Laminated glazing comprising a stack of layers

Patent metadata

Field	Value
Publication number	US-11485115-B2
Application number	US-201816498968-A
Country	US
Kind code	B2
Filing date	Mar 26, 2018
Priority date	Mar 29, 2017
Publication date	Nov 1, 2022
Grant date	Nov 1, 2022

Abstract

A process for manufacturing a colored laminated glazing including first and second glass sheets, the two sheets being connected together by a thermoplastic interlayer, includes depositing a stack of layers including functional layer on a face of the first and/or of the second glass sheet, liquid deposition, on a face of the first and/or of the second glass sheet, of a polymer layer including a coloring agent and polymer compounds, drying and optionally curing of the polymer layer, assembling the glass sheet, coated with the colored polymer layer, with a colorless transparent thermoplastic interlayer and with the second glass sheet, so that the colored polymer layer is in direct contact with the interlayer, degassing, and heat treatment under pressure and/or under vacuum of the laminated glass at a temperature of between 100° C. and 200° C.

First claim

The invention claimed is:

1. A process for manufacturing a colored laminated glazing comprising at least a first and a second glass sheet, the first and second glass sheets being connected together by a thermoplastic interlayer, the process comprising:
depositing a stack of layers comprising at least one functional layer on at least one face of the first and/or of the second glass sheet,
liquid depositing, on at least one face of the first glass sheet, a colored polymer layer comprising a coloring agent and polymer compounds, wherein said coloring agent comprises an anthraquinone,
drying and optionally curing the colored polymer layer,
assembling the first glass sheet, coated with the colored polymer layer, with a colorless transparent thermoplastic interlayer and with the second glass sheet to form the laminated glazing, so that the colored polymer layer is in direct contact with said colorless transparent thermoplastic interlayer,
degassing, during which the air trapped between the first and second glass sheets and the thermoplastic interlayer is removed, and
laminating an assembly that comprises the first and second glass sheets, the stack of layers, the colored polymer layer and the colorless transparent thermoplastic interlayer by performing a heat treatment under pressure and/or under vacuum of the assembly at a temperature of between 100° C. and 200° C. during which the colored laminated glazing is assembled, the polymer compounds of the colored polymer layer being selected such that during said laminating the coloring agent present in the colored polymer layer migrates toward the thermoplastic interlayer.

2. The process as claimed in claim 1 , wherein the depositing of the stack of layers is carried out by magnetron sputtering.

3. The process as claimed in claim 1 , wherein the depositing of the colored polymer layer is carried out on the stack of layers.

4. The process as claimed in claim 1 , wherein the colored polymer layer is a layer obtained by curing a composition comprising epoxide compounds or methacrylate compounds.

5. The process as claimed in claim 1 , wherein the colored polymer layer is obtained from a liquid composition comprising (meth)acrylate compounds chosen from monomers, oligomers, or polymers comprising at least one methacrylate function.

6. The process as claimed in claim 5 , wherein the liquid composition comprises, as percentage by weight with respect to the total weight of the (meth)acrylate compounds, from 30% to 80% by weight of at least one aliphatic urethane-acrylic oligomer and from 20% to 70% by weight of at least one monofunctional or bifunctional (meth)acrylate monomer.

7. The process as claimed in claim 1 , wherein the coloring agent represents between 0.01% and 10% by weight, with respect to the total weight of the polymer compounds.

8. The process as claimed in claim 1 , wherein the colored polymer layer comprises an adhesion promoter.

9. The process as claimed in claim 1 , wherein the colored polymer layer is deposited by application, at ambient temperature, of a liquid composition, by roll coating, by flow coating, by dip coating, by curtain coating or by spray coating.

10. The process as claimed in claim 9 , wherein the liquid composition is applied by roll coating or by curtain coating.

11. The process as claimed in claim 1 , wherein the colored polymer layer is cured by drying at a temperature below 200° C., by UV crosslinking or by an electron beam.

12. The process as claimed in claim 1 , wherein a thickness of the cured and dried colored polymer layer is between 1 and 200 μm.

13. The process as claimed in claim 1 , further comprising treating the surface of the first glass sheet on which the colored polymer layer is deposited and/or the surface of the face of the thermoplastic interlayer in contact with the colored polymer layer, with an adhesion promoter.

14. The process as claimed in claim 1 , wherein the thermoplastic interlayer is polyvinyl butyral, polyethylene or ethylene/vinyl acetate.

15. A laminated glazing capable of being obtained by the process as claimed in claim 1 .

16. A process for manufacturing a colored laminated glazing comprising at least a first and a second glass sheet, the first and second glass sheets being connected together by a thermoplastic interlayer, the process comprising:
depositing a stack of layers comprising at least one functional layer on at least one face of the first and/or of the second glass sheet,
liquid depositing, on at least one face of the first glass sheet, a colored polymer layer comprising a coloring agent and polymer compounds, wherein said coloring agent comprises an anthraquinone,
drying and optionally curing the colored polymer layer,
assembling the first glass sheet, coated with the colored polymer layer, with a colorless transparent thermoplastic interlayer and with the second glass sheet to form the laminated glazing, so that the colored polymer layer is in direct contact with said colorless transparent thermoplastic interlayer,
degassing, during which the air trapped between the first and second glass sheets and the thermoplastic interlayer is removed, and
laminating an assembly that comprises the first and second glass sheets, the stack of layers, the colored polymer layer and the colorless transparent thermoplastic interlayer by performing a heat treatment under pressure and/or under vacuum of the assembly at a temperature of between 100° C. and 200° C. during which the colored laminated glazing is assembled, the polymer compounds of the colored polymer layer being selected such that during said laminating the coloring agent present in the colored polymer layer migrates toward the thermoplastic interlayer, wherein the colored polymer layer is obtained from a liquid composition that comprises at least one aliphatic urethane-acrylic oligomer, at least one monofunctional, bifunctional or trifunctional (meth)acrylate monomer, at least one polymerization initiator and said coloring agent.

17. The process as claimed in claim 16 , wherein the depositing of the stack of layers is carried out by magnetron sputtering.

18. The process as claimed in claim 16 , wherein the depositing of the colored polymer layer is carried out on the stack of layers.

19. A process for manufacturing a colored laminated glazing comprising at least a first and a second glass sheet, the first and second glass sheets being connected together by a thermoplastic interlayer, the process comprising:
depositing a stack of layers comprising at least one functional layer on at least one face of the first and/or of the second glass sheet,
liquid depositing, on at least one face of the first glass sheet, a colored polymer layer comprising a coloring agent and polymer compounds, wherein the colored polymer layer is obtained from a liquid composition that comprises at least one aliphatic urethane-acrylic oligomer, at least one monofunctional, bifunctional or trifunctional (meth)acrylate monomer, and at least one polymerization initiator, and wherein the coloring agent comprises an anthraquinone and represents between 0.01% and 10% by weight, with respect to the total weight of the polymer compounds,
drying and optionally curing the colored polymer layer,
assembling the first glass sheet, coated with the colored polymer layer, with a colorless transparent thermoplastic interlayer and with the second glass sheet to form the laminated glazing, so that the colored polymer layer is in direct contact with said interlayer,
degassing, during which the air trapped between the f

Assignees

• Saint Gobain

Inventors

• Compoint François
• De Grazia Marco
• Dalle-Ferrier Cécile

Classifications

• B32B17/10036 Primary

  comprising two outer glass sheets · CPC title

• B32B17/10908

  in liquid form · CPC title

• B32B17/10229

  Metallic layers sandwiched by dielectric layers · CPC title

• B32B17/10651 Primary

  comprising colorants, e.g. dyes or pigments · CPC title

• B32B17/10972

  Degassing during the lamination (B32B17/10816 takes precedence) · CPC title