Abstract

A microwave induced solvothermal method to prepare lithium thiophosphate composites including α-Li 3 PS 4 and crystalline Li 7 P 3 S 11 is provided. The method is scaleable to commercial size production.

First claim

The invention claimed is:

1. A method to prepare a target lithium thiophosphate composite, comprising:
preparing an anhydrous mixture comprising:
Li 2 S;
P 2 S 5 ;
optionally a component B; and
a nonaqueous polar solvent;

mixing the anhydrous mixture to at least partially dissolve the Li 2 S, P 2 S 5 and component B if present;
applying microwave energy to the anhydrous mixture to raise the reaction temperature to an optimum value for synthesis of the target lithium thiophosphate composite to obtain the target lithium thiophosphate composite; and
removing the polar solvent from the obtained lithium thiophosphate composite;
wherein a molar ratio of Li 2 S to P 2 S 5 and to B, if present, is determined by the composition of the target lithium thiophosphate composite, and
wherein the optional component B, when present is at least one compound selected from the group consisting of Li 3 N, Li 2 O, LiN 3 , GeS 2 or LiX wherein X is I, Cl or Br.

2. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein the nonaqueous polar solvent is selected from the group consisting of ethers, nitriles, alcohols, carbonates and esters, with the proviso that the polar solvent is volatile under reduced pressure at a temperature less than a phase transition temperature of the target lithium thiophosphate composite.

3. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein the microwave energy applied the anhydrous mixture to induce reaction raises the temperature to a value of from 50° C. to 200° C.

4. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein a time of the microwave induced reaction may be from 30 minutes to 5 hours.

5. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein the target lithium thiophosphate composite is amorphous Li 3 PS 4 , a ratio of Li 2 S/P 2 S 5 is approximately 3/1, the solvent is tetrahydrofuran and no B component is present.

6. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein the target lithium thiophosphate composite is Li 7 P 3 S 11 , a ratio of Li 2 S/P 2 S 5 is approximately 70/30, the solvent is tetrahydrofuran or acetonitrile and no B component is present.

7. The method to prepare a target lithium thiophosphate composite according to claim 1 wherein the target lithium thiophosphate composite is xLi 2 S·yP 2 S 5 ·(100-x-y)B, a ratio of Li 2 S/P 2 S 5 is approximately x/y, and a B component is present in an amount of 100-x-y.

Assignees

• Toyota Eng & Mfg North America

Inventors

• Muldoon John
• Bonnick Patrick J
• Suto Koji
• NAGAI Erika
• Niitani Keita

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M10/0585

  of accumulators having only flat construction elements, i.e. flat positive electrodes, flat negative electrodes and flat separators · CPC title

• H01M10/0562

  Solid materials · CPC title

• H01M4/5825 Primary

  Oxygenated metallic salts or polyanionic structures, e.g. borates, phosphates, silicates, olivines · CPC title