Methods of producing bonded magnet and compound for bonded magnets

Patent metadata

Field	Value
Publication number	US-11440091-B2
Application number	US-201916251956-A
Country	US
Kind code	B2
Filing date	Jan 18, 2019
Priority date	Jan 22, 2018
Publication date	Sep 13, 2022
Grant date	Sep 13, 2022

Abstract

Included is a method of preparing a compound for bonded magnets, the method including: coating a magnetic material having an average particle size of 10 μm or less with a thermosetting resin and a curing agent at a ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin of 2 or higher and 10 or lower to obtain a coated material; granulating the coated material by compression to obtain a granulated product; milling the granulated product to obtain a milled product; and surface treating the milled product with a silane coupling agent to obtain a compound for bonded magnets, the method either including, between the granulation and the milling, heat curing the granulated product to obtain a cured product, or including, between the milling and the surface treatment, heat curing the milled product to obtain a cured product.

First claim

What is claimed is:

1. A method of preparing a compound for bonded magnets, the method comprising:
coating a magnetic material having an average particle size of 10 μm or less with a thermosetting resin and a curing agent at a ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin of 2.2 or higher and 10 or lower to obtain a coated material;
granulating the coated material by compression to obtain a granulated product;
milling the granulated product to obtain a milled product;
the method either comprising heat curing the granulated product between the granulation and the milling to obtain a cured product, or comprising heat curing the milled product to obtain a cured product; and
surface treating the cured product with a silane coupling agent to obtain a compound for bonded magnets so that the silane coupling agent exists on a surface of the cured product.

2. The method of preparing a compound for bonded magnets according to claim 1 ,
wherein the coating comprises mixing the thermosetting resin in an amount of 0.15 parts by weight or more and 0.65 parts by weight or less with respect to 100 parts by weight of the magnetic material.

3. The method of preparing a compound for bonded magnets according to claim 1 ,
wherein the method comprises heat curing the milled product between the milling and the surface treatment.

4. The method of preparing a compound for bonded magnets according to claim 1 ,
wherein the milled product has an average particle size of 1000 μm or less.

5. A method of preparing a bonded magnet, the method comprising:
coating a magnetic material having an average particle size of 10 μm or less with a thermosetting resin and a curing agent at a ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin of 2.2 or higher and 10 or lower to obtain a coated material;
granulating the coated material by compression to obtain a granulated product;
milling the granulated product to obtain a milled product;
the method either comprising heat curing the granulated product between the granulation and the milling to obtain a cured product, or comprising heat curing the milled product to obtain a cured product;
surface treating the cured product with a silane coupling agent to obtain a compound for bonded magnets so that the silane coupling agent exists on a surface of the cured product;
orientation injection molding the compound for bonded magnets to obtain a molded product; and
magnetizing the molded product in a magnetizing field of 25 kOe or higher.

6. The method of producing a bonded magnet according to claim 5 ,
wherein the coating comprises mixing the thermosetting resin in an amount of 0.15 parts by weight or more and 0.65 parts by weight or less with respect to 100 parts by weight of the magnetic material.

7. The method of producing a bonded magnet according to claim 5 ,
wherein the method comprises heat curing the milled product between the milling and the surface treatment.

8. The method of producing a bonded magnet according to claim 5 ,
wherein the milled product has an average particle size of 1000 μm or less.

9. The method of producing a bonded magnet according to claim 5 ,
wherein the magnetization is followed by heat treating the magnetized bonded magnet.

10. A method of preparing a bonded magnet, the method comprising:
preparing a compound for bonded magnets according to the method of claim 1 ;
melt-kneading the compound for bonded magnets with a thermoplastic resin to obtain a compound for injection molding;
orientation injection molding the compound for injection molding to obtain a molded product; and
magnetizing the molded product in a magnetizing field of 25 kOe or higher.

11. The method of preparing a compound for bonded magnets according to claim 1 , wherein the milled product has an average particle size of 30 μm or more and 1000 μm or less.

12. The method of preparing a compound for bonded magnets according to claim 1 , wherein the ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin in the coating step is 5.59 or higher and 10 or lower.

13. The method of preparing the bonded magnets according to claim 5 , wherein the ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin in the coating step is 5.59 or higher and 10 or lower.

14. A method of preparing a compound for bonded magnets, the method comprising:
coating a magnetic material having an average particle size of 10 μm or less with a thermosetting resin and a curing agent at a ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin of 2.2 or higher and 11.09 or lower to obtain a coated material;
granulating the coated material by compression to obtain a granulated product;
milling the granulated product to obtain a milled product;
the method either comprising heat curing the granulated product between the granulation and the milling to obtain a cured product, or comprising heat curing the milled product to obtain a cured product; and
surface treating the cured product with a silane coupling agent to obtain a compound for bonded magnets so that the silane coupling agent exists on a surface of the cured product.

15. The method of preparing a compound for bonded magnets according to claim 14 , wherein the ratio of the equivalent weight of the curing agent to the equivalent weight of the thermosetting resin in the coating step is 5.59 or higher and 11.09 or lower.

Assignees

• Nichia Corp

Inventors

• Yamanaka Satoshi
• Yano Takayuki

Classifications

• B22F1/148

  Agglomerating · CPC title

• B22F1/052

  characterised by a mixture of particles of different sizes or by the particle size distribution · CPC title

• B22F1/102 Primary

  Metallic powder coated with organic material · CPC title