminum through a simple ball milling method, for achieving the effect of activating a persulfate to efficiently oxidize and degrade refractory organics in water. The preparation method and operation process thereof are simple. Compared with a chemical synthesis method, the method of the present disclosure brings about less secondary pollution, and has a shorter synthesis time, higher yield and lower cost. The modified material is the natural iron-bearing clay, which is widely available, non-toxic and stable as a heterogeneous catalyst.

First claim

What is claimed is:

1. A refractory organic matter removing method using a zero-valent aluminum/iron-bearing clay composite, comprising:
adding the zero-valent aluminum/iron-bearing clay composite as per a ratio in a range of 0.2 g/L to 1.5 g/L and a persulfate as per a ratio in a range of 119 mg/L to 1904 mg/L into an organic pollutant solution, and the zero-valent aluminum/iron-bearing clay composite activating, at a pH value in a range of 3.00 to 9.00, the persulfate to remove a refractory organic pollutant in the solution, wherein the organic pollutant is one selected from the group consisting of 4-chlorophenol, benzoic acid, nitrobenzene, phenol and an ofloxacin in form of solution;
wherein the zero-valent aluminum/iron-bearing clay composite is prepared as a composite catalyst by mixing a micro-scale zero-valent aluminum and a natural iron-bearing clay mineral with ball milling, a particle size of the micro-scale zero-valent aluminum is in a range of 100 meshes to 200 meshes, namely 75 μm to 150 μm, and the natural iron-bearing clay mineral is nontronite;
wherein a preparation method of the composite catalyst comprises:
mixing the micro-scale zero-valent aluminum with the natural iron-bearing clay mineral in a mass ratio of 1:1 and then placing in an agate ball milling jar;
adding agate balls with a ball to material mass ratio in a range of 20:1 to 50:1 to the agate ball milling jar;
putting the agate ball milling jar into a vacuum jacket for vacuumizing and then performing ball milling to obtain mixed powder, wherein a duration of the ball milling is controlled in a range of 0.5 hours (h) to 4 h, and a rotation rate of planetary ball mill is controlled in a range of 200 revolutions per minute (rpm) to 800 rpm; and
placing the mixed powder obtained after the ball milling in a glove box, and drying the mixed powder to obtain the zero-valent aluminum/iron-bearing clay composite.

2. The refractory organic matter removing method using the zero-valent aluminum/iron-bearing clay composite according to claim 1 , wherein the zero-valent aluminum/iron-bearing clay composite activates, at the pH value of 3, the persulfate to remove the refractory organic pollutant.

3. The refractory organic matter removing method using the zero-valent aluminum/iron-bearing clay composite according to claim 1 , wherein the preparation method of the composite catalyst specifically comprises:
mixing the micro-scale zero-valent aluminum with the particle size 75 μm with the nontronite in the mass ratio of 1:1 and then placing in the agate ball milling jar of 50 mL;
adding the agate balls with the ball to material mass ratio of 20:1 to the agate ball milling jar;
putting the agate ball milling jar into the vacuum jacket for vacuumizing and then performing the ball milling to obtain the mixed powder, wherein the duration of the ball milling is controlled to be 1.0 h, and the rotation rate of planetary ball mill is controlled to be 600 rpm; and
placing the mixed powder obtained after the ball milling in the glove box, and drying the mixed powder to obtain a zero-valent aluminum/nontronite composite;
wherein the zero-valent aluminum/nontronite composite of 100 mg as the composite catalyst and the persulfate of 476 mg/L are added into a wastewater of 200 mL containing 4-chlorophenol of 20.0 mg/L and reacted for 1 h.

Assignees

• Nanjing University Of Technology

Inventors

• Yang Hu
• Yang Ran

Classifications

• C02F1/725

  by catalytic oxidation · CPC title

• C02F2101/30

  Organic compounds · CPC title

• B01J23/745 Primary

  Iron · CPC title

• B01J35/40

  characterised by dimensions, e.g. grain size (in a colloidal state B01J35/23; crystallite size B01J35/77) · CPC title

• B01J37/04

  Mixing {(B01J37/0009, B01J37/0018 take precedence)} · CPC title