Coating material for formation of matte hard coat, and decorative sheet using same

Patent metadata

Field	Value
Publication number	US-11466111-B2
Application number	US-201716464068-A
Country	US
Kind code	B2
Filing date	Nov 14, 2017
Priority date	Nov 25, 2016
Publication date	Oct 11, 2022
Grant date	Oct 11, 2022

Abstract

Embodiments provide a coating material containing: (A) 100 parts by mass of an acrylic curable resin; (B) 5-200 parts by mass of aluminum oxide particles having an average particle size of 1-100 μm; (C) 0.1-20 parts by mass of aluminum oxide fine particles having an average particle size of 1-100 nm; and (D) 1-100 parts by mass of a compound having two or more isocyanate groups per molecule. In one embodiment, the acrylic curable resin (A) includes: (a1) a structural unit derived from a hydroxy group-containing (meth)acrylic acid ester; (a2) a structural unit derived from a vinyl aromatic compound; and (a3) a structural unit derived from a (meth)acrylic acid alkyl ester. In one embodiment, the acrylic curable resin (A) may contain, in addition to the structural units (a1) and (a2): (a3-1) a structural unit derived from methyl methacrylate; and (a3-2) a structural unit derived from an aliphatic (including alicyclic) alkyl ester having 4 or more carbon atoms of a (meth)acrylic acid.

First claim

The invention claimed is:

1. A coating material consisting of:
(A) 100 parts by mass of an acrylic curable resin;
(B) 5-250 parts by mass of aluminum oxide particles having an average particle diameter of 1-100 μm, the aluminum oxide particles being not treated by a surface treatment agent;
(C) 0.1-10 parts by mass of aluminum oxide fine particles having an average particle diameter of 1-100 nm, the aluminum oxide fine particles being treated by a surface treatment agent;
(D) 1-100 parts by mass of a compound having two or more isocyanate groups per molecule; and
optionally, at least one member selected from the group consisting of inorganic particles other than component (B) and component (C), compounds having an isocyanate group other than component (D), antistatic agents, surfactants, antifouling agents or stain-proofing agents, printing property-improving agents, antioxidants, weather-resistant stabilizers, light-resistant stabilizers, ultraviolet ray absorbers, heat stabilizers, organic particles, coloring agents and solvents,
wherein the acrylic curable resin (A) comprises: (a1) a structural unit derived from a hydroxyl group-containing (meth)acrylic acid ester; (a2) a structural unit derived from a vinyl aromatic compound; and (a3) a structural unit derived from a (meth)acrylic acid alkyl ester.

2. The coating material according to claim 1 , wherein the acrylic curable resin (A) comprises the structural unit derived from a hydroxyl group-containing (meth)acrylic acid ester (a1) in an amount of 5 to 40 mol %, with respect to 100 mol % of the total sum of structural units derived from all constituent monomers.

3. The coating material according to claim 1 , wherein the acrylic curable resin (A) comprises the structural unit derived from a vinyl aromatic compound (a2) in an amount of 10 to 50 mol %, with respect to 100 mol % of the total sum of structural units derived from all constituent monomers.

4. The coating material according to claim 1 , wherein the acrylic curable resin (A) comprises the structural unit derived from a (meth)acrylic acid alkyl ester (a3) in an amount of 20 to 85 mol %, with respect to 100 mol % of the total sum of structural units derived from all constituent monomers.

5. The coating material according to claim 1 , wherein the acrylic curable resin (A) comprises:
(a1) the structural unit derived from a hydroxyl group-containing (meth)acrylic acid ester;
(a2) the structural unit derived from a vinyl aromatic compound;
(a3-1) a structural unit derived from methyl methacrylate; and
(a3-2) a structural unit derived from an aliphatic alkyl ester having 4 or more carbon atoms of a (meth)acrylic acid.

6. The coating material according to claim 5 , wherein the acrylic curable resin (A) comprises the structural unit derived from methyl methacrylate (a3-1) in an amount of 10 to 50 mol %, with respect to 100 mol % of the total sum of structural units derived from all constituent monomers.

7. The coating material according to claim 5 , wherein the acrylic curable resin (A) comprises the structural unit derived from the aliphatic alkyl ester having 4 or more carbon atoms of a (meth)acrylic acid (a3-2) in an amount of 5 to 40 mol %, with respect to 100 mol % of the total sum of structural units derived from all constituent monomers.

8. An article comprising a hard coat formed from the coating material according to claim 1 .

9. A decorative sheet comprising a hard coat formed from the coating material according to claim 1 .

10. An article comprising the decorative sheet according to claim 9 .

Assignees

• Riken Technos Corp

Inventors

• Ito Shigekazu
• Inagaki Koji

Classifications

• C08F220/14

  Methyl esters {, e.g. methyl (meth)acrylate} · CPC title

• C09D7/67

  Particle size smaller than 100 nm · CPC title

• C09D175/04

  Polyurethanes · CPC title

• C08G18/6225

  Polymers of esters of acrylic or methacrylic acid · CPC title

• C09D125/06

  Polystyrene · CPC title