Large V-belt

Patent metadata

Field	Value
Publication number	US-11313435-B2
Application number	US-202117543497-A
Country	US
Kind code	B2
Filing date	Dec 6, 2021
Priority date	Jun 7, 2019
Publication date	Apr 26, 2022
Grant date	Apr 26, 2022

Abstract

A large V-belt includes an endless rubber belt body including an adhesive rubber layer and a cord embedded in the adhesive rubber layer of the belt body. The large V-belt has a belt thickness of 15 mm or more and the belt width of 10 mm or more at the center, in a belt thickness direction, of a cord embedded position. The belt body further includes reinforced rubber layers made of a rubber composition having a type A durometer hardness of 92 or more, the reinforced rubber layers being stacked on a belt inner side and/or a belt outer side of the adhesive rubber layer in the belt thickness direction.

First claim

What is claimed is:

1. A large V-belt comprising:
an endless belt body made of rubber and including an adhesive rubber layer stacked in a belt thickness direction; and
a cord embedded in the adhesive rubber layer of the belt body and extending along a circumferential direction of the belt body while forming a helical pattern having a pitch in a belt width direction,
the large V-belt having a belt thickness of 15 mm or more and a belt width of 10 mm or more at a center, in the belt thickness direction, of a cord embedded position,
the belt body further including a reinforced rubber layer made of a rubber composition having a type A durometer hardness of 92 or more, the reinforced rubber layer being stacked on a belt inner side and/or a belt outer side of the adhesive rubber layer in the belt thickness direction,
the rubber composition containing a rubber component, cellulose-based fine fibers, carbon black, and para-aramid short fibers,
a content of the para-aramid short fibers in the rubber composition being 25 parts by mass or more and 40 parts by mass or less relative to 100 parts by mass of the rubber component,
a sum of a content of the carbon black and the content of the para-aramid short fibers in the rubber composition being 50 parts by mass or more and 100 parts by mass or less relative to 100 parts by mass of the rubber component,
the rubber composition being arranged such that a grain direction thereof corresponds to the belt width direction and a cross-grain direction thereof corresponds to a belt length direction,
a storage normal modulus E′ of the rubber composition at 25° C. in the cross-grain direction being 80 MPa or more and 200 MPa or less, and
a ratio of a storage normal modulus E′ of the rubber composition at 25° C. in the grain direction to the storage normal modulus E′ of the rubber composition at 25° C. in the cross-grain direction being 10 or more and 20 or less.

2. The large V-belt of claim 1 , wherein
the rubber component of the rubber composition includes chloroprene rubber.

3. The large V-belt of claim 1 , wherein
the para-aramid short fibers include copolyparaphenylene-3,4′-oxydiphenylene terephthalamide short fibers.

4. The large V-belt of claim 1 , wherein
the cellulose-based fine fibers include cellulose-based fine fibers formed by a mechanically-defibrating means.

5. The large V-belt of claim 1 , wherein
a content of the cellulose-based fine fibers in the rubber composition is 1 part by mass or more and 20 parts by mass or less relative to 100 parts by mass of the rubber component.

6. The large V-belt of claim 1 , wherein
the content of the para-aramid short fibers in the rubber composition is greater than the content of the cellulose-based fine fibers.

7. The large V-belt of claim 6 , wherein
a ratio of the content of the para-aramid short fibers to the content of the cellulose-based fine fibers in the rubber composition is 5 or more and 20 or less.

8. The large V-belt of claim 1 , wherein
the carbon black includes FEF.

9. The large V-belt of claim 1 , wherein
the content of the carbon black in the rubber composition is 20 parts by mass or more and 80 parts by mass or less relative to 100 parts by mass of the rubber component.

10. The large V-belt of claim 1 , wherein
the content of the para-aramid short fibers in the rubber composition is less than the content of the carbon black.

11. The large V-belt of claim 10 , wherein
a ratio of the content of the para-aramid short fibers to the content of the carbon black in the rubber composition is 0.45 or more and 0.90 or less.

12. The large V-belt of claim 1 , wherein
the content of the carbon black in the rubber composition is greater than the content of the cellulose-based fine fibers.

13. The large V-belt of claim 12 , wherein
a ratio of the content of the carbon black to the content of the cellulose-based fine fibers in the rubber composition is 5 or more and 20 or less.

14. The large V-belt of claim 1 , wherein
the storage normal modulus E′ of the rubber composition at 25° C. in the grain direction is 700 MPa or more and 2000 MPa or less.

15. The large V-belt of claim 1 , wherein
the carbon black has an arithmetic average particle diameter of 50 μm or less.

Assignees

• Bando Chemical Ind

Inventors

• Doi Ikuhito
• Kobayashi Shogo
• NAKAHIRA Yoshihito

Classifications

• C09J115/00

  Adhesives based on rubber derivatives (C09J111/00, C09J113/00 take precedence) · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title

• C08L15/02

  Rubber derivatives containing halogen · CPC title

• F16G5/06 Primary

  with reinforcement bonded by the rubber · CPC title

• F16G5/08 Primary

  with textile reinforcement · CPC title