Slurries for composite materials

Patent metadata

Field	Value
Publication number	US-11319253-B2
Application number	US-201314776993-A
Country	US
Kind code	B2
Filing date	Jun 12, 2013
Priority date	Mar 15, 2013
Publication date	May 3, 2022
Grant date	May 3, 2022

Abstract

Slurry and tape compositions include particles of a precursor that converts to a ceramic material when heated to a firing temperature, at least one binder that is capable of adhering the particles of the ceramic precursor together to form a pliable prepreg tape, at least one liquid plasticizer, and at least one solvent in which the binder is dissolved. The solvent may be sufficiently volatile to evaporate from the slurry composition during formation of the tape, yet the tape may also be pliable as a result of the slurry composition containing a sufficient amount of the liquid plasticizer.

First claim

What is claimed is:

1. A process of using a slurry composition to produce a pliable nonflammable tape, the process comprising:
forming the slurry composition to contain 30 to 60 weight percent of a powder comprising particles of at least one precursor; 5 to 10 weight percent of at least one binder; 5 to 10 weight percent of at least one liquid plasticizer; and a solvent in which the binder is dissolved, wherein the solvent is about 45 weight percent or more of the slurry composition, and wherein the at least one precursor comprising SiC, carbon, and/or one or more other carbon-containing particulate materials;
impregnating a fiber reinforcement material with the slurry composition to produce a slurry-impregnated reinforcement material; and
evaporating at least a portion of the solvent from the slurry-impregnated reinforcement material to form the tape in which the particles of the precursor are adhered together by a matrix material;
wherein a sufficient amount of the solvent evaporates to result in the tape being nonflammable and containing less than about 10 weight percent of the solvent, yet the tape is also pliable as a result of containing a sufficient amount of the liquid plasticizer.

2. The process according to claim 1 , wherein the binder is selected from the group consisting of polyethylenes, polycarbonates, polyvinyl acetates, polyvinyl alcohols, polyvinyl butyral (PVB), and acrylics.

3. The process according to claim 1 , wherein the solvent is selected from the group consisting of ethanol, isopropanol, butanol, acetates, toluene, acetone, ketones, glycols and xylene.

4. The process according to claim 1 , wherein the solvent constitutes less than about 7 weight percent of the tape.

5. The process according to claim 1 , wherein the liquid plasticizer is selected from the group consisting of dibutyl phthalate, butyl benzyl phthalate, triethyleneglycol bis(2-ethyl hexanoate), adipates, glycols, linseed oil, and castor oil.

6. The process according to claim 1 , wherein the liquid plasticizer constitutes about 4 to about 8 weight percent of the tape.

7. The process according to claim 1 , wherein the matrix material contains:
about 60 to about 70 weight percent of the powder;
about 10 to about 18 weight percent of the binder;
about 10 to about 14 weight percent of the liquid plasticizer; and
less than about 7 weight percent of the solvent.

8. The process according to claim 1 , further comprising:
using the tape to form a preform;
heating the preform to decompose the binder and the liquid plasticizer; and then
further heating the preform to convert the precursor to a ceramic material, the ceramic material forming a ceramic matrix for the fiber reinforcement material.

9. The process according to claim 8 , wherein the process produces a ceramic matrix composite component.

Assignees

• Gen Electric

Inventors

• Matsumoto Roger Lee Ken

Classifications

• C04B35/573

  obtained by reaction sintering {or recrystallisation} · CPC title

• C04B35/6264

  Mixing media, e.g. organic solvents · CPC title

• C04B35/63408

  Polyalkenes · CPC title

• C04B35/63424

  Polyacrylates; Polymethacrylates · CPC title

• C04B2235/6025

  Tape casting, e.g. with a doctor blade · CPC title