Threaded connection for oil country tubular goods and method for producing threaded connection for oil country tubular goods

Patent metadata

Field	Value
Publication number	US-11408550-B2
Application number	US-201816613525-A
Country	US
Kind code	B2
Filing date	May 10, 2018
Priority date	May 22, 2017
Publication date	Aug 9, 2022
Grant date	Aug 9, 2022

Abstract

This invention provides a threaded connection for oil country tubular goods that exhibits excellent corrosion resistance and galling resistance, and a method for producing the threaded connection for oil country tubular goods. The method includes a Zn—Ni alloy plating layer formation step of forming a Zn—Ni alloy plating layer, and a chromate coating formation step of forming a chromate coating after the Zn—Ni alloy plating layer formation step. The chromate coating formation step includes a chromate treatment step and a drying step. The chromate coating formation step satisfy one or more conditions selected from the following conditions 1 to 3.Condition 1: stirring speed of the chromating solution in the chromate treatment step: a linear speed of 0.5 m/s or more;Condition 2: chromate treatment time in the chromate treatment step: less than 50 seconds; andCondition 3: drying temperature in the drying step: 60° C. or less.

First claim

The invention claimed is:

1. A threaded connection for oil country tubular goods, the threaded connection comprising:
a pin having a pin-side contact surface including a pin-side threaded portion;
a box having a box-side contact surface including a box-side threaded portion;
a Zn—Ni alloy plating layer consisting of a Zn—Ni alloy and impurities on at least one of the pin-side contact surface and the box-side contact surface; and
a chromate coating on the Zn—Ni alloy plating layer,
wherein a lightness L value of the chromate coating surface is 45 or more and less than 65.

2. The threaded connection for oil country tubular goods according to claim 1 , wherein:
a coating amount of the chromate coating is 10 to 300 mg/m 2 expressed in terms of chromium.

3. The threaded connection for oil country tubular goods according to claim 2 , wherein:
the pin-side contact surface further includes a pin-side metal seal portion and a pin-side shoulder portion; and
the box-side contact surface further includes a box-side metal seal portion and a box-side shoulder portion.

4. The threaded connection for oil country tubular goods according to claim 1 , wherein:
the pin-side contact surface further includes a pin-side metal seal portion and a pin-side shoulder portion; and
the box-side contact surface further includes a box-side metal seal portion and a box-side shoulder portion.

5. A method for producing a threaded connection for oil country tubular goods according to claim 1 ,
the threaded connection for oil country tubular goods comprising a pin having a pin-side contact surface including a pin-side threaded portion, and a box having a box-side contact surface including a box-side threaded portion,
the method comprising:
a Zn—Ni alloy plating layer formation step of immersing at least one of the pin-side contact surface and the box-side contact surface in a plating solution containing zinc ions and nickel ions, and forming a Zn—Ni alloy plating layer consisting of a Zn—Ni alloy and impurities on at least one of the pin-side contact surface and the box-side contact surface by electroplating; and
a chromate coating formation step of forming a chromate coating having a lightness L value of the surface of 45 or more and less than 65 on the Zn—Ni alloy plating layer after the Zn—Ni alloy plating layer formation step,
wherein the chromate coating formation step includes:
a chromate treatment step of immersing the pin-side contact surface and/or the box-side contact surface having the Zn—Ni alloy plating layer formed thereon in a chromating solution containing chromium ions to perform a chromate treatment; and
a drying step of performing a drying treatment on the pin-side contact surface and/or the box-side contact surface after the chromate treatment step,
wherein the chromate coating formation step satisfies one or more conditions selected from the following condition 1 to condition 3:
Condition 1: stirring speed of the chromating solution in the chromate treatment step: linear speed of 0.5 m/s or more;
Condition 2: chromate treatment time in the chromate treatment step: less than 50 seconds; and
Condition 3: drying temperature in the drying step: 60° C. or less.

6. The method for producing a threaded connection for oil country tubular goods according to claim 5 , wherein:
the chromate coating formation step satisfies at least the condition 1, and
the chromate coating formation step further comprises, after the chromate treatment step and before the drying step, a non-stirring immersion step of immersing the pin-side contact surface and/or the box-side contact surface in the chromating solution for a certain time period while the stirring of the chromating solution is stopped.

7. The method for producing a threaded connection for oil country tubular goods according to claim 6 , wherein:
the pin-side contact surface further includes a pin-side metal seal portion and a pin-side shoulder portion, and the box-side contact surface further includes a box-side metal seal portion and a box-side shoulder portion.

8. The method for producing a threaded connection for oil country tubular goods according to claim 5 , wherein:
the pin-side contact surface further includes a pin-side metal seal portion and a pin-side shoulder portion, and the box-side contact surface further includes a box-side metal seal portion and a box-side shoulder portion.

Assignees

• Nippon Steel Corp
• Vallourec Oil & Gas France

Inventors

• Kimoto Masanari
• Oshima Masahiro

Classifications

• C23C22/77 Primary

  Controlling or regulating of the coating process · CPC title

• C23C28/345

  with at least one oxide layer · CPC title

• C23C28/322

  only coatings of metal elements only · CPC title

• C23C28/021

  including at least one metal alloy layer · CPC title

• C22C38/04

  containing manganese · CPC title