β-spodumene glass-ceramics that are white, opalescent, or opaque, with low titanium content, and tin-fined

Patent metadata

Field	Value
Publication number	US-11401202-B2
Application number	US-201816632740-A
Country	US
Kind code	B2
Filing date	Jul 19, 2018
Priority date	Jul 21, 2017
Publication date	Aug 2, 2022
Grant date	Aug 2, 2022

Abstract

The present application relates to glass-ceramics that are white, opalescent or opaque, of the lithium aluminosilicate (LAS) type, containing a solid solution of β-spodumene as the main crystalline phase. The application also provides articles that are constituted, at least in part, of said glass-ceramics, precursor glasses for said glass-ceramics, and a method of preparing said article. Said glass-ceramics have a composition that is free from arsenic oxide and antimony oxide, with the exception of inevitable traces, and that contains the following, expressed as percentages by weight of oxides: 60% to 70% of SiO2, 18% to 23% of Al2O3, 3.0% to 4.3% of Li2O, 0 to 2% of MgO, 1 to 4% of ZnO, 0 to 4% of BaO, 0 to 4% of SrO, 0 to 2% of CaO, 1.3% to 1.75% of TiO2, 1% to 2% of ZrO2, 0.05% to 0.6% of SnO2, 0 to 2% of Na2O, 0 to 2% of K2O, 0 to 2% of P2O5, 0 to 2% of B2O3, with Na2O+K2O+BaO+SrO+CaO≤6% and Na2O+K2O≤2%, and a maximum of 500 ppm of Fe2O3.

First claim

The invention claimed is:

1. A glass-ceramic that is white, opalescent or opaque, of the lithium aluminosilicate (LAS) type, containing a solid solution of β-spodumene as the main crystalline phase, the composition of which, exempt of arsenic oxide and antimony oxide, with the exception of inevitable traces, comprises, expressed as percentages by weight of oxides:
60% to 70% of SiO 2 ,
18% to 23% of Al 2 O 3 ,
3.0% to 4.3% of Li 2 O,
0 to 2% of MgO,
1 to 4% of ZnO,
0 to 4% of BaO,
0 to 4% of SrO,
0 to 2% of CaO,
1.3% to 1.75% of TiO 2 ,
1% to 2% of ZrO 2 ,
0.05% to 0.6% of SnO 2 ,
0 to 2% of Na 2 O,
0 to 2% of K 2 O,
0 to 2% of P 2 O 5 ,
0 to 2% of B 2 O 3 ,

with Na 2 O+K 2 O+BaO+SrO+CaO≤6% and Na 2 O+K 2 O≤2%, and a maximum of 500 ppm of Fe 2 O 3 , wherein
the glass-ceramic comprises an optical transmission (Y) greater than or equal to 0.1% for a 4 mm thick panel.

2. The glass-ceramic according to claim 1 , the composition of which comprises ZrO 2 at a content greater than or equal to 1.5% and less than or equal to 1.9%.

3. The glass-ceramic according to claim 1 , the composition of which comprises 0.1 to 4% of BaO.

4. The glass-ceramic according to claim 1 , the composition of which comprises Na 2 O: 0-1%, K 2 O:0-1%, with Na 2 O+K 2 O+BaO+SrO+CaO≤5% and Na 2 O+K 2 O≤1.5%.

5. The glass-ceramic according to claim 1 , the composition of which comprises Na 2 O: 0-1%, K 2 O: 0-1%, with Na 2 O+K 2 O+BaO+SrO+CaO≤5% and Na 2 O+K 2 O≤1%.

6. The glass-ceramic according to claim 1 , the composition of which comprises an Al 2 O 3 content greater than 20%.

7. The glass-ceramic according to claim 6 , the composition of which comprises a MgO content less than or equal to 1.2%.

8. The glass-ceramic according to claim 1 , the composition of which comprises a BaO+SrO content less than or equal to 1.5% and a CaO content greater than or equal to 0.5%; the composition of which is free of SrO, with the exception of inevitable traces, and comprises a BaO content less than or equal to 1.5%.

9. The glass-ceramic according to claim 6 , the composition of which is exempt, with the exception of inevitable traces, of P 2 O 5 or B 2 O 3 .

10. The glass-ceramic according to claim 1 , the composition of which contains an Al 2 O 3 content less than or equal to 20%.

11. The glass-ceramic according to claim 10 , the composition of which contains an MgO content greater than 1.2%.

12. The glass-ceramic according to claim 10 , the composition of which contains:
0 to 1.5% of BaO,
0 to 1.5% of SrO,
0 to 1% of Na 2 O,
0 to 1% of K 2 O,
<1% of P 2 O 5 ,
<1% of B 2 O 3 ,
with Na 2 O+K 2 O+BaO+SrO+CaO≤5% and Na 2 O+K 2 O≤1%.

13. An article that is constituted, at least in part, by the glass-ceramic according to claim 1 , comprising a cooktop, a worktop, a cooking utensil, a microwave oven plate, or a support for heat treatment.

14. A method of preparing an article according to claim 13 , the method comprising in succession:
melting a charge of vitrifiable raw materials, followed by fining the resulting molten glass;
cooling the resulting fined molten glass and simultaneously shaping it into the shape desired for the intended article; and
applying ceramming heat treatment to the shaped glass, which heat treatment comprises a first step of nucleation and a second step of crystal growth;
wherein said charge of vitrifiable raw materials has a composition making it possible to obtain the glass-ceramic; and wherein said ceramming heat treatment comprises a crystal growth second step that is performed at least in part at a temperature higher than 1000° C.

Assignees

• Eurokera

Inventors

• Lehuede Philippe
• Comte Marie

Classifications

• C03C3/087

  containing calcium oxide, e.g. common sheet or container glass · CPC title

• C03C2204/00

  Glasses, glazes or enamels with special properties · CPC title

• C03B32/02

  Thermal crystallisation, e.g. for crystallising glass bodies into glass-ceramic articles {(C03B27/012 takes precedence)} · CPC title

• C03C3/085

  containing an oxide of a divalent metal · CPC title

• C03C10/0054

  containing PbO, SnO2, B2O3 · CPC title