Inorganic filler, polyarylene sulfide resin composition, molded article, and methods for producing same

Patent metadata

Field	Value
Publication number	US-11390744-B2
Application number	US-201816626319-A
Country	US
Kind code	B2
Filing date	Jul 2, 2018
Priority date	Jul 3, 2017
Publication date	Jul 19, 2022
Grant date	Jul 19, 2022

Abstract

More specifically, provided are a polyarylene sulfide resin composition including 100 parts by mass of a polyarylene sulfide resin and 1 to 100 parts by mass of an inorganic filler surface-treated with a sizing agent, wherein the sizing agent is a sizing agent (α) containing at least a urethane-modified epoxy resin having an alkoxy polyoxyalkylene structure and a urethane resin having a sulfonate group, a sizing agent (β) containing a copolymer (β1) having a mass average molecular weight of 5000 to 150000, which is obtained by radical copolymerization of a polymerizable monomer mixture of at least a (meth)acrylic acid ester and maleic acid (anhydride), or a sizing agent (γ) containing at least a polyether resin, a urethane resin, and a silane coupling agent, a molded article thereof, an inorganic filler used for the composition, and methods for producing them.

First claim

The invention claimed is:

1. A polyarylene sulfide resin composition comprising:
100 parts by mass of a polyarylene sulfide resin (1); and
1 to 100 parts by mass of an inorganic filler (2) surface-treated with a sizing agent,
wherein the sizing agent is a sizing agent (γ) containing at least a polyether resin (γ1), a urethane resin (γ2), and a silane coupling agent (γ3),
wherein the polyether resin (γ1) is selected from the group consisting of polyoxypropylene glycol, polyoxytetramethylene glycol, and an alkyleneoxide adduct of bisphenol having 2 to 4 carbon atoms,
wherein the urethane resin (γ2) is formed from a polyol selected from the group consisting of polyethylene glycol, polypropylene glycol, polyoxyethylene oxypropylene glycol, and polyoxytetramethylene glycol, and
wherein at least one resin selected from the group consisting of the polyether resin (γ1) and the urethane resin (γ2) has a polyoxytetramethylene glycol group in the repeating unit.

2. The polyarylene sulfide resin composition according to claim 1 , further comprising a silane coupling agent (3) in an amount of 0.01 to 5 parts by mass with respect to 100 parts by mass of the polyarylene sulfide resin (1).

3. A molded article comprising a product obtained by molding the polyarylene sulfide resin composition according to claim 1 .

4. A method for producing a polyarylene sulfide resin composition of claim 1 , comprising blending 1 to 100 parts by mass of the inorganic filler (2) surface-treated with the sizing agent with respect to 100 parts by mass of the polyarylene sulfide resin (1), and melt-kneading the mixture.

5. The method for producing a polyarylene sulfide resin composition according to claim 4 , wherein the polyarylene sulfide resin (1) and the inorganic filler (2) surface-treated with a sizing agent are further blended with a silane coupling agent (3) in an amount of 0.01 to 5 parts by mass with respect to 100 parts by mass of the polyarylene sulfide resin (1), followed by melt-kneading.

6. A method for producing a molded article, comprising melt molding the polyarylene sulfide resin composition obtained by the method according to claim 4 .

7. An inorganic filler used in a polyarylene sulfide resin composition containing a polyarylene sulfide resin (1), wherein the inorganic filler is surface-treated with a sizing agent, and the sizing agent is a sizing agent (γ) containing at least a polyether resin (γ1), a urethane resin (γ2), and a silane coupling agent (γ3) wherein the polyether resin (γ1) is selected from the group consisting of polyoxypropylene glycol, polyoxytetramethylene glycol, and an alkyleneoxide adduct of bisphenol having 2 to 4 carbon atoms,
wherein the urethane resin (γ2) is formed from a polyol selected from the group consisting of polyethylene glycol, polypropylene glycol, polyoxyethylene oxypropylene glycol, and polyoxytetramethylene glycol, and
wherein at least one resin selected from the group consisting of the polyether resin (γ1) and the urethane resin (γ2) has a polyoxytetramethylene glycol in the repeating unit.

8. A method for producing an inorganic filler used in a polyarylene sulfide resin composition including a polyarylene sulfide resin (1), comprising surface-treating the inorganic filler with a sizing agent, wherein the sizing agent is a sizing agent (γ) containing at least a polyether resin (γ1), a urethane resin (γ2), and a silane coupling agent (γ3) wherein the polyether resin (γ1) is selected from the group consisting of polyoxypropylene glycol, polyoxytetramethylene glycol, and an alkyleneoxide adduct of bisphenol having 2 to 4 carbon atoms,
wherein the urethane resin (γ2) is formed from a polyol selected from the group consisting of polyethylene glycol, polypropylene glycol, polyoxyethylene oxypropylene glycol, and polyoxytetramethylene glycol, and
wherein at least one resin selected from the group consisting of the polyether resin (γ1) and the urethane resin (γ2) has a polyoxytetramethylene glycol in the repeating unit.

9. The polyarylene sulfide resin composition according to claim 1 , wherein a polyol constituting the urethane resin (γ2) is polyoxytetramethylene glycol.

10. The method for producing a polyarylene sulfide resin composition according to claim 4 , wherein a polyol constituting the urethane resin (γ2) is polyoxytetramethylene glycol.

11. The inorganic filler according to claim 7 , wherein a polyol constituting the urethane resin (γ2) is polyoxytetramethylene glycol.

12. The method for producing an inorganic filler according to claim 8 , wherein a polyol constituting the urethane resin (γ2) is polyoxytetramethylene glycol.

Assignees

• Dainippon Ink & Chemicals

Inventors

• Yamada Keisuke
• Nakase Hirokiyo
• Goto Takashi
• Kajikawa Masahiro

Classifications

• C08L2203/30

  used for thermoforming · CPC title

• C08J5/042

  with carbon fibres · CPC title

• C08K9/04 Primary

  Ingredients treated with organic substances {(treated with macromolecular compounds C08K9/08)} · CPC title

• C08L81/02 Primary

  Polythioethers; Polythioether-ethers · CPC title

• C08J5/043

  with glass fibres · CPC title