Corrosion protection with Al/Zn-based coatings

Patent metadata

Field	Value
Publication number	US-11512377-B2
Application number	US-202017015208-A
Country	US
Kind code	B2
Filing date	Sep 9, 2020
Priority date	Mar 13, 2009
Publication date	Nov 29, 2022
Grant date	Nov 29, 2022

Abstract

Red rust staining of Al/Zn coated steel strip in “acid rain” or “polluted” environments can be minimised by forming the coating as an Al—Zn—Si—Mg alloy coating with an OT:SDAS ratio greater than a value of 0.5:1, where OT is the overlay thickness on a surface of the strip and SDAS is the measure of the secondary dendrite arm spacing for the Al-rich alpha phase dendrites in the coating. Red rust staining in “acid rain” or “polluted” environments and corrosion at cut edges in marine environments can be minimised in Al—Zn—Si—Mg alloy coatings on steel strip by selection of the composition (principally Mg and Si) and solidification control (principally by cooling rate) and forming Mg2Si phase particles of a particular morphology in interdendritic channels.

First claim

The invention claimed is:

1. A method for forming a coating of a corrosion resistant Al—Zn—Si—Mg alloy on a metal strip, the method comprising:
(a) passing the metal strip through a molten bath of the Al—Zn—Si—Mg alloy and forming a coating of the alloy on one or both surfaces of the metal strip, with the alloy containing 45-60 wt. % Al, 35-50 wt. % Zn, 1.3-2.5 wt. % Si, 1.5-2.5 wt. % Mg, and optionally other elements in small amounts of less than 0.5 wt. % for each other element, with step (a) including forming the coating to have an overlay thickness of 5-20 μm, and with step (a) including forming the coating to have a total coating mass of less than 200 g per m 2 coating on both surfaces of the metal strip, which equates to less than 100 g per m 2 coating on one surface of the metal strip when the metal strip is coated on one surface only and the coating thickness is the same on both surfaces,
(b) solidifying the coating on the metal strip and forming a solidified coating having a microstructure that consists of dendrites of Al-rich alpha phase and interdendritic channels of Zn-rich eutectic phase mixture, extending from the metal strip to the coating surface, with the interdendritic channels being columnar or bamboo structure, and with particles of Mg 2 Si phase in the interdendritic channels, wherein the SDAS of the Al-rich alpha phase dendrites in the coating is greater than 3 μm but smaller than 20 μm, and
the method comprising controlling steps (a) and (b) to form the solidified coating with an OT:SDAS ratio greater than 0.5:1, where OT is the overlay thickness and SDAS is the secondary dendrite arm spacing for the Al-rich alpha phase dendrites of the coating,
wherein a cooling rate CR during coating solidification step (b) is maintained to be less than 170-4.5CT, where CR is the cooling rate in ° C./second and CT is the coating thickness on a surface of the metal strip in micrometres, and
(c) controlling the cooling rate during coating solidification step (b) such that the particles of Mg2Si phase in the interdendritic channels in the solidified coating block corrosion along the interdendritic channels, wherein greater than 60% of the interdendritic channels are blocked by particles of Mg 2 Si phase.

2. The method defined in claim 1 , wherein the Zn concentration is 39-48 wt. %.

3. The method defined in claim 1 , wherein the Mg concentration is 1.7-2.3 wt. %.

4. The method defined in claim 1 , wherein the metal strip is a steel strip.

5. The method defined in claim 1 , wherein the OT:SDAS ratio is greater than 1:1.

6. The method defined in claim 1 , wherein the OT:SDAS ratio is greater than 2:1.

7. The method defined in claim 1 , wherein greater than 70% of the total volume fraction of Mg 2 Si phase in the solidified coating is in the lower two thirds of the overlay thickness of the solidified coating.

Assignees

• Bluescope Steel Ltd

Inventors

• Smith Ross Mcdowall
• Liu Qiyang
• Shedden Bryan Andrew
• Neufeld Aaron Kiffer
• Williams Joe
• Nolan David James
• Renshaw Wayne

Classifications

• C23C2/12 Primary

  Aluminium or alloys based thereon · CPC title

• Y10T428/12028

  Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.] · CPC title

• C23C2/06 Primary

  Zinc or cadmium or alloys based thereon · CPC title

• Y10T428/12021

  having composition or density gradient or differential porosity · CPC title

• C23C2/14

  Removing excess of molten coatings; Controlling or regulating the coating thickness · CPC title