Polystyrene compositions for foam extrusion

Patent metadata

Field	Value
Publication number	US-11414529-B2
Application number	US-201816014883-A
Country	US
Kind code	B2
Filing date	Jun 21, 2018
Priority date	Jun 21, 2018
Publication date	Aug 16, 2022
Grant date	Aug 16, 2022

Abstract

A polystyrene (PS) composition for making an extruded foam, the PS composition comprising polystyrene, a blowing agent, and an additive selected from glycerol monostearate (GMS), glycerol tri-stearate (GTS), mineral oil (MO), epoxidized soy oil (ESO), epoxidized polybutadiene, or combinations thereof. Methods of producing a low density polystyrene (PS) foam are also provided.

First claim

What is claimed is:

1. A polystyrene (PS) composition for making an extruded foam having an increased blowing agent concentration and/or blowing agent retention relative to an extruded foam made from a same PS composition absent a solubility and/or retention additive, the PS composition consisting essentially of:
polystyrene;
a blowing agent consisting of carbon dioxide;
the solubility and/or retention additive selected from mineral oil (MO), epoxidized polybutadiene, or a combination thereof; and
one or more additional additives selected from stabilizers, costabilizers, talc, UV stabilizers, lubricants, plasticizers, ultraviolet screening agents, oxidants, anti-static agents, ultraviolet light absorbents, processing oils, mold release agents, pigments, dyes, fillers, fragrances, odor masking agents, foaming aids, and deterioration inhibitors,
wherein an amount of the solubility and/or retention additive is selected such that extrusion of the PS composition produces the extruded foam having the increased blowing agent concentration and/or blowing agent retention relative to the extruded foam made from a same PS composition absent the solubility and/or retention additive;
wherein the polystyrene is selected from PS copolymers containing a metallic monomer, glycidyl methacrylate, or 2-hydroxylethyl methacrylate.

2. The PS composition of claim 1 comprising from about 0.01 to 10.0 weight percent (wt %) of the solubility and/or retention additive, said weight percentages being based on the total amount of the polystyrene and the solubility and/or retention additive in the PS composition.

3. The PS composition of claim 1 , wherein the retention additive consists of the MO.

4. The PS composition of claim 1 , wherein the polystyrene has a melt flow rate (MFR), as measured by ASTM D-1238 in the range of from 0.2 to 30 grams (g)/10 minutes (min).

5. A low density polystyrene (PS) foam produced via extrusion of the PS composition of claim 1 , wherein the low density PS foam contains the increased blowing agent concentration relative to the extruded foam made from the same PS composition absent the solubility and/or retention additive.

6. A low density polystyrene (PS) foam produced via extrusion of the PS composition of claim 1 , wherein the low density PS foam exhibits at least one superior insulative property relative to that of an otherwise similar low density foam that does not contain the solubility and/or retention additive.

7. A low density polystyrene (PS) foam produced via extrusion of the PS composition of claim 1 , wherein the low density PS foam exhibits at least one mechanical property that is at least comparable to that of an otherwise similar low density foam that does not contain the solubility and/or retention additive.

8. A polystyrene (PS) composition for making an extruded foam having an increased blowing agent concentration and/or blowing agent retention relative to an extruded foam made from a same PS composition absent a solubility and/or retention additive, the PS composition consisting essentially of:
polystyrene;
a blowing agent consisting of carbon dioxide;
the solubility and/or retention additive consists of epoxidized polybutadiene; and
one or more additional additives selected from stabilizers, costabilizers, talc, UV stabilizers, lubricants, plasticizers, ultraviolet screening agents, oxidants, anti-static agents, ultraviolet light absorbents, processing oils, mold release agents, pigments, dyes, fillers, fragrances, odor masking agents, foaming aids, and deterioration inhibitors,
wherein an amount of the solubility and/or retention additive is selected such that extrusion of the PS composition produces the extruded foam having the increased blowing agent concentration and/or blowing agent retention relative to the extruded foam made from a same PS composition absent the solubility and/or retention additive.

9. A low density polystyrene (PS) foam produced via extrusion of the PS composition of claim 8 , wherein the low density PS foam exhibits at least one insulative property that is at least equivalent to that of an otherwise similar low density foam produced in the absence of the solubility and/or retention additive and with one or more blowing agents selected from hydrofluorocarbons (HFCs).

10. A method of increasing a blowing agent concentration and/or a blowing agent retention relative to an extruded foam made from a same foamable mixture absent a solubility and/or retention additive during the producing of a low density polystyrene (PS) foam, the method comprising:
forming a foamable mixture consisting of polystyrene (PS), a blowing agent, the solubility and/or retention additive, wherein the solubility and/or retention is selected from mineral oil (MO), epoxidized polybutadiene, or a combination thereof, and one or more additional additives selected from stabilizers, costabilizers, talc, UV stabilizers, lubricants, plasticizers, ultraviolet screening agents, oxidants, anti-static agents, ultraviolet light absorbents, processing oils, mold release agents, pigments, dyes, fillers, fragrances, odor masking agents, foaming aids, coloring agents, and deterioration inhibitors wherein the blowing agent comprises one or more hydrofluoroolefins (HFOs) or comprises the one or more HFOs and carbon dioxide as a co-blowing agent;
producing the extruded foam by extruding the foamable mixture through a die and into a region of reduced pressure; and
optimizing an amount of the solubility and/or retention additive such that the extruded foam has an increased blowing agent concentration and/or blowing agent retention relative to an extruded foam made from a same foamable mixture absent the solubility and/or retention additive and retains at least one desired mechanical property of the extruded foam.

11. The method of claim 10 , wherein the foamable mixture comprises from about 0.01 to 10.0 weight percent (wt %) of the solubility and/or retention additive.

12. The method of claim 10 , wherein the solubility of the blowing agent in the foamable mixture is at least 5% greater than the solubility of the blowing agent in an otherwise similar foamable mixture absent the solubility and/or retention additive.

13. The method of claim 10 , wherein the PS is selected from crystal polystyrene, high impact polystyrene (HIPS), PS copolymers, or a combination thereof.

14. A method of increasing a blowing agent concentration and/or a blowing agent retention relative to an extruded foam made from a same foamable mixture absent a solubility and/or retention additive during the producing of a low density polystyrene (PS) foam, the method comprising:
forming a foamable mixture consisting of polystyrene (PS), a blowing agent, the solubility and/or retention additive, wherein the solubility and/or retention is selected from mineral oil (MO), epoxidized polybutadiene, or a combination thereof, and one or more additional additives selected from stabilizers, costabilizers, talc, UV stabilizers, lubricants, plasticizers, ultraviolet screening agents, oxidants anti-static agents, ultraviolet light absorbents, processing oils, mold release agents, coloring agents, pigments, dyes, fillers, fragrances, odor masking agents, foaming aids, and deterioration inhibitors, wherein the blowing agent comprises one or more hydrofluoroolefins (HFOs) or comprises the one or more HFOs and carbon dioxide as a co-blowing agent;
producing the extruded foam by extruding the foamable mixture through a die and into a region of reduced pressure; and
optimizing an amount of the solubility and/or retention additive such that the extruded foam has an increased blowing agent co

Assignees

• Fina Technology

Inventors

• Li Fengkui
• Brown Jayna
• Wang Ying
• Stephens Wyman T

Classifications

• B29C44/20

  for articles of indefinite length · CPC title

• C08J2201/03

  Extrusion of the foamable blend · CPC title

• B29K2105/0005

  containing compounding ingredients (releasing, lubricating or separating agents B29C33/56, fibers B29K2105/08, B29K2105/12; fillers B29K2105/16, recycled material B29K2105/26) · CPC title

• C08K5/103

  with polyalcohols · CPC title

• C08J9/0023

  containing oxygen · CPC title