Water cured concrete mix composition

Patent metadata

Field	Value
Publication number	US-11485684-B2
Application number	US-201816168312-A
Country	US
Kind code	B2
Filing date	Oct 23, 2018
Priority date	Jun 28, 2016
Publication date	Nov 1, 2022
Grant date	Nov 1, 2022

Abstract

A cementitious blend composition and a concrete mix composition preferable for making concrete resistant to high temperatures and alkaline conditions, particularly for making durable concrete for constructing an alumina digester tank in an aluminum smelter. The cementitious blend composition includes at least one hydraulic cement, silica fume (SF), and natural pozzolan (NP), wherein a weight percent ratio of at least one hydraulic cement:SF:NP in the cementitious blend composition lies in the range of (24-63):(5-44):(32-40) with the sum of the weight percentages of the at least one hydraulic cement, the SF, and the NP not exceeding 100%. The concrete mix composition comprises water and the cementitious blend composition, wherein a weight ratio of the water to the cementitious blend composition is 0.2-0.5, and wherein the concrete mix composition has a content of the cementitious blend composition of 400-550 kg/m3.

First claim

The invention claimed is:

1. A water cured product of a concrete mix composition, consisting of:
a hydrated cementitious blend composition consisting of Portland cement, silica fume (SF), and natural pozzolan (NP), wherein the Portland cement, the silica fume, and the natural pozzolan are present in amounts of 255 kg/m 3 , 45 kg/m 3 and 160 kg/m 3 , respectively, based on a total weight of the cementitious blend composition being 460 kg/m 3 , and
at least one of a solid reinforcing material and an aggregate,
wherein the water cured product is obtained by hydrating the concrete mix composition at a weight ratio of water to the cementitious blend composition of 0.35, and
wherein the water cured product has a compressive strength of 60-90 MPa.

2. The water cured product of the concrete mix composition of claim 1 , wherein the water cured product has a reduction in compressive strength of 2-15% when exposed to an alkaline solution comprising 10-50% of one or more alkali hydroxides at 40-80° C. for 4-16 months as compared to the water cured product exposed to water at 15-35° C. for the same length of time.

3. The water cured product of the concrete mix composition of claim 1 , wherein the water cured product has a weight loss of 0-6% when exposed to an alkaline solution comprising 10-50% of one or more alkali hydroxides at 40-80° C. for 4-16 months as compared to the water cured product exposed to water at 15-35° C. for the same length of time.

4. The water cured product of the concrete mix composition of claim 1 , wherein the water cured product has a chloride permeability of 1200-2000 Coulombs when exposed to an alkaline solution comprising 10-50% of one or more alkali hydroxides at 40-80° C. for 12-16 months.

5. The water cured product of the concrete mix composition of claim 1 , wherein the water cured product has an expansion of 200-850 microns when exposed to an alkaline solution comprising 10-50% of one or more alkali hydroxides at 40-80° C. for 4-16 months.

6. The water cured product of the concrete mix composition of claim 1 , wherein a 40×40×160 mm prism specimen expands 740 microns after immersion in a caustic soda solution for 16 months as determined according to ASTM C157.

7. The water cured product of the concrete mix composition of claim 1 , wherein a cylinder specimen having a diameter of 75 mm and a height of 150 mm has a chloride permeability of 1,795 to 2,705 Coulombs after 16 months of exposure to a caustic soda solution according to ASTM C1202.

Assignees

• Univ King Fahd Pet & Minerals

Inventors

• Ibrahim Mohammed
• Barry Mohammed Salihu
• Maslehuddin Mohammed

Classifications

• C04B2111/802

  White cement · CPC title

• B01J2219/0245

  of synthetic organic material · CPC title

• B01J2219/0263

  Ceramic · CPC title

• B01J2219/025

  characterised by the construction materials of the reactor vessel proper · CPC title

• C04B2103/302

  Water reducers · CPC title