Composition for producing a polymer, a method for producing the polymer, said polymer, use of the polymer, and an electrically dimmable glazing enclosing the polymer

Patent metadata

Field	Value
Publication number	US-11326012-B2
Application number	US-201816489813-A
Country	US
Kind code	B2
Filing date	Mar 2, 2018
Priority date	Mar 3, 2017
Publication date	May 10, 2022
Grant date	May 10, 2022

Abstract

The present invention relates to a composition for producing a polymer, comprising: a) from 20 to 60% by weight, based on the entire composition, of at least one monomer; and b) from 30 to 60% by weight, based on the entire composition, of at least one branched pre-polymer, wherein the composition is liquid at room temperature and under normal pressure; use of the composition, a method for producing a polymer using the composition, as well as an electrically dimmable glazing that encloses the polymer.

First claim

The invention claimed is:

1. A composition for producing a polymer, comprising:
20 to 60% by weight, based on the entire composition, of at least one monomer; and
30 to 60% by weight, based on the entire composition, of at least one branched pre-polymer,

wherein the composition is liquid at 20° C. and 1 bar;
the at least one monomer is selected from the group consisting of methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, n-butyl acrylate, n-butyl methacrylate, isobutyl methacrylate, methyl acrylate, ethyl acrylate, vinyl chloride, acrylonitrile, vinyl acetate, styrene, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, N-Isopropyl acrylamide, N, N-dimethylaminoethyl methacrylate, N, N-dimethylaminoethyl acrylate, 2-vinylpyridine, 4-vinylpyridine, and any combination thereof; and
the branched pre-polymer is a reaction product of a) at least one monomer having one polymerizable group, b) at least one monomer having at least two polymerizable groups, and c) at least one chain transfer agent.

2. The composition according to claim 1 , wherein the at least one chain transfer agent includes an aliphatic thiol, an aromatic thiol, or a combination thereof.

3. The composition according to claim 1 , wherein the branched pre-polymer has a number average of the molar mass M n of 1,000 to 10,000 g/mol.

4. The composition according to claim 1 , wherein the branched pre-polymer has a weight average of the molar mass M w of 2,000 to 40,000 g/mol.

5. The composition according to claim 1 , wherein the pre-polymer has a dispersity of 2 to 10.

6. The composition according to claim 5 , wherein the branched pre-polymer has a dispersity of 2.5 to 8.

7. The composition of claim 1 , wherein a viscosity of the composition is not greater than 41 mPas.

8. The composition according to claim 1 , wherein the branched pre-polymer includes a branched poly(alkyl)acrylate, a branched polyacrylate, a branched polystyrene, or a combination thereof.

9. The composition according to claim 8 , wherein the branched pre-polymer includes branched poly-n-butyl acrylate, branched poly-2-ethylhexyl acrylate, branched poly(n-butyl acrylate-co-2-ethylhexyl acrylate), or any combination thereof.

10. The composition according to claim 1 , wherein the monomer of the composition includes n-butyl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, styrene, or any combination thereof.

11. The composition according to claim 1 , wherein the composition comprises a further monomer having at least two polymerizable groups in an amount of 0.1 to 2% by weight based on the total weight of the composition.

12. The composition of claim 1 , wherein the composition is adapted for producing a dental composite, a glass ionomer cement, an acrylate adhesive, an acrylic glass sheet, an acrylic material in electrical engineering, or a glass-polymer-glass composite pane.

13. An electrically dimmable glazing comprising the polymer of claim 1 .

14. A method of producing a polymer, comprising:
forming a branched pre-polymer, wherein forming the branched pre-polymer comprises reacting a) at least one monomer having one polymerizable group, b) at least one monomer having at least two polymerizable groups, and c) at least one chain transfer agent;
preparing a composition comprising 30-60 wt % of the branched pre-polymer and 20-60 wt % of at least one monomer, the monomer being selected from the group consisting of methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, n-butyl acrylate, n-butyl methacrylate, isobutyl methacrylate, methyl acrylate, ethyl acrylate, vinyl chloride, acrylonitrile, vinyl acetate, styrene, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, N-Isopropyl acryl; and
reacting the composition to form the polymer.

15. The method of claim 14 , wherein a shrinkage of the composition after reacting the composition and forming the polymer is not greater than 7%.

16. The method of claim 14 , wherein a viscosity of the composition is not greater than 41 mPas.

17. The method of claim 14 , wherein a ratio for forming the branched pre-polymer of a) the at least one monomer having one polymerizable group to b) the at least one monomer having at least two polymerizable groups to c) the at least one chain transfer agent is 1-100/1/0.1-10.

18. The method according to claim 14 , wherein the branched pre-polymer includes a branched poly(alkyl)acrylate, a branched polyacrylate, a branched polystyrene, or a combination thereof.

Assignees

• Univ Jena Friedrich Schiller

Inventors

• Schacher Felix Helmut
• Eckardt Oliver
• Mueller Axel H E
• Breuermann Sven
• Joedicke Dirk

Classifications

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• B60J3/04

  adjustable in transparency · CPC title

• C08F220/1808

  C8-(meth)acrylate, e.g. isooctyl (meth)acrylate or 2-ethylhexyl (meth)acrylate · CPC title

• C08F2800/20

  as weight or mass percentages · CPC title

• H01B1/122

  Ionic conductors · CPC title