Method for producing machine component

Patent metadata

Field	Value
Publication number	US-11344948-B2
Application number	US-201716078786-A
Country	US
Kind code	B2
Filing date	Mar 1, 2017
Priority date	Mar 3, 2016
Publication date	May 31, 2022
Grant date	May 31, 2022

Abstract

Provided is a method of manufacturing a machine part having a radial crushing strength of 120 MPa or more, including: a compression molding step of compressing raw material powder including, as a main component, metal powder that is capable of forming an oxide coating and has a pure iron powder content ratio of 95 mass % or more, to thereby obtain a green compact (10) having a predetermined shape; and a coating forming step of causing the metal powder to react with an oxidizing gas while heating the green compact (10) at a temperature lower than a sintering temperature of the metal powder in an oxidizing gas atmosphere, to thereby obtain a reinforced green compact (11) in which the oxide coating (5) is formed between particles of the metal powder.

First claim

The invention claimed is:

1. A method of manufacturing a machine part having a radial crushing strength of 120 MPa or more, the method comprising:
a compression molding step of compressing raw material powder comprising, as a main component, metal powder that is capable of forming an oxide coating and has a pure iron powder content ratio of 95% or more in mass ratio, to thereby obtain a green compact having a cylindrical shape, in which a cylindrical radial bearing surface for rotatably supporting a shaft in a radial direction is molded on an inner peripheral surface; and
a coating forming step of causing the metal powder to react with an oxidizing gas without reacting with water vapor while heating the green compact at a temperature lower than a sintering temperature of the metal powder in the oxidizing gas atmosphere, to thereby obtain a reinforced green compact in which the oxide coating is formed between particles of the metal powder,
wherein the cylindrical radial bearing surface of the reinforced green compact obtained through the compression molding step and the coating forming step has a cylindricity defined in JIS B 0021 of 3 μm or less.

2. The method of manufacturing a machine part according to claim 1 ,
wherein the raw material powder comprises a solid lubricant, and
wherein the method further comprises, between the compression molding step and the coating forming step, a degreasing step of removing the solid lubricant included in the green compact, the degreasing step being performed in a non-oxidizing atmosphere.

3. A method of manufacturing a machine part made of a porous metal, the method comprising:
a compression molding step of compressing raw material powder comprising: as a main component, metal powder that is capable of forming an oxide coating; and a solid lubricant, to thereby obtain a green compact having a cylindrical shape, in which a cylindrical radial bearing surface for rotatably supporting a shaft in a radial direction is molded on an inner peripheral surface;
a degreasing step of removing the solid lubricant included in the green compact; and
a coating forming step of causing the metal powder to react with an oxidizing gas without reacting with water vapor while heating the green compact after being subjected to degreasing treatment at a temperature lower than a sintering temperature of the metal powder in the oxidizing gas atmosphere, to thereby obtain a reinforced green compact in which the oxide coating is formed between particles of the metal powder,
wherein the solid lubricant is a fatty acid amide that is free of a metal component and formed of an element selected from the group consisting of C, H, O, N, P, S, and halogen group elements, has a decomposition temperature of less than 500° C., and has a decomposition rate in the degreasing step of 95% or more in mass fraction, to thereby obtain the reinforced green compact having the cylindrical radial bearing surface with a cylindricity defined in JIS B 0021 of 3 μm or less.

4. The method of manufacturing a machine part according to claim 3 , wherein the degreasing step is performed in a non-oxidizing atmosphere.

5. The method of manufacturing a machine part according to claim 1 , wherein the compression molding step comprises obtaining the green compact having a density of 5.8 g/cm 3 or more and 7.2 g/cm 3 or less.

6. The method of manufacturing a machine part according to claim 1 , wherein the coating forming step comprises setting a heating temperature of the green compact to 350° C. or more and less than 700° C.

7. The method of manufacturing a machine part according to claim 1 , wherein the coating forming step comprises setting treatment time to 60 minutes or less.

8. The method of manufacturing a machine part according to claim 1 , further comprising an oil-impregnating step of impregnating lubricating oil into inner pores of the reinforced green compact.

9. The method of manufacturing a machine part according to claim 1 , wherein the cylindrical radial bearing surface comprises a dynamic pressure generating portion formed through die molding.

10. The method of manufacturing a machine part according to claim 3 , wherein the compression molding step comprises obtaining the green compact having a density of 5.8 g/cm 3 or more and 7.2 g/cm 3 or less.

11. The method of manufacturing a machine part according to claim 3 , wherein the coating forming step comprises setting a heating temperature of the green compact to 350° C. or more and less than 700° C.

12. The method of manufacturing a machine part according to claim 3 , wherein the coating forming step comprises setting treatment time to 60 minutes or less.

13. The method of manufacturing a machine part according to claim 3 , further comprising an oil-impregnating step of impregnating lubricating oil into inner pores of the reinforced green compact.

14. The method of manufacturing a machine part according to claim 3 , wherein the cylindrical radial bearing surface comprises a dynamic pressure generating portion formed through die molding.

Assignees

• Ntn Toyo Bearing Co Ltd

Inventors

• Yashiro Naoki
• Oohira Kouya

Classifications

• B22F1/16

  Metallic particles coated with a non-metal (coated with lubricating or binding agents or with organic material B22F1/10) · CPC title

• B22F1/10

  Metallic powder containing lubricating or binding agents; Metallic powder containing organic material · CPC title

• F16C2220/20

  by sintering pulverised material, e.g. powder metallurgy · CPC title

• F16C17/10

  for both radial and axial load · CPC title

• B22F3/11

  Making porous workpieces or articles · CPC title