Composite pigment and production method thereof, paint composition containing composite pigment, and coating film

Patent metadata

Field	Value
Publication number	US-11512205-B2
Application number	US-201716343792-A
Country	US
Kind code	B2
Filing date	Oct 23, 2017
Priority date	Oct 24, 2016
Publication date	Nov 29, 2022
Grant date	Nov 29, 2022

Abstract

The purpose of the present invention is to provide a composite pigment which can be dispersed and made into paint in a manner that saves labor compared with conventional flat emulsion paints, and which can achieve concealing properties and low glossiness (a luster reduction effect) without separately adding a matting agent. This composite pigment contains an inorganic compound and/or an organic compound, and a fixed extender pigment.

First claim

The invention claimed is:

1. A composite pigment comprising:
extender pigment particles comprising barium sulfate; and
an inorganic compound comprising silica,
the composite pigment in which a plurality of the extender pigment particles are aggregated in a granular shape with the inorganic compound interposed between the particles,
wherein a content ratio of the extender pigment particles and the inorganic compound in the composite pigment is 0.3 to 3 parts by volume of the inorganic compound to 1 part by volume of the extender pigment particles, and
wherein the composite pigment having a diameter on cumulative 50% (D50) in a volume cumulative distribution measured by a laser diffraction/scattering-type particle size distribution measuring apparatus is 1 μm or more and 15 μm or less.

2. A matting pigment comprising the composite pigment set forth in claim 1 .

3. A method for producing a composite pigment comprising:
adjusting a pH of a slurry containing an inorganic compound source and extender pigment particles so that an inorganic compound derived from the inorganic compound source is precipitated to fix the extender pigment particles,
the composite pigment in which a plurality of the extender pigment particles are aggregated in a granular shape with the inorganic compound interposed between the particles,
wherein the extender pigment particles comprise barium sulfate and the inorganic compound comprises silica,
wherein a content ratio of the extender pigment particles and the inorganic compound in the composite pigment is 0.3 to 3 parts by volume of the inorganic compound to 1 part by volume of the extender pigment particles, and
wherein the composite pigment having a diameter on cumulative 50% (D50) in a volume cumulative distribution measured by a laser diffraction/scattering-type particle size distribution measuring apparatus is 1 μm or more and 15 μm or less.

4. A paint composition comprising the composite pigment set forth in claim 1 and a resin.

5. The paint composition according to claim 4 , further comprising a dispersant having an amine value.

6. A paint film comprising the paint composition set forth in claim 4 .

7. A paint composition comprising the matting pigment set forth in claim 2 , and a resin.

8. A matting pigment consisting essentially of:
a composite pigment in which a plurality of extender pigment particles are aggregated in a granular shape with an inorganic compound interposed between the particles,
wherein the extender pigment particles comprise barium sulfate and the inorganic compound comprises silica,
wherein a content ratio of the extender pigment particles and the inorganic compound in the composite pigment is 0.3 to 3 parts by volume of the inorganic compound to 1 part by volume of the extender pigment particles, and
wherein the matting pigment having a diameter on cumulative 50% (D50) in a volume cumulative distribution measured by a laser diffraction/scattering-type particle size distribution measuring apparatus is 1 μm or more and 15 μm or less.

9. The composite pigment according to claim 1 , wherein the inorganic compound has an aggregating property used to form the granular shape with the inorganic compound interposed between the extender pigment particles.

10. The method according to claim 3 , wherein the inorganic compound has an aggregating property used to form the granular shape with the inorganic compound interposed between the extender pigment particles.

11. The matting pigment according to claim 8 , wherein the inorganic compound has an aggregating property used to form the granular shape with the inorganic compound interposed between the extender pigment particles.

Assignees

• Ishihara Sangyo Kaisha

Inventors

• Fujimura Takeshi
• ISEYA Shogo
• SHIMOITA Hironori
• Taniguchi Yusuke

Classifications

• C09C1/3653

  Treatment with inorganic compounds · CPC title

• C09D7/45

  Anti-settling agents · CPC title

• C09C3/06 Primary

  Treatment with inorganic compounds {(C09C3/006, C09C3/048 take precedence)} · CPC title

• C09D133/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C01P2006/12

  Surface area · CPC title