Zeolite membrane complex, method for producing zeolite membrane complex, and separation method

Patent metadata

Field	Value
Publication number	US-11498035-B2
Application number	US-202017015469-A
Country	US
Kind code	B2
Filing date	Sep 9, 2020
Priority date	Mar 30, 2018
Publication date	Nov 15, 2022
Grant date	Nov 15, 2022

Abstract

A zeolite membrane complex includes a porous support, and a zeolite membrane formed on the support. The zeolite membrane includes a zeolite crystal phase constituted by a plurality of zeolite crystals, and a dense grain boundary phase, which is a region between the plurality of zeolite crystals. A density of at least part of the grain boundary phase is smaller than a density of the zeolite crystal phase. A width of the grain boundary phase is 2 nm or more and 10 nm or less. Accordingly, it is possible to realize high permeability and high separating performance, and high durability of the zeolite membrane.

First claim

The invention claimed is:

1. A zeolite membrane complex comprising:
a porous support; and
a zeolite membrane formed on said support,
wherein said zeolite membrane includes
a zeolite crystal phase constituted by a plurality of zeolite crystals, and
a dense grain boundary phase, which is a region between said plurality of zeolite crystals,

a density of at least part of said grain boundary phase is smaller than a density of said zeolite crystal phase, and
a width of said grain boundary phase is 2 nm or more and 10 nm or less.

2. The zeolite membrane complex according to claim 1 , wherein the width of said grain boundary phase is 5 times or more and 27 times or less a pore size of said zeolite crystals contained in said zeolite crystal phase.

3. The zeolite membrane complex according to claim 1 , wherein the width of said grain boundary phase is 0.005 times or more and 0.12 times or less an average particle size of zeolite particles in said zeolite membrane.

4. The zeolite membrane complex according to claim 1 , wherein said grain boundary phase is constituted by an inorganic substance.

5. The zeolite membrane complex according to claim 1 , wherein said grain boundary phase contains an amorphous substance.

6. The zeolite membrane complex according to claim 1 , wherein an area of a portion of said grain boundary phase with a density that is smaller than a density of said zeolite crystal phase is 10% or more of an area of said entire grain boundary phase.

7. A method for producing a zeolite membrane complex, comprising the steps of:
a preparing a seed crystal;
b attaching said seed crystal to a porous support;
c immersing said support in a raw material solution, and causing zeolite to grow from said seed crystal through hydrothermal synthesis, thereby forming a zeolite membrane on said support,
wherein said zeolite membrane includes
a zeolite crystal phase constituted by a plurality of zeolite crystals, and
a dense grain boundary phase, which is a region between said plurality of zeolite crystals,

a density of at least part of said grain boundary phase is smaller than a density of said zeolite crystal phase, and
a width of said grain boundary phase is 2 nm or more and 10 nm or less.

8. The method for producing a zeolite membrane complex according to claim 7 , wherein, in said step c, solvent of said raw material solution does not contain an amine other than a structure-directing agent.

9. The method for producing a zeolite membrane complex according to claim 7 , wherein, in said step c, solvent of said raw material solution contains alcohol.

10. A separation method comprising the steps of:
a preparing the zeolite membrane complex according to claim 1 ; and
b supplying a mixture containing a plurality of types of gases or liquids to said zeolite membrane complex, and allowing a substance with high permeability in said mixture to permeate said zeolite membrane complex, thereby separating said substance from other substances.

11. The separation method according to claim 10 , wherein said mixture contains at least one of hydrogen, helium, nitrogen, oxygen, water, steam, carbon monoxide, carbon dioxide, nitrogen oxide, ammonia, sulfur oxide, hydrogen sulfide, sulfur fluoride, mercury, arsine, hydrogen cyanide, carbonyl sulfide, C1 to C8 hydrocarbons, organic acid, alcohol, mercaptans, ester, ether, ketone, and aldehyde.

Assignees

• Ngk Insulators Ltd

Inventors

• Kinoshita Naoto
• Ichikawa Makiko
• Yajima Kenji
• Miyahara Makoto
• Shimizu Katsuya

Classifications

• B01D2323/24

  Use of template or surface directing agents [SDA] · CPC title

• B01D69/105

  Support pretreatment · CPC title

• B01D53/228 Primary

  characterised by specific membranes · CPC title

• B82Y30/00

  Nanotechnology for materials or surface science, e.g. nanocomposites · CPC title

• C01B39/48

  using at least one organic template directing agent · CPC title