Three component composition for the manufacture of primer layer or scratch coating for flooring

Patent metadata

Field	Value
Publication number	US-11459273-B2
Application number	US-201816634513-A
Country	US
Kind code	B2
Filing date	Aug 22, 2018
Priority date	Aug 23, 2017
Publication date	Oct 4, 2022
Grant date	Oct 4, 2022

Abstract

A three component composition consisting of a polyol component (A) including at least two polyols, one with high, one with low molecular weight and water, a polyisocyanate component (B) including a methylene diphenyl diisocyanate (MDI) product with an average NCO functionality of at least 2.5, or a methylene diphenyl diisocyanate (MDI) product with an average NCO functionality of at least 2 and at least one further polyol with an amount of between 1% and 30% based on the weight of the polyisocyanate component (B), wherein the MDI product and the polyol have reacted at least partially, and a powder component (C) including at least one hydraulic binder, preferably cement and/or calcined paper sludge, preferably a calcium compound selected from calcium hydroxide and/or calcium oxide, and optionally one or more aggregates.

First claim

The invention claimed is:

1. A three component composition consisting of
a) a polyol component (A), the polyol component (A) being
at least one polyol P1a with a number average molecular weight of 800 to 30,000 g/mol, whereby the polyol P1a is:

a polyhydroxy-functional fat and/or a polyhydroxy-functional oil or
a polyol obtained by chemical modification of natural fats and/or natural oils, and
at least one polyol P1b with a number average molecular weight of 48 to 800 g/mol, and
water;

b) a polyisocyanate component (B), the polyisocyanate component (B) being
a methylene diphenyl diisocyanate (MDI) product optionally with up to 0.05% by weight of any other additives, the MDI product being either
a polymeric MDI with an average NCO functionality of at least 2.5, or
a mixture of monomeric MDI and polymeric MDI, the monomeric MDI and polymeric MDI being present in the mixture in amounts such that an average NCO functionality of the mixture is at least 2.5;

c) a powder component (C), the powder component (C) being at least one hydraulic binder;
wherein 2-(Dimethylamino)ethanol is present in the three component composition,
and wherein the weight ratio of components (A+B) to component (C) ((A+B)/(C)) is in the range of 2:1.5 to 2:3.5, wherein components (A+B) represents the combined weight of component (A) and component (B); and
wherein at least one tertiary amine tAM of the formula

is present in the three component composition, where R 1 is an alkylene group having 1 to 20 carbon atoms, which is optionally substituted, and n has a value of 1 to 3, whereby the molar ratio of the tertiary amine tAM to the OH-groups of the polyol P1a is between 0.0003 and 0.0042, and the molar ratio of the 2-(Dimethylamino)ethanol to the OH-groups of the polyol P1a is between 0.0008 and 0.0042.

2. The three component composition according to claim 1 , wherein, R 1 is CH 2 or —CH 2 —NH—C 3 H 6 and n is 1-3.

3. The three component composition according to claim 1 , wherein the tertiary amine tAM is selected from the group consisting of 2-(dimethylaminomethyl) phenol, 2,6-bis (dimethylaminomethyl) phenol, 2,4-bis (dimethylaminomethyl) phenol, 2,4,6-tris (dimethylaminomethyl) phenol and 2,4,6-tris (((3-(dimethylamino) propyl) amino) methyl) phenol.

4. The three component composition according to claim 1 , wherein the weight ratio of components (A+B) to component (C) ((A+B)/(C)) is in the range of 2:2.5 to 2:3.5, wherein components (A+B) represents the combined weight of component (A) and component (B).

5. The three component composition according to claim 1 , wherein the weight ratio of components (A+B) to component (C) ((A+B)/(C)) is in the range of 2:1.5 to 2:2.5, wherein components (A+B) represents the combined weight of component (A) and component (B).

6. The three component composition according to claim 1 , wherein said polyol P1a is present in component (A) at an amount of 20 to 75% by weight, based on the total weight of component (A), and said polyol P1b is present in component (A) at an amount of 1 to 25%, by weight, based on the total weight of component (A).

7. The three component composition according to claim 1 , wherein said at least one polyol P1b of component (A) has an average OH functionality of 1.6 to 6.

8. The three component composition according to claim 1 , wherein the water is present in component (A) at an amount of 20 to 40%, based on the total weight of component (A), and/or wherein the weight ratio of the water hi component (A) to polyol P1 b is in the range of 0.8 to 40, and/or wherein the weight ratio of the water in component (A) to hydraulic binder in component (C) is in the range of 0.1 to 0.7.

9. The three component composition according to claim 1 , wherein the weight ratio of component (A) to component (B) is in the range of 0.7 to 1.4.

10. The three component composition according to claim 1 having an open time between 15 min and 5 hours at temperatures between 5 and 35° C. at 50% relative humidity, whereby the open time is measured by having applied a freshly mixed three component composition in films of 3 mm thickness and pulling a spatula with a thickness of 2 mm (immersion depth 2 mm) through the film, whereby the end of the open time is reached when the composition does not close a remaining mark anymore and the measurement of the open time starts after mixing of the material.

11. The three component composition according to claim 1 , wherein the MDI product is the polymeric MDI and contains up to 0.05% by weight of any other additives.

12. A method for the manufacture of a polyurethane cementitious hybrid primer or scratch coat with the three component composition according to claim 1 , wherein the method comprises
a) mixing polyol component (A) and polyisocyanate component (B),
b) adding the powder component (C) to the mixture of polyol component (A) and polyisocyanate component (B) and mixing, to obtain a mixed material,
c) applying the mixed material to a substrate
d) optionally smoothing the applied mixed material, and
e) curing the applied mixed material, to obtain the polyurethane cementitious hybrid primer or scratch coat.

13. A method comprising applying the three component composition according to claim 1 to a substrate as a primer or scratch coat with a thickness of 1-2 mm.

Assignees

• Sika Tech Ag

Inventors

• Gimeno Patricia
• Kaddatz Carola
• Grötzinger Jochen

Classifications

• C08G18/3206

  aliphatic · CPC title

• C04B22/064

  of the alkaline-earth metals · CPC title

• C08G18/1825 Primary

  having hydroxy or primary amino groups · CPC title

• C04B24/282 Primary

  Polyurethanes; Polyisocyanates · CPC title

• C08G2150/00

  Compositions for coatings · CPC title