Adhesive composition based on ethylene copolymers, useful for extrusion-coating and extrusion-lamination on a variety of supports

Patent metadata

Field	Value
Publication number	US-11459477-B2
Application number	US-72171605-A
Country	US
Kind code	B2
Filing date	Dec 13, 2005
Priority date	Dec 16, 2004
Publication date	Oct 4, 2022
Grant date	Oct 4, 2022

Abstract

The invention concerns an adhesive composition consisting of at least one ethylene polymer or copolymer, said composition comprising at least one unsaturated carboxylic acid ester comonomer, and at least one functional comonomer, useful in an extrusion-coating process for application on a support or in an extrusion-lamination process for bonding together several supports of different type or not, in a wide temperature range. The invention is characterized in that said composition has an unsaturated carboxylic acid ester content higher than 5 wt % and in that the functional comonomer consists of at least one reactive function in the form of an acid group, anhydride or epoxy, whereof the proportion is less than 1 wt % of the composition. Said composition has advantageous uses, in particular for bonding together substrates selected among aluminum, paper or cardboard, cellophane, films based of polyethylene, polypropylene, polyamide, polyester, polyvinyl chloride (PVC), polyvinylidene chloride (PVDC), polyacrylonitrile (PAN) resins, oriented or not, metal-coated or not, physically or chemically treated or not and films coated with a thin inorganic barrier layer, such as polyester (PET, SiOx or AlOx).

First claim

The invention claimed is:

1. A multilayer structure comprising:
a) an adhesive composition consisting of:
at least one ethylene polymer or copolymer;
at least one alkyl methacrylate, the alkyl group having from 1 to 24 carbon atoms; and
at least one functional comonomer,

wherein said alkyl methacrylate(s) are present at from 6 to 25 weight percent of the composition and
wherein said functional comonomer comprises at least one reactive function in the form of maleic anhydride, wherein in said adhesive composition the content of maleic anhydride is between 0.15% and 0.6% by weight of the composition, wherein the adhesive composition is extruded at temperatures ranging from 290 to 320° C. to form the multilayer structure, and
b) a support, wherein said support is chosen from aluminum; paper or board; cellophane; films based on polyethylene, polypropylene, polyamide, polyester, polyvinyl chloride (PVC), polyvinylidene chloride (PVDC) or polyacrylonitrile (PAN) resins, wherein said films are oriented or unoriented, metallized or unmetallized, treated or untreated by physical or chemical means; and films coated with a thin inorganic barrier layer, wherein said multi-layer structure is formed by an extrusion-coating process or an extrusion lamination process.

2. A multilayer structure comprising:
a) an adhesive composition consisting of:
at least one ethylene polymer or copolymer;
at least one alkyl methacrylate, the alkyl group having from 1 to 24 carbon atoms; and
at least one functional comonomer,

wherein said alkyl methacrylate(s) are present at from 6 to 25 weight percent of the composition and
wherein said functional comonomer comprises at least one reactive function in the form of acid, anhydride or epoxide group, the level of which is less than 1% by weight of the composition, wherein the adhesive composition is extruded at temperatures ranging from 300° C. to 320° C. to form the multilayer structure, and
b) a support, wherein said support is a polyethylene terephthalate;
wherein said multi-layer structure is formed by an extrusion-coating process or an extrusion lamination process.

3. The multilayer structure as claimed in claim 2 , wherein the adhesive composition consists of the at least one ethylene polymer or copolymer, at least one alkyl methacrylate, and the at least one functional comonomer.

4. A multilayer structure comprising:
a) an adhesive composition comprising at least one ethylene polymer or copolymer, at least one unsaturated carboxylic acid ester type comonomer, and at least one functional comonomer, wherein said unsaturated carboxylic acid ester type comonomer is at least one alkyl methacrylate, the alkyl group having from 1 to 24 carbon atoms, and wherein said alkyl methacrylate(s) are present at from 10 to 25 weight percent of the composition and wherein said functional comonomer is maleic anhydride, the level of which is between 0.05% and 0.9% by weight of the composition, wherein the adhesive composition is formed by high-pressure radical polymerization of all the comonomers in a single step, wherein the adhesive composition is extruded at temperatures ranging from 290° C. to 300° C. to form the multilayer structure, and
b) a support, wherein said support is aluminum film; wherein said multi-layer structure is formed by an extrusion-coating process or an extrusion lamination process.

5. The multilayer structure as claimed in claim 4 , wherein the adhesive composition consists of the at least one ethylene polymer or copolymer, at least one alkyl methacrylate, and the at least one functional comonomer.

6. A multilayer structure comprising:
a) an adhesive composition comprising at least one ethylene polymer or copolymer, at least one unsaturated carboxylic acid ester type comonomer, and at least one functional comonomer, wherein said unsaturated carboxylic acid ester type comonomer is at least one alkyl methacrylate, the alkyl group having from 1 to 24 carbon atoms, and wherein said alkyl methacrylate(s) are present at from 10 to 25 weight percent of the composition and
wherein said functional comonomer comprises at least one reactive function in the form of an acid, anhydride or epoxide group, the level of which is less than 1% by weight of the composition, wherein the adhesive composition is extruded at temperatures ranging from 310° C. to 320° C. to form the multilayer structure, and
b) a support, wherein said support is chosen from aluminum film, wherein said multi-layer structure is formed by an extrusion-coating process or an extrusion lamination process.

7. The multilayer structure as claimed in claim 6 , wherein in said adhesive composition the functional comonomer is chosen from unsaturated carboxylic acid anhydrides.

8. The multilayer structure as claimed in claim 6 , wherein the adhesive composition is formed by melt-blending at least two ethylene copolymers obtained by high-pressure radical polymerization, of which one at least comprises the functional comonomer.

9. The multilayer structure as claimed in claim 6 , wherein the adhesive composition consists of the at least one ethylene polymer or copolymer, at least one alkyl methacrylate, and the at least one functional comonomer.

10. The multilayer structure as claimed in claim 6 , wherein in said adhesive composition said functional monomer is maleic anhydride.

11. A multilayer structure according to claim 6 , wherein the adhesive composition is formed by high-pressure radical polymerization of all the comonomers in a single step.

12. A multilayer structure according to claim 6 , wherein the functional comonomer comprises at least one reactive function in the form of an acid, anhydride or epoxide group, the level of which is between 0.05% and 0.9% by weight of the composition.

13. The multilayer structure as claimed in claim 6 , wherein in said adhesive composition said functional monomer is maleic anhydride.

Assignees

• Pascal Jerome
• Chopinez Fabrice
• Rauline Damien
• Sk Global Chemical Co Ltd

Inventors

• Pascal Jerome
• Chopinez Fabrice
• Rauline Damien

Classifications

• Y10T428/31935

  Ester, halide or nitrile of addition polymer · CPC title

• Y10T428/3154

  Of fluorinated addition polymer from unsaturated monomers · CPC title

• Y10T428/31699

  Ester, halide or nitrile of addition polymer · CPC title

• Y10T428/31797

  Next to addition polymer from unsaturated monomers · CPC title

• C09J123/0869

  Acids or derivatives thereof · CPC title