Dual catalyst system for producing LLDPE and MDPE copolymers with long chain branching for film applications

Patent metadata

Field	Value
Publication number	US-11339279-B2
Application number	US-202016837009-A
Country	US
Kind code	B2
Filing date	Apr 1, 2020
Priority date	Apr 1, 2020
Publication date	May 24, 2022
Grant date	May 24, 2022

Abstract

Disclosed herein are ethylene-based polymers generally characterized by a melt index of less than 15 g/10 min, a density from 0.91 to 0.945 g/cm3, a CY-a parameter at 190° C. from 0.2 to 0.6, an average number of long chain branches per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than 5, and a maximum ratio of ηE/3η at an extensional rate of 0.03 sec−1 in a range from 3 to 15. The ethylene polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in the lower molecular weight fraction, such that polymer melt strength and bubble stability are maintained for the fabrication of blown films and other articles of manufacture. These ethylene polymers can be produced using a dual catalyst system containing a single atom bridged metallocene compound with an indenyl group and a cyclopentadienyl group, and an unbridged hafnium metallocene compound with two cyclopentadienyl groups.

First claim

We claim:

1. An ethylene polymer having:
a melt index in a range from 0 to about 15 g/10 min;
a density in a range from about 0.91 to about 0.945 g/cm 3 ;
a CY-a parameter at 190° C. in a range from about 0.2 to about 0.6;
an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 500,000 to 2,000,000 g/mol of less than or equal to about 5; and
a maximum ratio of extensional viscosity to three times shear viscosity, η E /3η, at an extensional rate of 0.03 sec −1 in a range from about 3 to about 15.

2. An article of manufacture comprising the ethylene polymer of claim 1 .

3. The ethylene polymer of claim 1 , wherein:
the average number of LCBs per 1,000,000 total carbon atoms of the ethylene polymer in the molecular weight range of 500,000 to 2,000,000 g/mol is less than or equal to about 2; and
the maximum ratio of η E /3η at the extensional rate of 0.03 sec −1 is in a range from about 4 to about 12.

4. The ethylene polymer of claim 1 , wherein:
the melt index is in a range from about 0.4 to about 4 g/10 min;
the density is in a range from about 0.92 to about 0.94 g/cm 3 ; and
the CY-a parameter at 190° C. is in a range from about 0.3 to about 0.55.

5. The ethylene polymer of claim 4 , wherein the ethylene polymer comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof.

6. The ethylene polymer of claim 5 , wherein the ethylene polymer has a ratio of HLMI/MI in a range from about 20 to about 80.

7. An article of manufacture comprising the ethylene polymer of claim 5 .

8. The ethylene polymer of claim 1 , wherein the ethylene polymer has:
a ratio of Mw/Mn in a range from about 3 to about 6; and
a ratio of Mz/Mw in a range from about 2 to about 4.5.

9. The ethylene polymer of claim 1 , wherein the ethylene polymer has:
a Mn in a range from about 10,000 to about 50,000 g/mol;
a Mw in a range from about 50,000 to about 250,000 g/mol; and
a Mz in a range from about 200,000 to about 550,000 g/mol.

10. The ethylene polymer of claim 1 , wherein the ethylene polymer contains from about 1 to about 10 LCBs per 1,000,000 total carbon atoms.

11. The ethylene polymer of claim 1 , wherein the ethylene polymer has a number of short chain branches (SCBs) per 1000 total carbon atoms of the ethylene polymer at Mn that is greater than at Mz.

12. The ethylene polymer of claim 1 , wherein the ethylene polymer has a maximum ratio of η E /3η at an extensional rate of 0.1 sec −1 in a range from about 2 to about 10.

13. The ethylene polymer of claim 1 , wherein the ethylene polymer comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof.

14. The ethylene polymer of claim 13 , wherein:
the melt index is in a range from about 0.4 to about 4 g/10 min;
the density is in a range from about 0.91 to about 0.94 g/cm 3 ; and
the CY-a parameter at 190° C. is in a range from about 0.3 to about 0.6.

15. The ethylene polymer of claim 14 , wherein the ethylene polymer has:
an D3 parameter in a range from about 1.1 to about 1.8;
a relaxation time in a range from about 0.002 to about 0.025 sec.

16. The ethylene polymer of claim 14 , wherein the ethylene polymer has an ATREF profile characterized by:
a peak ATREF temperature in a range from about 88 to about 98° C.;
from about 0.5 to about 6 wt % of the ethylene polymer eluting below a temperature of 40° C.;
from about 12 to about 26 wt % of the ethylene polymer eluting between 40 and 76° C.;
from about 52 to about 82 wt % of the ethylene polymer eluting above a temperature of 86° C.; and
a remainder of the ethylene polymer eluting between 76 and 86° C.

17. The ethylene polymer of claim 16 , wherein:
the peak ATREF temperature is in a range from about 90 to about 96° C.;
from about 1 to about 5 wt % of the ethylene polymer is eluted below a temperature of 40° C.;
from about 13 to about 24 wt % of the ethylene polymer is eluted between 40 and 76° C.;
from about 58 to about 75 wt % of the ethylene polymer is eluted above a temperature of 86° C.; and
the remainder of the ethylene polymer is eluted between 76 and 86° C.

18. A film comprising the ethylene polymer of claim 17 .

19. The ethylene polymer of claim 14 , wherein the ethylene polymer contains less than 0.1 ppm, independently, of chromium and titanium.

20. A film comprising the ethylene polymer of claim 14 , wherein the film has:
a MD Elmendorf tear strength in a range from about 40 to about 250 g/mil;
a ratio of MD Elmendorf tear strength to TD Elmendorf tear strength (MD:TD) in a range from about 0.15:1 to about 0.55:1; and
a haze in a range from about 3 to about 10%.

21. The film of claim 20 , wherein the film has an average thickness in a range from about 0.5 to about 8 mils.

22. The ethylene polymer of claim 13 , wherein:
the melt index is in a range from about 0.1 to about 10 g/10 min;
the density is in a range from about 0.91 to about 0.94 g/cm 3 ;
the CY-a parameter at 190° C. is in a range from about 0.3 to about 0.55;
the average number of LCBs per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 500,000 to 2,000,000 g/mol is less than or equal to about 3; and
the maximum ratio of η E /3η at and extensional rate of 0.03 sec −1 is in a range from about 4 to about 12.

23. The ethylene polymer of claim 13 , wherein:
the ethylene polymer has a ratio of Mw/Mn in a range from about 3.5 to about 8; and
the ethylene polymer contains from about 1 to about 10 LCBs per 1,000,000 total carbon atoms.

24. The ethylene polymer of claim 23 , wherein:
the ethylene polymer has a Mw in a range from about 70,000 to about 185,000 g/mol;
the ethylene polymer has a maximum ratio of η E /3η at an extensional rate of 0.1 sec −1 in a range from about 2 to about 10; and
the ethylene polymer contains less than 0.1 ppm, independently, of chromium and titanium.

25. An article of manufacture comprising the ethylene polymer of claim 23 .

26. The ethylene polymer of claim 13 , wherein:
the melt index is in a range from about 0.4 to about 4 g/10 min;
the density is in a range from about 0.92 to about 0.94 g/cm 3 ;
the CY-a parameter at 190° C. is in a range from about 0.3 to about 0.55;
the average number of LCBs per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 500,000 to 2,000,000 g/mol is less than or equal to about 2; and
the maximum ratio of η E /3η at an extensional rate of 0.03 sec −1 is in a range from about 5 to about 9.

27. The ethylene polymer of claim 26 , wherein:
the ethylene polymer has a ratio of Mw/Mn in a range from about 3.5 to about 6;
the ethylene polymer has a relaxation time in a range from about 0.002 to about 0.025 sec;
the ethylene polymer has a maximum ratio of η E /3η at an extensional rate of 0.1 sec −1 in a range from about 3 to about 7; and
the ethylene polymer contains from about 1 to about 8 LCBs per 1,000,000 total carbon atoms.

28. An olefin polymerization process, the process comprising contacting a catalyst composition with ethylene and an olefin comonomer in a polymerization reactor system under polymerization conditions to produce an ethylene polymer, wherein:
the catalyst composition

Assignees

• Chevron Phillips Chemical Co Lp

Inventors

• Ding Errun
• Tso Chung Ching
• Mcdaniel Max P
• Sukhadia Ashish M
• Yu Youlu
• Muninger Randall S
• Osborn Aaron M
• Wittner Christopher E

Classifications

• C08F2410/07

  Catalyst support treated by an anion, e.g. Cl-, F-, SO42- · CPC title

• C08F4/65908

  in combination with an ionising compound other than alumoxane, e.g. (C6F5)4B-X+ · CPC title

• C08F4/65912

  in combination with an organoaluminium compound · CPC title

• C08L23/0815 Primary

  with aliphatic 1-olefins containing one carbon-to-carbon double bond · CPC title

• C08F210/16 Primary

  Copolymers of ethene with alpha-alkenes, e.g. EP rubbers · CPC title