Green fabrication of polytetrafluoroethylene and expanded polytetrafluoroethylene and uses thereof

Patent metadata

Field	Value
Publication number	US-11339267-B2
Application number	US-202016744505-A
Country	US
Kind code	B2
Filing date	Jan 16, 2020
Priority date	Jan 22, 2019
Publication date	May 24, 2022
Grant date	May 24, 2022

Abstract

Green, fast and easy evaporating organic solvent for use as a lubricant in the processing of polytetrafluoroethylene (PTFE) and expanded polytetrafluoroethylene (ePTFE) products and processes of using the solvents to fabricate the products are disclosed herein. The products can be used in the field of bio- and medical applications, such as for use in vascular grafts, cardiovascular and soft tissue patches, facial implants, surgical sutures, and endovascular prosthesis, and for any products known in the aerospace, electronics, fabrics, filtration, industrial and sealant arts.

First claim

What is claimed is:

1. A process for preparing an extruded product, the process comprising:
blending a polytetrafluoroethylene (PTFE) powder with a lower alkyl (C 1 -C 10 ) alcohol to form a blend, wherein the lower alkyl (C 1 -C 10 ) alcohol is present in the blend in an amount of from about 10% by weight to about 30% by weight;
preforming the blend;
extruding the preformed blend to form a product; and evaporating the lower alkyl (C 1 -C 10 ) alcohol from the extruded product.

2. The process as set forth in claim 1 , wherein the lower alkyl (C 1 -C 10 ) alcohol is a biocompatible lower alkyl (C 1 -C 10 ) alcohol selected from the group consisting of methanol, ethanol, isopropanol, and combinations thereof.

3. The process as set forth in claim 2 , wherein the biocompatible lower alkyl (C 1 -C 10 ) alcohol is ethanol.

4. The process as set forth in claim 1 , wherein the lower alkyl (C 1 -C 10 ) alcohol is further mixed with water before blended with the PTFE powder and the alcohol/water mixture has a weight ratio of alcohol:water of from about 10:90 to about 100:0.

5. The process as set forth in claim 1 , wherein blending comprising rolling the PTFE powder and lower alkyl (C 1 -C 10 o) alcohol for a period of from about 30 minutes to about 120 minutes.

6. The process as set forth in claim 5 further comprising aging the blend for a period of from about 30 minutes to about 48 hours after rolling.

7. The process as set forth in claim 1 comprising preforming the blend at a pressure of from about 1 MPa to about 30 MPa.

8. The process as set forth in claim 1 , wherein evaporating of the lower alkyl (C 1 -C 10 ) alcohol comprises heating the extruded product to a temperature of from 60° C. to about 200° C. for a period of from about 0.5 minutes to about 120 minutes.

9. The process as set forth in claim 1 further comprising sintering the heated extruded product at a temperature of from about 360° C. to about 400° C. for a period of from about 10 seconds to about 10 minutes.

10. The process as set forth in claim 1 further comprising expanding the extruded product.

11. The process as set forth in claim 9 , wherein the expanding is conducted at a temperature of from about 25° C. to about 340° C.

12. The process as set forth in claim 9 , wherein the extruded product is expanded at a rate of from about 1 mm/min to about 1000 mm/min.

13. The process as set forth in claim 9 , wherein the extruded product is expanded at an expansion ratio of from about 100% to about 800%.

14. The process as set forth in claim 4 further comprising dissolving a target material in the lower alkyl (C 1 -C 10 ) alcohol.

15. A medical implant comprising the extruded product made by the process of claim 1 .

16. The medical implant as set forth in claim 15 selected from the group consisting of vascular grafts, cardiovascular and soft tissue patches, facial implants, surgical sutures, and endovascular prostheses.

17. A process for preparing an extruded product, the process comprising:
mixing a lower alkyl (C 1 -C 10 ) alcohol with water wherein the alcohol/water mixture has a weight ratio of alcohol:water of from about 10:90 to about 100:0;
blending a polytetrafluoroethylene (PTFE) powder with the alcohol/water mixture to form a blend;
preforming the blend;
extruding the preformed blend to form a product; and evaporating the lower alkyl (C 1 -C 10 ) alcohol from the extruded product.

Assignees

• Wisconsin Alumni Res Found

Inventors

• Turng Lih-Sheng
• Xu Yiyang
• Lin Yu-Jyun
• Wang dong-fang

Classifications

• A61L31/16

  Biologically active materials, e.g. therapeutic substances {(A61L31/047 takes precedence)} · CPC title

• A61L27/56

  Porous materials, {e.g. foams or sponges} · CPC title

• A61L27/16

  obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• A61L27/507

  for artificial blood vessels (apparatus for applying cells on a blood vessel prosthesis A61F2/062) · CPC title

• C08J2203/10

  Water or water-releasing compounds · CPC title