Coating material for gas barrier, gas barrier film, and laminated body

Patent metadata

Field	Value
Publication number	US-11427715-B2
Application number	US-202117205131-A
Country	US
Kind code	B2
Filing date	Mar 18, 2021
Priority date	Jul 31, 2014
Publication date	Aug 30, 2022
Grant date	Aug 30, 2022

Abstract

A coating material for a gas barrier includes polycarboxylic acid, a polyamine compound, a polyvalent metal compound, and a base, in which (molar number of —COO— groups included in the polycarboxylic acid)/(molar number of amino groups included in the polyamine compound)=100/20 to 100/90.

First claim

The invention claimed is:

1. A laminated body comprising:
a substrate layer; and
a gas barrier film layer provided on at least one surface of the substrate layer,
wherein the gas barrier film layer is formed of a gas barrier film,
wherein the gas barrier film is a cured product of a coating material for a gas barrier,
wherein the coating material for a gas barrier comprising a polycarboxylic acid, a polyamine compound, a polyvalent metal compound, and a base,
wherein (molar number of —COO— groups included in the polycarboxylic acid)/(molar number of amino groups included in the polyamine compound)=100/25 to 100/90 in the coating material for a gas barrier,
wherein the polyamine compound includes polyethylene imine, and
wherein (a chemical equivalent of —COO— groups included in the polycarboxylic acid)/(a chemical equivalent of polyvalent metal contained in the polyvalent metal compound)=100/0.1 to 100/80 in the coating material for a gas barrier,
wherein the substrate layer is selected from the group consisting of a paper and a plastic film that contains a thermoplastic resin,
wherein the thickness of the substrate layer is 1 to 1000 μm,
wherein the oxygen permeability at 20° C. and 90% RH at a thickness of 1 μm of the gas barrier film layer is 5 ml/m 2 ·day·MPa or less, and
wherein, in an infrared absorption spectrum of the gas barrier film layer, when a total peak area in a range of an absorption band of equal to or more than 1493 cm −1 and equal to or less than 1780 cm −1 is A and a total peak area in a range of an absorption band of equal to or more than 1598 cm −1 and equal to or less than 1690 cm −1 is B, an area ratio of an amide bond which is indicated by B/A is 0.370 or more.

2. The laminated body according to claim 1 ,
wherein an inorganic compound or an oxide of an inorganic compound is deposited on the surface of the substrate layer.

3. The laminated body according to claim 1 ,
wherein the polycarboxylic acid includes at least one selected from the group consisting of polyacrylic acid, polymethacrylic acid, and a copolymer of acrylic acid and methacrylic acid.

4. The laminated body according to claim 1 ,
wherein the polyvalent metal compound includes one or two or more of divalent or higher valency metal selected from the group consisting of Mg, Ca, Zn, Ba and Al.

5. The laminated body according to claim 1 ,
wherein the polyvalent metal compound includes one or two or more of divalent metal compound selected from the group consisting of magnesium oxide, calcium oxide, barium oxide, zinc oxide, magnesium hydroxide, calcium hydroxide, barium hydroxide, and zinc hydroxide.

6. The laminated body according to claim 1 ,
wherein the base includes ammonia.

Assignees

• Mitsui Chemicals Tohcello Inc
• Mitsui Chemicals Tochello Inc

Inventors

• Kidokoro Masako
• Nomoto Akira

Classifications

• C08J7/048

  Forming gas barrier coatings · CPC title

• B32B27/30

  comprising vinyl {(co)polymers; comprising acrylic (co)polymers} · CPC title

• C08J2479/02

  Polyamines · CPC title

• C09D7/40

  Additives · CPC title

• C08K3/22

  of metals · CPC title