Method for producing modified polytetrafluoroethylene, method for producing modified polytetrafluoroethylene powder, and method for producing stretched porous material

Patent metadata

Field	Value
Publication number	US-11512151-B2
Application number	US-202016814106-A
Country	US
Kind code	B2
Filing date	Mar 10, 2020
Priority date	Sep 28, 2017
Publication date	Nov 29, 2022
Grant date	Nov 29, 2022

Abstract

A method for producing a modified polytetrafluoroethylene, the method including: polymerizing tetrafluoroethylene in an aqueous medium in which a polymer having units based on a fluorine-free monomer is present. The fluorine-free monomer is a monomer represented by formula (1): CH2═CR1-L-R2, where R1 is a hydrogen atom or an alkyl group, L is a single bond, —CO—O—*, —O—CO—* or —O—, * is a bonding position to R2, and R2 is an alkyl group. To the total amount of tetrafluoroethylene supplied to the polymerization, a proportion of the polymer is from 0.001 to 0.050 mass %.

First claim

What is claimed is:

1. A method for producing a modified polytetrafluoroethylene, comprising:
polymerizing tetrafluoroethylene in an aqueous medium in which a polymer comprising units based on a fluorine-free monomer is present,
wherein the fluorine-free monomer is represented by the formula (1):
CH 2 ═CR 1 -L-R 2 ,  Formula (1)

where R 1 represents a hydrogen atom or an alkyl group, L represents a single bond, —CO—O—*, —O—CO—* or —O—, * represents a bonding position to R 2 , and R 2 represents an alkyl group, and
to a total amount of tetrafluoroethylene which is supplied during the polymerizing of tetrafluoroethylene, a proportion of the polymer is from 0.001 to 0.050 mass %.

2. The method according to claim 1 ,
wherein in the formula (1), R 1 represents a hydrogen atom or an alkyl group having from 1 to 3 carbon atoms, L represents —CO—O—* or —O—CO—*, * and R 2 represents an alkyl group having from 1 to 4 carbon atoms.

3. The method according to claim 1 , wherein a content proportion of the units based on the fluorine-free monomer in the polymer is from 90 to 100 mass % to a total amount of monomer units in the polymer.

4. The method according to claim 1 , wherein to the total amount of tetrafluoroethylene which is supplied during the polymerizing of tetrafluoroethylene, the proportion of the polymer is from 0.001 to 0.020 mass %.

5. The method according to claim 1 , wherein tetrafluoroethylene is polymerized in the presence of a fluorine-free surfactant.

6. The method according to claim 5 , wherein the fluorine-free surfactant is a hydrocarbon type surfactant.

7. The method according to claim 5 , wherein an amount of the fluorine-free surfactant in the aqueous medium, as expressed as a proportion to the total amount of tetrafluoroethylene which is supplied during the polymerizing of tetrafluoroethylene, is from 0.01 to 0.50 mass %.

8. The method according to claim 5 , wherein the fluorine-free surfactant comprises at least one selected from the group consisting of sodium dodecyl sulfate, sodium lauryl sulfate, ammonium lauryl sulfate, polyoxyethylene lauryl ether sodium sulfate, polyoxyethylene lauryl ether ammonium sulfate, sodium dodecylbenzenesulfonate, sodium di(2-ethylhexyl)sulfosuccinate, sodium laurate, and ammonium laurate.

9. The method according to claim 1 , wherein tetrafluoroethylene is polymerized in the presence of a stabilizing aid.

10. The method according to claim 1 , further comprising, prior to the polymerizing of tetrafluoroethylene:
polymerizing the fluorine-free monomer in an aqueous medium, thereby obtaining the aqueous medium containing the polymer,
wherein the polymerizing of tetrafluoroethylene is performed in the obtained aqueous medium containing the polymer.

11. The method according to claim 10 , wherein tetrafluoroethylene is polymerized by adding a polymerization initiator to the aqueous medium in which the fluorine-free monomer is polymerized, in such an amount that a proportion of the polymerization initiator becomes to be at least 0.10 mass % to the total amount of tetrafluoroethylene which is supplied during the polymerizing of tetrafluoroethylene.

12. The method according to claim 10 , wherein the polymerizing of tetrafluoroethylene is carried out while supplying tetrafluoroethylene to a polymerization system, and a fluorine-free surfactant is added to the polymerization system between the initiation and termination of the supply of tetrafluoroethylene.

13. The method according to claim 10 , wherein the aqueous medium in which the fluorine-free monomer is polymerized contains a stabilizing aid, and tetrafluoroethylene is polymerized in the obtained aqueous medium containing the stabilizing aid.

14. The method according to claim 13 , wherein the stabilizing aid is a paraffin wax.

15. A method for producing a modified polytetrafluoroethylene powder, comprising:
producing an aqueous dispersion having particles of a modified polytetrafluoroethylene dispersed in an aqueous medium by the method of claim 1 ; and then
coagulating the particles to produce a powder of a modified polytetrafluoroethylene.

16. A method for producing a stretched porous material, comprising:
producing a modified polytetrafluoroethylene powder by the method of claim 15 ;
subjecting the modified polytetrafluoroethylene powder to paste extrusion to obtain an extruded bead; and then
stretching the extruded bead to produce a stretched porous material.

17. The method according to claim 15 , wherein the particles of the modified polytetrafluoroethylene have an average primary particle size of from 0.10 to 0.50 μm.

18. The method according to claim 1 , wherein the fluorine-free monomer is represented by the formula (1-1) or formula (1-2):
CH 2 ═CR 1 —CO—O—R 3   Formula (1-1)

CH 2 ═CR 1 —O—CO—R 4   Formula (1-2)

where R 3 represents an alkyl group having from 1 to 6 carbon atoms, and R 4 represents an alkyl group having from 1 to 3 carbon atoms.

19. The method according to claim 1 , wherein the fluorine-free monomer is butyl methacrylate or vinyl acetate.

20. The method according to claim 1 , wherein tetrafluoroethylene is polymerized without using a fluorinated surfactant.

Assignees

• Agc Inc

Inventors

• Higuchi Shinya
• Ebata Shiro
• Kose Takehiro

Classifications

• C08F214/265

  with non-fluorinated comonomers · CPC title

• C08L27/18

  Homopolymers or copolymers or tetrafluoroethene · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title

• C08J2327/18

  Homopolymers or copolymers of tetrafluoroethylene · CPC title

• C08J3/16

  by coagulating dispersions {(C08J3/122 takes precedence)} · CPC title