Thin aluminum pigments having a narrow thickness distribution, method for producing same, and use of aluminum pigments

Patent metadata

Field	Value
Publication number	US-11427712-B2
Application number	US-201916544151-A
Country	US
Kind code	B2
Filing date	Aug 19, 2019
Priority date	Dec 22, 2006
Publication date	Aug 30, 2022
Grant date	Aug 30, 2022

Abstract

The invention relates to aluminum pigments which are at least partially coated with lubricant, wherein the aluminum pigments have a relative breadth of thickness distribution Δh of from 30% to less than 70%, as determined by a scanning electron microscope thickness count and as calculated on the basis of the corresponding cumulative breakthrough curve of the relative frequencies of occurrence, according to the formula Δh=100×(h 90 −h 10 )/h 50 , and an X-ray diffractogram, measured on pigments in substantially plane-parallel orientation, having one or two main peaks which do not correspond to the [111] reflexes.
The invention further relates to a method for the production of said aluminum pigments and to uses thereof and also to nail varnishes and printing inks containing said aluminum pigments of the invention.

First claim

The invention claimed is:

1. Platelet-like aluminum pigments having a narrow thickness distribution and at least partially coated with lubricant, wherein the pigments have
a) a mean thickness h 50 of from 15 nm to 75 nm as determined by a scanning electron microscope thickness count,
b) a relative breadth of thickness distribution Δh of from 30% to 65%, as determined by a scanning electron microscope thickness count and as calculated on the basis of the corresponding cumulative breakthrough curve of the relative frequencies of occurrence, according to the formula Δh=100×(h 90 −h 10 )/h 50 , and
c) an X-ray diffractogram, measured on pigments in substantially plane-parallel orientation, having one or two main peaks which do not correspond to the reflexes.

2. The platelet-type aluminum pigments according to claim 1 , wherein said aluminum pigments are produced by grinding processes.

3. The platelet-type aluminum pigments according to claim 1 wherein said aluminum pigments exhibit a relative breadth of said thickness distributions Δh of from 35% to 65%.

4. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments have a form factor d 50 /h 50 of from 200 to 1500.

5. The platelet-type aluminum pigments as defined in claim 1 , wherein the X-ray diffractogram has one or two peaks of maximum intensity assignable to at least one of the and reflexes.

6. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments are coated at least partially with fatty acids as lubricants.

7. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments are coated at least partially with stearic acid as lubricant.

8. The platelet-type aluminum pigments as defined in claim 1 , wherein said aluminum pigments are coated at least partially with oleic acid as lubricant.

9. The platelet-type aluminum pigments as defined in claim 1 , wherein said aluminum pigments are coated at least partially with a mixture of stearic acid and oleic acid as lubricants.

10. The platelet-type aluminum pigments as defined in claim 1 , wherein said aluminum pigments are at least partially coated with phosphonic acids, phosphates, or a mixture thereof as lubricants.

11. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments are coated with a passivating inhibitory layer or anticorrosive layer.

12. The platelet-type aluminum pigments as defined in claim 11 , wherein said passivating inhibitory layer comprises at least one selected from the group consisting of anticorrosive organic phosphonic acids and phosphoric acid esters, organically functionalized silanes, aliphatic and cyclic amines, aliphatic and aromatic nitro compounds, heterocyclic compounds containing at least one heterocyclic atom selected from the group consisting of oxygen, sulfur and nitrogen, and sulfur and nitrogen compounds of higher ketones, aldehydes, and alcohols, thiols, and mixtures thereof.

13. The platelet-type aluminum pigments as defined in claim 11 , wherein said passivating anti-corrosive layer comprises at least one selected from the group consisting of silicon dioxide, zirconium oxide, aluminum oxide, chromium oxide, polymerized synthetic resins, vanadium oxides, molybdenum oxides and peroxides, phosphates, phosphates, borates, and mixtures and combinations thereof.

14. The platelet-type aluminum pigments as defined in claim 13 , wherein said passivating anti-corrosive layer comprises silicon dioxide.

15. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments are oxidized by water in a chemical wet process and the aluminum pigments have a colored appearance.

16. The platelet-type aluminum pigments as defined in claim 1 , wherein the aluminum pigments exist as powders.

17. A method for the production of aluminum effect pigments as defined in claim 1 , wherein the method comprises the following steps:
a) providing aluminum shot exhibiting a particle size distribution having a d shot,10 <3.0 μm, a d shot,50 <5.0 μm, and a d shot,90 <8.0 μm,
b) grinding the aluminum shot defined under a) using a grinder in the presence of solvent and lubricants and grinding media having an individual weight of from 1.2 mg to 13 mg.

18. The method as defined in claim 17 , wherein said grinding media have an individual weight of from 5.0 mg to 12 mg.

19. The method as defined in claim 17 wherein said aluminum shot as produced according to step a) has a particle size distribution having a d shot,10 <0.6 μm, a d shot,50 <2.0 μm, and a d shot,90 <4.0 μm.

20. The method as defined in claim 17 , wherein the grinding time is from 15 to 100 hours.

21. The method as defined in claim 17 , wherein said aluminum pigments are subjected in a further step (c) to size classification.

22. The method as defined in claim 17 , wherein the aluminum pigments provided in said step b) are converted to a compact form.

23. The method as defined in claim 17 , wherein the aluminum pigments provided in said step b) are converted to an aluminum powder.

24. The method as defined in claim 17 , wherein the solvents used are organic solvents.

25. The method as defined in claim 17 , wherein the solvent used is water and the lubricants used are at least one selected from the group consisting of organic phosphonic acids and esters thereof and phosphoric acids and esters thereof.

26. A cosmetic formulation, wherein said cosmetic formulation contains aluminum pigments as defined in claim 1 .

27. A printing ink, wherein said printing ink contains aluminum pigments as defined in claim 1 .

28. The cosmetic formulation of claim 26 , wherein the formulation is a nail varnish.

29. A water-based lacquer, wherein said lacquer contains coated aluminum pigments as defined in claim 11 .

30. A coating composition adapted for exterior application, wherein said coating contains coated aluminum pigments as defined in claim 11 .

31. A method for producing a composition selected from the group consisting of coating, lacquers, printing inks, powder-based ceramics and cosmetic formulations, said method comprising incorporating aluminum pigments as defined in claim 1 in said composition.

32. The platelet-type aluminum pigments defined in claim 14 , wherein a surface of the silicon dioxide layer is coated with silanes.

33. The platelet-type aluminum pigments as defined in claim 16 , wherein the powder is a non-dusting powder.

34. The platelet-type aluminum pigments as defined in claim 16 , wherein the powder is in a paste or in a compacted form selected from the group consisting of granules, pellets, tablets, small cylinders and briquets.

35. The method as defined in claim 22 , which further comprises selecting the compact form from the group consisting of paste, granules, tablets, small cylinders, briquets and pellets.

36. The method as defined in claim 23 wherein the aluminum powder is a non-dusting aluminum powder.

37. The method as defined in claim 24 , which further comprises selecting the organic solvent from the group consisting of white spirit, solvent naphtha, isopropanol, alcohols, ketones and mixtures thereof.

38. A method for producing a reve

Assignees

• Eckart Gmbh

Inventors

• Trummer Stefan
• Becker Michael
• Schlegl Thomas

Classifications

• C01P2004/54

  Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension · CPC title

• C09C1/644

  treated with organic compounds, e.g. polymers · CPC title

• C09C1/64 Primary

  Aluminium · CPC title

• C09C1/646

  concomitant with mechanical comminution, shaping or abrasion of the particles · CPC title

• C01P2002/72

  by d-values or two theta-values, e.g. as X-ray diagram · CPC title