Abstract

A process for manufacturing a fibrous preform filled with particles, includes forming the filled preform by compacting a stack of a plurality of fibrous strata impregnated by a suspension of ceramic oxide particles in a liquid medium, wherein the liquid medium includes at least one compound having a saturated vapor pressure of less than 2.3 kPa at 20° C., this compound being present in a weight content of greater than or equal to 30% relative to the total weight of the suspension.

First claim

The invention claimed is:

1. A method for manufacturing a fiber preform filled with particles, the method comprising:
forming the filled preform by compacting a stack of a plurality of fiber plies impregnated with a suspension of particles of ceramic oxide in a liquid medium,
wherein the liquid medium includes at least one compound having a saturation vapor pressure less than 2.3 kPa at 20° C., the compound being present at a mass content greater than or equal to 30% relative to the total weight of the suspension, the particles being present at a mass content, relative to the total weight of the suspension, of between 40% and 70%.

2. The method according to claim 1 , wherein the compound has a saturation vapor pressure less than or equal to 0.6 kPa at 20° C.

3. The method according to claim 1 , wherein the compound is chosen among: glycerol, lactic esters, dimethyl-2-methylglutarate, and mixtures thereof.

4. The method according to claim 3 wherein the compound is glycerol.

5. The method according to claim 1 , wherein the compaction is performed by vacuum drawing.

6. The method according to claim 1 , wherein the particles are present at a mass content, relative to the total weight of the suspension, of between 40% and 60%.

7. The method according to claim 1 , wherein the liquid medium comprises:
the compound at a mass content, relative to the total weight of the suspension, of between 30% and 50%, and
optionally a solvent, different from the compound, at a mass content, relative to the total weight of the suspension, of between 5% and 30%, and
optionally an organic binder at a mass content, relative to the total weight of the suspension, of between 1% and 15%, and optionally
a dispersant at a mass content, relative to the total weight of the suspension, of between 0.1% and 1.5%.

8. The method according to claim 1 , wherein the fiber plies are formed of fibers of ceramic oxide.

9. The method according to claim 1 , wherein the method comprises, prior to the compaction step, a step of forming the stack by depositing the plies in the dry state, the deposited ply being impregnated with the suspension before the deposition of the next ply.

10. The method according to claim 1 , wherein the method comprises, prior to the compaction step, a step of forming the stack by superposition of plies pre-impregnated with the suspension.

11. A method for manufacturing a part made of composite material, the method comprising:
forming a filled preform by implementing a method according to claim 1 , and
forming a matrix in the porosity of the preform filled by sintering the particles.

12. The method according to claim 7 , wherein the dispersant is at a mass content, relative to the total weight of the suspension, of between 0.5% and 1%.

Assignees

• Safran Ceram

Inventors

• Diss Pascal
• Deliane Florent
• Duee Natacha

Classifications

• C04B2235/604

  Pressing at temperatures other than sintering temperatures · CPC title

• C04B35/117

  Composites · CPC title

• B32B18/00 Primary

  Layered products essentially comprising ceramics, e.g. refractory products · CPC title

• C04B35/6264

  Mixing media, e.g. organic solvents · CPC title

• C04B2237/341

  Silica or silicates · CPC title