Lead casing for pencil, and pencil thereof for writing, drawing, marking, plotting, and coloring

Patent metadata

Field	Value
Publication number	US-11524518-B2
Application number	US-201917415545-A
Country	US
Kind code	B2
Filing date	Dec 17, 2019
Priority date	Dec 18, 2018
Publication date	Dec 13, 2022
Grant date	Dec 13, 2022

Abstract

There is a lead casing for pencil for writing, drawing, marking, plotting, and/or coloring, made of a composition having, by weight relative to the total weight of the lead casing for pencil: a) from 50 to 95% of a mixture of polylactic acid and bio-polyethylene in a weight ratio polylactic acid/bio-polyethylene ranging from 60/40 to 90/10, and b) from 5 to 40% of vegetable fillers chosen in the group consisting of wood fibers. There is a pencil including the lead casing for the pencil of the disclosure for writing, drawing, marking, plotting, and/or coloring as well as a method for manufacturing such a pencil.

First claim

The invention claimed is:

1. A lead casing for a pencil, comprising a composition including, by weight relative to a total weight of the lead casing for the pencil:
a) from 50 to 95% of a mixture of polylactic acid and bio-polyethylene in a weight ratio polylactic acid/bio-polyethylene ranging from 60/40 to 90/10, and
b) from 5 to 40% of vegetable fillers selected from the group consisting of wood fibers.

2. A lead casing for the pencil according to claim 1 , comprising, by weight relative to a total weight of the lead casing for the pencil:
a) from 60 to 95% of a mixture of polylactic acid and bio-polyethylene in a weight ratio polylactic acid/bio-polyethylene ranging from 60/40 to 90/10, and
b) from 7 to 30% of vegetable fillers selected from the group consisting of wood fibers.

3. The lead casing for the pencil according to claim 1 , comprising, by weight relative to the total weight of the lead casing for the pencil:
a) from 80 to 90% of a mixture of polylactic acid and bio-polyethylene in a weight ratio polylactic acid/bio-polyethylene ranging from 65/35 to 85/15, and
b) from 10 to 20% of vegetable fillers selected from the group consisting of wood fibers.

4. A lead casing for the pencil according to claim 1 , wherein the weight ratio polylactic acid/polybutylene adipate terephthalate is ranging from 65/45 to 80/20.

5. The lead casing for the pencil according to claim 1 , wherein the composition comprises an additional filler different from the vegetable fillers.

6. The lead casing for the pencil according to claim 5 , wherein the additional filler is selected from the group consisting of shellfish shells.

7. The lead casing for the pencil according to claim 5 , wherein the additional filler is milled oyster shells.

8. The lead casing for the pencil according to claim 1 , wherein the total content of filler ranges from 5 to 50%, by weight, with respect to total weight of the lead casing.

9. The lead casing for the pencil according to claim 1 , wherein the total content of filler ranges from 7 to 40%, by weight, with respect to total weight of the lead casing.

10. The lead casing for the pencil according to claim 1 , wherein the total content of filler ranges from 8 to 30%, by weight, with respect to total weight of the lead casing.

11. The lead casing for the pencil according to claim 1 , wherein the total content of filler ranges from 9 to 20%, by weight with respect to total weight of the lead casing.

12. The lead casing for the pencil according to claim 1 , wherein a content of mineral filler ranges from 5 to 40% by weight, relative to the total weight of the lead casing.

13. The lead casing for the pencil according to claim 1 , further comprising at least one additive selected from the group consisting of dyes, pigments, blowing agent, agents for use, lubricants, slip agents, performance modifiers of polylactic acid, and their mixtures.

14. The lead casing for the pencil according to claim 4 , wherein the additive represents from 0.1 to 10% by weight, relative to the total weight of the lead casing for the pencil.

15. The lead casing for the pencil according to claim 1 , further comprising an adhesion promoter.

16. The lead casing for the pencil according to claim 15 , wherein the adhesion promoter is a polylactic acid grafted with maleic anhydride (PLA-MA).

17. A pencil comprising a lead casing for the pencil according to claim 1 surrounding a lead.

18. The pencil according to claim 17 , wherein the lead includes at least graphite and/or pigments.

19. The pencil according to claim 17 , being a graphite pencil and/or a colored pencil.

20. A method for manufacturing a pencil according to claim 17 , wherein the constituents of the lead casing for the pencil are coextruded around the constituents of the lead.

Assignees

• SOCIéTé BIC

Inventors

• Gouerec Julien

Classifications

• B43K19/14 Primary

  Sheathings · CPC title

• B43K19/16

  Making non-propelling pencils (making slate-pencil writing-cores B28D) · CPC title

• B43K19/02 Primary

  Pencils with graphite; Coloured pencils · CPC title

• B29C48/154

  Coating solid articles, i.e. non-hollow articles · CPC title

• B29K2105/0005

  containing compounding ingredients (releasing, lubricating or separating agents B29C33/56, fibers B29K2105/08, B29K2105/12; fillers B29K2105/16, recycled material B29K2105/26) · CPC title