Laser pulse shaping for additive manufacturing

Patent metadata

Field	Value
Publication number	US-11524458-B2
Application number	US-201916538152-A
Country	US
Kind code	B2
Filing date	Aug 12, 2019
Priority date	Oct 14, 2015
Publication date	Dec 13, 2022
Grant date	Dec 13, 2022

Abstract

The present disclosure relates to an apparatus for additively manufacturing a product in a layer-by-layer sequence, wherein the product is formed using powder particles deposited on an interface layer of a substrate. A laser generates first and second beam components. The second beam component has a higher power level and a shorter duration than the first beam component. A mask creates a 2D optical pattern in which only select portions of the second beam components can irradiate the powder particles. The first beam component heats the powder particles close to a melting point, where the particles experience surface tension forces relative to the interface layer. While the particles are heated, the second beam component further heats the particles and also melts the interface layer before the surface tension forces can act on and distort the particles, enabling the particles and the interface layer are able to bond together.

First claim

What is claimed is:

1. An apparatus for additively manufacturing a product in a layer-by-layer sequence, wherein the product is formed using particles of powdered feedstock material deposited on an interface layer of a substrate, the apparatus comprising:
a laser system configured to generate:
a first beam component providing a first power flux level;
a second beam component providing a second power flux level which is greater than said first power flux level;

a mask disposed between the laser system and the powdered feedstock material for creating a 2D optical pattern in which first portions of the first and second beam components are allowed to pass through the mask to irradiate the powdered feedstock material, and second portions of the first and second beam components are not allowed to pass through to the powdered feedstock material;
the first beam component being operable to heat the powdered feedstock material to a first level short of a melting point of the powdered feedstock material, at which point the particles of powdered feedstock material begin to experience surface tension forces relative to said interface layer of the substrate, wherein the interface layer forms only an upper surface portion of the substrate; and
after the particles of powdered feedstock material are heated to the first level short of the melting point, the second beam component being operable to further heat the particles of powdered feedstock material to a second level to melt the particles of powdered feedstock material and also to melt the interface layer of the substrate before the surface tension forces can act on the particles of powdered feedstock material to distort the particles of powdered feedstock material, wherein the interface layer of the substrate comprises a layer having a thickness less than a full thickness of the substrate, such that a portion of the interface layer remains unmelted by the second beam component as the particles of powdered feedstock material and the interface layer are bonded together; and
the laser further being configured such that the second beam component has a duration shorter than the first beam component by a factor of at least 1×10 −3 , and a power controlled to be sufficient only to melt the interface layer of the substrate.

2. The apparatus of claim 1 , wherein the first and second beam components comprise temporally varying laser beam pulses.

3. The apparatus of claim 1 , wherein the laser system includes a laser diode array for generating the first beam component.

4. The apparatus of claim 1 , wherein the laser system includes a pulsed solid state laser for generating the second beam component.

5. The apparatus of claim 1 , wherein:
the laser system includes a laser diode array configured to generate the first beam component, wherein the first beam component forms a first laser pulse having a duration of milliseconds and a power level on an order of kilowatts; and
the laser system includes a pulsed laser configured to generate the second beam component, wherein the second beam component forms a second laser pulse having a duration which is shorter by at least an additional 1×10 −3 factor than milliseconds, and a power level on an order of milli-Joules to Joules of energy.

6. The apparatus of claim 1 , wherein the mask comprises a dynamically controllable mask.

7. The apparatus of claim 6 , further comprising a computer for controlling the mask.

8. The apparatus of claim 7 , wherein the computer is configured to use 2D data files for controlling the mask to construct each layer of the product.

9. The apparatus of claim 1 , wherein the mask comprises a dynamically controllable, optically addressable light valve enabling selected portions of the first and second beam components to pass therethrough to reach the particles of powdered feedstock material, while preventing non-selected portions of the first and second beam components from reaching the particles of powdered feedstock material.

10. The apparatus of claim 8 , wherein the computer is configured to control the laser system such that the second beam component is applied after the first beam component has heated the particles of powdered feedstock material to the first level short of the melting point.

11. The apparatus of claim 8 , wherein the computer is configured to control the laser system such that the second beam component is applied while the first beam component is still being used to heat the particles of powdered feedstock material to the first level short of the melting point.

12. The apparatus of claim 1 , wherein the mask comprises a static mask formed from a sheet of reflective material.

13. The apparatus of claim 1 , further comprising a computer for controlling the mask;
wherein the mask comprises a dynamically controllable mask controllable by the computer;
the mask including a liquid crystal polarization rotator, the liquid crystal polarization rotator including a liquid crystal module and a polarizer;
the liquid crystal module configured to receive and to rotate a first portion of each of the first and second beam components while allowing a second portion of each of the first and second beam components to pass therethrough without being rotated;
wherein the polarizer is configured to reject one of the first or second portions received from the liquid crystal module, and thus to prevent the one of the first or second portions from reaching the particles of powdered feedstock material, while allowing the other one of the first or second portions to reach the particles of powdered feedstock material; and
the liquid crystal module of the mask having a plurality of effective pixels arranged in a two dimensional pattern that are individually controlled to enable the mask to mask off one or more selected areas of a specific layer of the particles of powdered feedstock material of the substrate, and wherein the mask absorbs no optical energy from the first and second beam components.

14. An apparatus for additively manufacturing a product in a layer-by-layer sequence, wherein the product is formed using particles of powdered feedstock material deposited on an interface layer of a substrate, the apparatus comprising:
a computer;
a laser system controlled by the computer and configured to generate:
a first beam component providing a first power flux level through a laser pulse having a millisecond duration;
a second beam component providing a second power flux level through a second laser pulse which has a second power flux level greater than said first power flux level, but which has a time duration which is shorter by at least an additional 1×10 −3 factor than milliseconds;

a dynamically controllable mask disposed between the laser system and the particles of powdered feedstock material, and controllable by the computer, for creating a 2D optical pattern in which first portions of the first and second beam components are allowed to pass through the mask to irradiate the particles of powdered feedstock material, and second portions of the first and second beam components are not allowed to pass through to the particles of powdered feedstock material;
the first beam component being operable to heat the particles of powdered feedstock material at least to a first level short of a melting point of the particles of powdered feedstock material, at which point the particles of powdered feedstock material begin to experience surface tension forces relative to said interface layer of the substrate, wherein the interface layer forms only an upper surface portion of the substrate; and
while the particles of powdered feedstock material

Assignees

• L Livermore Nat Security Llc

Inventors

• Demuth James A
• Bayramian Andrew J
• Duoss Eric B
• Kuntz Joshua D
• Spadaccini Christopher M

Classifications

• B22F10/362

  for preheating · CPC title

• B22F10/366

  Scanning parameters, e.g. hatch distance or scanning strategy · CPC title

• B22F10/28

  Powder bed fusion, e.g. selective laser melting [SLM] or electron beam melting [EBM] · CPC title

• B29C64/282

  of the same type, e.g. using different energy levels · CPC title

• B33Y30/00

  Apparatus for additive manufacturing; Details thereof or accessories therefor · CPC title