Negative electrode active material for electrochemical device, negative electrode including the negative electrode active material and electrochemical device including the same

Patent metadata

Field	Value
Publication number	US-11335909-B2
Application number	US-201816604963-A
Country	US
Kind code	B2
Filing date	Oct 30, 2018
Priority date	Oct 30, 2017
Publication date	May 17, 2022
Grant date	May 17, 2022

Abstract

A negative electrode active material for an electrochemical device which has improved quick charging characteristics. The negative electrode active material includes two types of graphite particles having a different particle diameter and shows a bimodal distribution, wherein the ratio of the average particle diameter (D50) of the first graphite particles to the average particle diameter (D50) of the second graphite particles is larger than 1.7.

First claim

What is claimed is:

1. A negative electrode active material for an electrochemical device, comprising:
first graphite particles, wherein the first graphite particles have an average particle diameter (D 50 ) of 15 μm to 25 μm; and
second graphite particles, wherein the second graphite particles have an average particle diameter (D 50 ) of 4 μm to 11 μm,
wherein the first graphite particles and the second graphite particles have a bimodal distribution, and a ratio of the average particle diameter (D 50 ) of the first graphite particles to the average particle diameter (D 50 ) of the second graphite particles is larger than 1.7,
wherein R S and R B are ratios (R R ) of D band peak intensity (1358 cm −1 ) to G band peak intensity (1580 cm −1 ) showing a degree of crystallization in Raman spectroscopy, wherein a ratio R S of the second graphite particles to R B of the first graphite particles, R S /R B , is 0.03-0.82.

2. The negative electrode active material for the electrochemical device according to claim 1 ,
wherein the first and the second graphite particles have an orientation index of less than 35,
wherein the orientation index is defined as an area ratio of a (004) surface to a (110) surface, wherein the (110) surface and (004) surface of the particles are measured with X-ray diffractometry integration of peak intensities from the X-ray diffractometry.

3. The negative electrode active material for the electrochemical device according to claim 1 , wherein the ratio of (R R ) is 0.19-0.60.

4. The negative electrode active material for the electrochemical device according to claim 1 , wherein the ratio of R S /R B is 0.03-0.82, and R S is 0.03-0.200.

5. The negative electrode active material for the electrochemical device according to claim 1 , wherein the ratio of R S /R B is 0.03-0.82, and R B is 0.146-1.000.

6. The negative electrode active material for the electrochemical device according to claim 1 , wherein the first graphite particles are present in an amount of 50 wt % to 99 wt % based on 100 wt % of the negative electrode active material.

7. The negative electrode active material for the electrochemical device according to claim 1 , wherein the first graphite particles have a specific surface area of 0.01 m 2 /g to 1.9 m 2 /g.

8. The negative electrode active material for the electrochemical device according to claim 1 , wherein the second graphite particles have a specific surface area of 0.05 m 2 /g to 2.6 m 2 /g.

9. The negative electrode active material for the electrochemical device according to claim 1 , wherein each of the first graphite particle and the second graphite particle is independently at least one selected from the group consisting of natural graphite, artificial graphite, graphitized carbon fibers, graphitized mesocarbon microbeads and amorphous carbon.

10. A negative electrode for an electrochemical device comprising the negative electrode active material as defined in claim 1 .

11. The negative electrode for the electrochemical device according to claim 10 , which has an orientation index, defined by an area ratio ((004 surface)/(110 surface)) of the first and the second graphite particles contained in the negative electrode, less than 35.

12. An electrochemical device comprising:
a positive electrode;
a negative electrode; and
a separator interposed between the positive electrode and the negative electrode,
wherein the negative electrode comprises the negative electrode active material as defined in claim 1 .

Assignees

• Lg Chemical Ltd
• Lg Energy Solution Ltd

Inventors

• Piao Lilin
• Kim Eun-Kyung
• Chung Ju-Ho

Classifications

• H01G11/42

  Powders or particles, e.g. composition thereof · CPC title

• H01G11/24

  characterised by structural features of the materials making up or comprised in the electrodes, e.g. form, surface area or porosity; characterised by the structural features of powders or particles used therefor · CPC title

• H01M2004/027

  Negative electrodes · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M4/133 Primary

  Electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx · CPC title