Polymer-dispersed liquid crystal composition, preparation method of polymer-dispersed liquid crystal film, and display panel

Patent metadata

Field	Value
Publication number	US-11518939-B2
Application number	US-201916621670-A
Country	US
Kind code	B2
Filing date	Nov 5, 2019
Priority date	Sep 12, 2019
Publication date	Dec 6, 2022
Grant date	Dec 6, 2022

Abstract

A polymer-dispersed liquid crystal composition, a preparation method of a polymer-dispersed liquid crystal film, and a display panel are provided. The polymer-dispersed liquid crystal composition includes a prepolymer and a liquid crystal molecule, wherein the prepolymer is a fluorine-containing polyimide precursor chemically bonded to a polyaniline, including a polycondensation unit formed from a fluorine-containing dianhydride monomer and a fluorine-containing diamine monomer. In the present application, the conductive polyaniline is chemically bonded to the fluorine-containing polyimide precursor to increase the conductivity of the polyimide precursor. Further, a polymer-dispersed liquid crystal film having a driving voltage lower than 30 V and excellent insulating property and radiation resistance is obtained.

First claim

What is claimed is:

1. A polymer-dispersed liquid crystal composition, comprising a liquid crystal molecule and a prepolymer, wherein the prepolymer is a fluorine-containing polyimide precursor chemically bonded to a polyaniline, comprising a polycondensation unit formed from a fluorine-containing dianhydride monomer and a fluorine-containing diamine monomer; and wherein the fluorine-containing dianhydride monomer has any one of structures represented by formulas (i-1) to (i-3):

and
the fluorine-containing diamine monomer has any one of structures represented by formulas (ii-1) to (ii-4):

2. The polymer-dispersed liquid crystal composition according to claim 1 , wherein the prepolymer has a structure represented by formula (I):

wherein Ar1 is selected from any one of:

Ar2 is selected from any one of:

and
n is from 3 to 5.

3. The polymer-dispersed liquid crystal composition according to claim 1 , wherein a mass ratio of the prepolymer to the liquid crystal molecule is (70-90):(10-30).

4. A method for preparing a polymer-dispersed liquid crystal film, comprising:
a step of obtaining polyamic acid: reacting a monomer mixture at room temperature to obtain a;
a step of forming a polymer film: forming the polymer film by reacting the polyamic acid at a high temperature; and
a step of forming the polymer-dispersed liquid crystal film: mixing liquid crystal material and the polymer film, melting the mixed liquid crystal material and the polymer film, and cooling the melted mixed liquid crystal material and the polymer film to form the polymer-dispersed liquid crystal film;
wherein the prepolymer of the polymer-dispersed liquid crystal comprises a fluorine-containing dianhydride monomer, a fluorine-containing diamine monomer, and a polyaniline, and the fluorine-containing dianhydride monomer has any one of structures represented by formulas (i-1) to (i-3):

and the fluorine-containing diamine monomer has any one of structures represented by formulas (ii-1) to (ii-4):

5. The preparing method according to claim 4 , wherein the polyaniline has a structure represented by formula (iii):

n is from 3 to 5.

6. The preparing method according to claim 4 , wherein the monomer mixture further comprises a solvent.

7. The preparing method according to claim 6 , wherein the solvent is N-methyl pyrrolidone or N-ethyl pyrrolidone.

8. The preparing method according to claim 6 , wherein the solvent has a mass fraction of 90% based on a total mass of the monomer mixture.

9. The preparing method according to claim 4 , wherein in the monomer mixture, a molar ratio of the fluorine-containing dianhydride monomer, the fluorine-containing diamine monomer, and the polyaniline is 10:9:1.

10. The preparing method according to claim 4 , wherein in the step of forming the polymer film, reacting the obtained polyamic acid at 80° C. to 100° C. for 1 to 3 hours, and then further reacting the obtained polyamic acid at 200° C. to 230° C. for 1 to 3 hours to obtain the polymer film.

11. The preparing method according to claim 4 , wherein in the step of forming the polymer-dispersed liquid crystal film, a mass ratio of the liquid crystal material to the obtained polymer film is (70-90):(10-30).

12. The preparing method according to claim 4 , wherein in the step of forming the polymer-dispersed liquid crystal film, mixing the liquid crystal material with the obtained polymer film and then melted at a high temperature, and then cooled at a temperature drop rate of 5° C. to 10° C./minute to obtain the polymer-dispersed liquid crystal film.

13. A display panel, comprising a first substrate and an opposite substrate disposed in parallel with the first substrate; and a polymer-dispersed liquid crystal film interposed between the first substrate and the opposite substrate; wherein the polymer-dispersed liquid crystal film is made of the polymer-dispersed liquid crystal composition of claim 1 .

14. The display panel according to claim 13 , wherein the polymer-dispersed liquid crystal film is prepared by the method according to claim 4 .

15. The display panel according to claim 13 , wherein the display panel further comprises a first electrode and a second electrode, and the first electrode is disposed on a surface of the first substrate facing the opposite substrate, and the second electrode is disposed on a surface of the opposite substrate facing the first substrate, and the polymer-dispersed liquid crystal film contacts the first electrode and the second electrode.

16. The display panel according to claim 15 , wherein at least one of the first electrode and the second electrode is an indium tin oxide (ITO) thin-film electrode.

Assignees

• Shenzhen China Star Optoelectronics Semiconductor Display Tech Co Ltd

Inventors

• Lan Song

Classifications

• C09K19/544 Primary

  as dispersing or encapsulating medium around the liquid crystal · CPC title

• C08G73/1032

  characterised by the solvent(s) used · CPC title

• C08G73/1067

  Wholly aromatic polyimides, i.e. having both tetracarboxylic and diamino moieties aromatically bound · CPC title

• C08G73/1007 Primary

  from tetracarboxylic acids or derivatives and diamines · CPC title

• C08G73/1042

  Copolyimides derived from at least two different tetracarboxylic compounds or two different diamino compounds · CPC title