Aqueous alkyd dispersions with improved application performances in terms of resistance to blocking and yellowing, hardness development and shine

Patent metadata

Field	Value
Publication number	US-11499047-B2
Application number	US-201716322533-A
Country	US
Kind code	B2
Filing date	Jul 21, 2017
Priority date	Aug 11, 2016
Publication date	Nov 15, 2022
Grant date	Nov 15, 2022

Abstract

The present invention relates to aqueous alkyd resin dispersions comprising a) a short oil alkyd resin comprising, in its fatty acid component a1), at least one polyunsaturated fatty monoacid a11) having at least two unsaturations per molecule and comprising at least 35% by weight of a monoacid a111) having conjugated unsaturations, the content by weight of said fatty monoacid a111), with respect to said alkyd resin, being at least 5%, preferably from 5% to 40% and more preferably from 5% to 35%, and b) at least one anionic phosphate surfactant. The invention also covers a preparation process and its use in decorative coatings. The coatings based on these aqueous dispersions exhibit improved performance qualities in resistance to blocking and yellowing, in development of hardness and in gloss.

First claim

The invention claimed is:

1. An aqueous alkyd resin dispersion comprising:
a) a short oil alkyd resin having a Noury viscosity at 110° C. according to AFNOR XPT 51213 ranging from 7000 to 13 000 mPa·s and comprising, in its fatty acid component a1), at least one polyunsaturated fatty monoacid a11) having at least two unsaturations per molecule and a content by weight of monoacid a111) having conjugated unsaturations of at least 35%, the content by weight of said fatty monoacid a111), with respect to said alkyd resin, being from 5% to 40%,
b) at least one anionic phosphate surfactant which is a phosphate alkyl alkoxy ester.

2. The aqueous dispersion of claim 1 , wherein said fatty monoacid a11) is a product of the dehydration of castor oil.

3. The aqueous dispersion of claim 1 wherein the acid number of said resin is less than 25 KOH/g.

4. The aqueous dispersion of claim 1 wherein said surfactant b) is a phosphate ester of a C 10 to C 16 alcohol which is alkoxylated with from 4 to 10 ethoxy units.

5. The aqueous dispersion of claim 4 wherein said surfactant b) comprises a phosphate diester and a phosphate monoester of said alcohol.

6. The aqueous dispersion as claimed in claim 1 wherein said surfactant b) is a mixture of phosphate monoester and of phosphate diester with the ratio by weight of the phosphate monoester to the phosphate diester being from 0.8 to 1.2.

7. The aqueous dispersion as claimed in claim 4 wherein said alcohol is a C 12 to C 14 alcohol.

8. The dispersion of claim 7 wherein the number of said alkoxy units is from 4 to 8.

9. The dispersion of claim 1 wherein the content by weight of said surfactant b) with respect to said dispersion varies from 1% to 3%.

10. The dispersion of claim 1 wherein the content by weight of said alkyd resin a) with respect to said dispersion varies from 35% to 65%.

11. The dispersion of claim 1 wherein said dispersion comprises, in addition to said surfactant b), a surfactant c) chosen from the group consisting of polymeric non-ionic surfactants with a ratio by weight of anionic surfactant b) to non-ionic surfactant c), b)/c), ranging from 1 to 3.

12. The dispersion of claim 1 wherein said resin comprises, in its acid component A, at least one aromatic dicarboxylic acid or anhydride a2) and optionally an aromatic monocarboxylic acid a3) and, in its alcohol component B, a polyol b1) with a functionality ranging from 3 to 6.

13. The dispersion as claimed in claim 1 wherein said alkyd resin additionally comprises, in its fatty acid component a1), at least one other non-conjugated polyunsaturated fatty monoacid a12) having at least two unsaturations per molecule and comprising at least 90% by weight of a non-conjugated polyunsaturated monoacid a121).

14. A process for the preparation of an aqueous dispersion of claim 1 , said process comprising the following successive stages:
i) Preparation of said alkyd resin a) in bulk,
ii) Melting said resin a),
iii) Addition of said surfactant b) and optionally of a non-ionic surfactant c),
iv) Partial addition of water, before
v) Neutralization of the acidity of a) and of b) by a base, said base selected from LiOH, KOH, NaOH, NH 4 OH and tertiary amines,
vi) Emulsification by phase inversion with adjustment of the solids content after the emulsification.

15. The process of claim 14 wherein stages ii) and iii) are carried out at a temperature ranging from 80 to 100° C., stage iv) at a temperature ranging from 80 to 65° C., stage v) at a temperature ranging from 60 to 70° C. and stage vi) at a temperature ranging from 55 to 65° C.

16. A coating composition comprising an aqueous dispersion of claim 1 .

17. The composition of claim 16 which is an aqueous paint, varnish or stain composition.

Assignees

• Arkema France

Inventors

• Riondel Alain
• Harlay Emile
• Kurczak Michael
• Mazajczyk Jerome
• Beurdeley Patricia
• Chaineau Cecile

Classifications

• C09D167/08 Primary

  Polyesters modified with higher fatty oils or their acids, or with natural resins or resin acids · CPC title

• C08G63/918

  Polycarboxylic acids and polyhydroxy compounds in which at least one of the two components contains aliphatic unsaturation · CPC title

• C08K5/521

  Esters of phosphoric acids, e.g. of H3PO4 · CPC title

• C08J3/05

  from solid polymers · CPC title

• C08L67/08 Primary

  Polyesters modified with higher fatty oils or their acids, or with resins or resin acids · CPC title