Environmentally friendly aqueous coating composition

Patent metadata

Field	Value
Publication number	US-11472902-B2
Application number	US-201816484724-A
Country	US
Kind code	B2
Filing date	Feb 8, 2018
Priority date	Feb 8, 2017
Publication date	Oct 18, 2022
Grant date	Oct 18, 2022

Abstract

An aqueous emulsion is made by emulsion polymerizing at least one free-radically polymerizable monomer and one or more di- or higher-functional chain-extending monomers in the presence of an aqueous solution of an oligomer made from a mixture of free-radically polymerizable monomers including acid-functional free-radically polymerizable comonomers, adhesion-promoting free-radically polymerizable comonomers and other free-radically polymerizable comonomers. The aqueous emulsion is substantially free of adipic dihydrazide, has a minimum film forming temperature≤55° C., and on drying has a Koenig hardness of at least 40 sec.

First claim

The invention claimed is:

1. A method for making an aqueous emulsion, which method comprises:
a) oligomerizing a mixture of free-radically polymerizable monomers in aqueous solution, the mixture including 1 to 45 wt. % acid-functional free-radically polymerizable comonomer(s), 0.5 to 20 wt. % adhesion-promoting free-radically polymerizable comonomer(s), and 98.5 to 50 wt. % other free-radically polymerizable comonomer(s), to form a water-soluble oligomer having a number average molecular weight (Mn) of 500 to 50,000 and a glass transition temperature (Tg) of at least 70° C., the acid-functional comonomer(s) rendering the oligomer water-soluble per se or by neutralization and the adhesion-promoting comonomer(s) imparting improved adhesion to a wood, plastic, metal or cementitious substrate when a coating composition containing the aqueous emulsion is applied and dried on such substrate, and
b) emulsion polymerizing, in the presence of an aqueous solution of the oligomer, at least one free-radically polymerizable monomer and 0.1 to 20 wt. %, based on the weight of free-radically polymerizable monomer(s), of at least one di- or higher-functional chain-extending monomer(s), to form an aqueous emulsion of a hydrophobic polymer having a Tg at least 40° C. lower than the Tg of the oligomer, wherein the weight of oligomer is 5 to 50 wt. % of the weight of oligomer plus hydrophobic polymer, and the aqueous emulsion is substantially free of adipic dihydrazide and other hydrolyzable crosslinkers and has a minimum film forming temperature≤55° C. and on drying has a Koenig hardness of at least 40 sec.

2. A coating composition comprising an aqueous emulsion of a hydrophobic polymer made from at least one free-radically polymerizable monomer and 0.1 to 20 wt. %, based on the weight of free-radically polymerizable monomer(s), of at least one di- or higher-functional chain-extending monomer(s), the hydrophobic polymer having been emulsion polymerized in the presence of an aqueous solution of an oligomer made from a mixture of free-radically polymerizable monomers in aqueous solution, the mixture including 1 to 45 wt. % acid-functional free-radically polymerizable comonomer(s), 0.5 to 20 wt. % adhesion-promoting free-radically polymerizable comonomer(s), and 98.5 to 50 wt. % other free-radically polymerizable comonomer(s), the acid-functional comonomer(s) rendering the oligomer water-soluble per se or by neutralization and the adhesion-promoting comonomer(s) imparting improved adhesion to a wood, plastic, metal or cementitious substrate when the coating composition is applied and dried on such a substrate, the oligomer having an Mn of 500 to 50,000 and a Tg of at least 70° C., and the hydrophobic polymer having a Tg at least 40° C. lower than the Tg of the oligomer, wherein the weight of oligomer is 5 to 50 wt. % of the weight of oligomer plus hydrophobic polymer, and the aqueous emulsion is substantially free of adipic dihydrazide and other hydrolyzable crosslinkers, has a minimum film forming temperature≤55° C. and on drying has a Koenig hardness of at least 40 sec.

3. The coating composition according to claim 2 , wherein the acid-functional free-radically polymerizable comonomer(s) comprise carboxyl groups.

4. The coating composition according to claim 2 , wherein the adhesion-promoting free-radically polymerizable comonomer(s) comprise an aldehyde, ketone, ester, hydroxyl, silane or ureido group.

5. The coating composition according to claim 2 , wherein the adhesion-promoting free-radically polymerizable comonomer(s) comprise acetoacetoxyethyl methacrylate, diacetone acrylamide or mixture thereof.

6. The coating composition according to claim 2 , wherein the adhesion-promoting free-radically polymerizable comonomer(s) comprise a vinyl silane.

7. The coating composition according to claim 2 , wherein the oligomer is made from up to about 15 wt. % acid-functional free-radically polymerizable comonomer(s), up to about 5 wt. % adhesion-promoting free-radically polymerizable comonomer(s), and at least about 80 wt. % other free-radically polymerizable comonomer(s).

8. The coating composition according to claim 2 , wherein the oligomer has an Mn of about 2,500 to about 5,000, a Tg of 80 to 125° C. and is free of functional groups that would impart crosslinkability when the aqueous emulsion is applied and dried on a substrate.

9. The coating composition according to claim 2 , wherein the chain-extending monomer(s) comprise a di- or higher-functional acrylate or methacrylate; allyl acrylate or methacrylate; vinyl silane or acetoacetoxy ester of a hydroxyalkyl (meth)acrylate.

10. The coating composition according to claim 2 , wherein the chain-extending monomer(s) are difunctional monomers.

11. The coating composition according to claim 2 , wherein the hydrophobic polymer is formed from about 0.1 to about 3 wt. % chain-extending monomers and represents at least about 50 wt. % and up to about 95 wt. % of the combined weight of oligomer plus hydrophobic polymer.

12. The coating composition according to claim 2 , wherein the hydrophobic polymer has a Tg less than about −40° C.

13. The coating composition according to claim 2 , wherein the aqueous emulsion has a minimum film forming temperature of about 0 to about 55° C. and a Koenig hardness of about 60 to about 200 seconds.

14. The coating composition according to claim 2 , wherein the aqueous emulsion contains about 20 up to about 65 wt. % solids and two facing substrates coated with the dried aqueous emulsion and stored under a pressure of 1 kg/cm 2 for 1 hour at 23° C. do not exhibit blocking.

15. The coating composition according to claim 2 , wherein the coating composition is a glaze or a Lazure finish.

16. A coated article comprising a substrate having thereon a layer of a coating composition comprising an aqueous emulsion of a hydrophobic polymer made from at least one free-radically polymerizable monomer and 0.1 to 20 wt. %, based on the weight of free-radically polymerizable monomer(s), of at least one di- or higher-functional chain-extending monomer(s), the hydrophobic polymer having been emulsion polymerized in the presence of an aqueous solution of an oligomer made from a mixture of free-radically polymerizable monomers in aqueous solution, the mixture including 1 to 45 wt. % acid-functional free-radically polymerizable comonomer(s), 0.5 to 20 wt. % adhesion-promoting free-radically polymerizable comonomer(s), and 98.5 to 50 wt. % other free-radically polymerizable comonomer(s), the acid-functional comonomer(s) rendering the oligomer water-soluble per se or by neutralization and the adhesion-promoting comonomer(s) imparting improved adhesion to the substrate when the coating composition is dried, the oligomer having a number average molecular weight Mn of 500 to 50,000 and a glass transition temperature Tg of at least 70° C., and the hydrophobic polymer having a Tg at least 40° C. lower than the Tg of the oligomer, wherein the weight of oligomer is 5 to 50 wt. % of the weight of oligomer plus hydrophobic polymer, and the aqueous emulsion is substantially free of adipic dihydrazide, and other hydrolyzable crosslinkers and has a minimum film forming temperature≤55° C. and on drying has a Koenig hardness of at least 40 sec.

17. A coated article according to claim 16 , wherein the di- or higher-functional chain-extending monomers comprise 1,3-butanediol diacrylate, 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, ethylene glycol dimethacrylate, allyl methacrylate, vinyl trimethoxy silane or acetoacetoxyethyl methacrylate; the acid-functional free-radically polyme

Assignees

• Swimc Llc

Inventors

• Hearley Andrew

Classifications

• C08F2/22

  Emulsion polymerisation · CPC title

• C08F220/14

  Methyl esters {, e.g. methyl (meth)acrylate} · CPC title

• C08F220/06

  Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof · CPC title

• C08F230/085

  the monomer being a polymerisable silane, e.g. (meth)acryloyloxy trialkoxy silanes or vinyl trialkoxysilanes · CPC title

• C08F4/40

  Redox systems · CPC title