Abstract

An Al-steel assembly is provided. The assembly includes an aluminum-based element and a steel element on at least one surface of the aluminum-based element. The steel element has a metal coating made of a zinc-aluminum-magnesium alloy and includes from 2.3% to 3.3% by weight of magnesium and from 3.6% to 3.9% by weight of aluminum. A coated surface of the steel element is in contact with the aluminum-based element in an assembly zone and a protective coating coats the assembly around and adjacent the assembly zone. A body-in-white, further assembly and method are also provided.

First claim

What is claimed is:

1. An assembly comprising:
an aluminum-based element; and
a steel element on at least one surface of the aluminum-based element, the steel element having a metal coating made of a zinc-aluminum-magnesium alloy consisting of:
from 2.3% to 3.3% by weight of magnesium; and
from 3.6% to 3.9% by weight of aluminum; and
a remainder being zinc, inevitable impurities and possibly one or more additional elements selected from among Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni or Bi;

a coated surface of the steel element being in contact with the aluminum-based element in an assembly zone; and
a protective coating coating the assembly around and adjacent the assembly zone.

2. The assembly as recited in claim 1 , wherein the protective coating coats at least one part of a surface of the aluminum-based element.

3. The assembly as recited in claim 1 , wherein the protective coating includes a phosphating coating.

4. The assembly as recited in claim 1 , wherein the protective coating includes a cataphoresis coating.

5. The assembly as recited in claim 1 , wherein the protective coating includes a cataphoresis coating and a phosphating coating.

6. The assembly as recited in claim 1 , wherein the assembly includes an adhesive bonding the aluminum-based element to the steel element.

7. The assembly as recited in claim 1 , wherein an entirety of the assembly outside of the assembly zone has the protective coating.

8. A method for manufacturing the assembly as recited in claim 1 , comprising:
connecting the steel element to the aluminum-based element in the assembly zone; and, subsequently,
passing the connected steel element and the aluminum-based element in a bath containing the protective coating.

9. An assembly comprising:
an aluminum-based element having a first surface;
a steel element provided on at least one surface of the aluminum-based element, the steel element having a metal coating made of a zinc-aluminum-magnesium alloy consisting of:
from 2.3% to 3.3% by weight of magnesium, and
from 3.6% to 3.9% by weight of aluminum, and
a remainder of the metal coating being zinc, inevitable impurities and possibly one or more additional elements selected from among Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni or Bi; and

an adhesive bonding a coated surface of the steel element with the aluminum-based element in an active assembly zone, the aluminum-based element and the steel element being spaced from each other due to the adhesive.

10. The assembly as recited in claim 9 , comprising a paint covering the assembly outside the active assembly zone.

11. The assembly as recited in claim 9 , wherein the steel element is further crimped to the aluminum-based element.

12. The assembly as recited in claim 9 , wherein a spacing between the aluminum-based element and the steel element is less than 5 mm.

13. The assembly as recited in claim 9 , wherein a spacing between the aluminum-based element and the steel element is less than 1 mm.

14. The assembly as recited in claim 9 wherein a spacing between the aluminum-based element and the steel element is less than 200 microns.

15. The assembly as recited in claim 9 , wherein a thickness of the metal coating is greater than or equal to 3 microns.

Assignees

• Arcelormittal

Inventors

• Allely Christian
• Coffigny-Gregoire Astrid
• Dosdat Laurence
• Morel Stéphane

Classifications

• C23C2/06 Primary

  Zinc or cadmium or alloys based thereon · CPC title

• C22C18/04

  with aluminium as the next major constituent · CPC title

• Y10T428/12736

  Al-base component · CPC title

• B32B2605/00

  Vehicles · CPC title

• Y10T156/10

  Methods of surface bonding and/or assembly therefor · CPC title