Process for manufacturing a sorbent for a flue gas treatment process, sorbent and use of said sorbent in such flue gas treatment process

Patent metadata

Field	Value
Publication number	US-11331646-B2
Application number	US-201816603033-A
Country	US
Kind code	B2
Filing date	Apr 6, 2018
Priority date	Apr 7, 2017
Publication date	May 17, 2022
Grant date	May 17, 2022

Abstract

The present invention is related to a process for manufacturing a sorbent suitable for a use in a circulating dry scrubber device comprising the steps of: providing quicklime and water in an hydrator; slaking said quicklime via a non-wet route in the hydrator; collecting a lime based sorbent at an exit of the hydrator. The process is characterized in that it comprises a further step of adding at least a first additive comprising: a compound comprising silicon, and/or, a compound comprising aluminum, and/or a compound comprising silicon and aluminum before or during said slaking step, at a molar ratio between silicon or aluminum or a combination thereof and the calcium provided to said hydrator equal to or below 0.2 and equal to or above 0.02. In some other aspects, the present invention is related to a sorbent, a premix, and a flue gas treatment process.

First claim

The invention claimed is:

1. Process for manufacturing a circulating dry scrubber lime based sorbent composition comprising the steps of:
providing quicklime and water in an hydrator;
slaking said quicklime in a slaking step via a non-wet route in the hydrator;
collecting a lime based sorbent at an exit of the hydrator, the lime based sorbent being a composition wherein said, sorbent composition comprises 1 to 12 weight % of bound water with respect to the total weight of said sorbent under a dry form and;
wherein said process comprises a further step of adding at least a first additive comprising
a silicon compound, said silicon compound being selected from the group consisting of silicates, silicates of sodium, metasilicates, metasilicates of sodium, kieselguhr, diatomite, precipitated silica, silica fume, rice husk ash, silicic acid, amorphous silica, and combinations thereof, and/or;
a compound comprising aluminum selected from the group consisting of aluminum trihydroxide, boehmite, and combinations thereof, and/or;
a compound comprising silicon and aluminum selected from the group consisting of vermiculite, paper ash, and combinations thereof;
before or during said slaking step, at a molar ratio between silicon or aluminum or a combination thereof and the calcium provided to said hydrator equal to or below 0.2 and equal to or above 0.02.

2. Process according to claim 1 , further comprising a step of drying said lime based sorbent or classifying said lime based sorbent or grinding said lime based sorbent or milling said lime based sorbent or a combination thereof.

3. Process according to claim 1 , wherein said first additive is provided at least partially in a solution or in a suspension and added to said water.

4. Process according to claim 1 , wherein said first additive is provided at least partially under solid form and added to said quicklime.

5. Process according to, claim 1 wherein said quicklime and said first additive are provided in a premix containing at least 50 weight % of quicklime and at least 0.7 weight % of silicon or aluminum or a combination thereof and at most 10 weight % of silicon or aluminum or a combination thereof with respect to said total weight of said premix under a dry form.

6. Process according to claim 1 , wherein said first additive further comprises sodium.

7. Process according to claim 1 , further comprising an additional step of adding a second additive comprising a compound comprising sodium.

8. Process according claim 7 , wherein the said second additive comprising a compound comprising sodium is selected from the group consisting of sodium hydroxide, sodium carbonate, sodium hydrogenocarbonate, sodium nitrate, sodium phosphate, sodium persulfate or sodium acetate.

Assignees

• Lhoist Rech Et Developpement Sa

Inventors

• Lorgouilloux Marion
• Maazoun Mehdi
• Nyssen Olivier
• Johan Heiszwolf

Classifications

• B01D53/80

  Semi-solid phase processes, i.e. by using slurries · CPC title

• B01J20/041 Primary

  Oxides or hydroxides · CPC title

• B01D2253/112

  Metals or metal compounds not provided for in B01D2253/104 or B01D2253/106 · CPC title

• B01D53/83

  with moving reactants · CPC title

• B01D53/508

  by treating the gases with solids · CPC title