Method for preparing graft copolymer complex, graft copolymer complex, and thermoplastic resin composition comprising graft copolymer complex

Patent metadata

Field	Value
Publication number	US-11312852-B2
Application number	US-201816463830-A
Country	US
Kind code	B2
Filing date	Oct 2, 2018
Priority date	Oct 18, 2017
Publication date	Apr 26, 2022
Grant date	Apr 26, 2022

Abstract

The present invention relates to a method for preparing a graft copolymer complex, a copolymer complex prepared by the method, and a thermoplastic resin composition comprising the copolymer complex, wherein the method comprises emulsion-polymerizing a conjugated diene-based polymer, an aromatic vinyl-based monomer, and an alkyl (meth)acrylate-based monomer to prepare a graft copolymer latex; and adding an imidazole-based ionic compound to the graft copolymer latex and coagulating the same.

First claim

The invention claimed is:

1. A method for preparing a graft copolymer complex, the method comprising:
emulsion-polymerizing a conjugated diene-based polymer, an aromatic vinyl-based monomer, and an alkyl (meth)acrylate-based monomer to prepare a graft copolymer latex; and
adding an imidazole-based ionic compound to the graft copolymer latex and coagulating the same,
wherein the imidazole-based ionic compound is added in an amount of 1.0 to 7.0 parts by weight based on 100 parts by weight of the graft copolymer latex.

2. The method of claim 1 , wherein the imidazole-based ionic compound is added in an amount of 2.0 to 5.0 parts by weight based on 100 parts by weight of the graft copolymer latex.

3. The method of 1 , wherein the imidazole-based ionic compound is one or more selected from the group consisting of 1-butyl-3-methylimidazolium chloride and 1-hexyl-3-methylimidazolium chloride.

4. The method of claim 1 , wherein the coagulation is performed at 93 to 97° C. for 5 to 20 minutes.

5. The method of claim 1 , wherein, after the coagulation, an aging process is further performed at 95 to 100° C. for 10 to 30 minutes.

6. The method of claim 1 , wherein 20 to 70% by weight of the conjugated diene-based polymer, 7 to 30% by weight of the aromatic vinyl-based monomer, and 20 to 60% by weight of the alkyl (meth)acrylate-based monomer are emulsion-polymerized based on a total weight of the conjugated diene-based polymer and the monomers.

7. The method of claim 1 , wherein, during the emulsion polymerization, an α,β-unsaturated nitrile-based monomer is further added.

8. A graft copolymer complex, comprising:
a graft copolymer comprising a conjugated diene-based polymer and units derived from an aromatic vinyl-based monomer and units derived from an alkyl (meth)acrylate-based monomer graft-polymerized with the conjugated diene-based polymer; and
a compound derived from an imidazole-based ionic compound,
wherein the compound derived from the imidazole-based ionic compound is present in an amount of 1 to 7 parts by weight based on 100 parts by weight of the graft copolymer.

9. The graft copolymer complex of claim 8 , wherein the compound derived from the imidazole-based ionic compound is present in an amount of 2.0 to 5.0 parts by weight based on 100 parts by weight of the graft copolymer.

10. The graft copolymer complex of claim 8 , wherein the compound derived from the imidazole-based ionic compound is derived from one or more selected from the group consisting of 1-butyl-3-methylimidazolium chloride and 1-hexyl-3-methylimidazolium chloride.

11. The graft copolymer complex of claim 8 , wherein 20 to 70% by weight of the conjugated diene-based polymer, 7 to 30% by weight of units derived from the aromatic vinyl-based monomer and 20 to 60% by weight of units derived from the alkyl (meth)acrylate-based monomer are comprised based on a total weight of the graft polymer.

12. The graft copolymer complex of claim 8 , wherein units derived from an α,β-unsaturated nitrile-based monomer is further graft-copolymerized onto the conjugated diene-based polymer.

13. A thermoplastic resin composition, comprising the graft copolymer complex according to claim 8 ; and a copolymer comprising units derived from an alkyl (meth)acrylate, units derived from an aromatic vinyl-based monomer, and units derived from an α,β-unsaturated nitrile-based monomer.

14. A method for preparing a graft copolymer complex, the method comprising:
emulsion-polymerizing a conjugated diene-based polymer, an aromatic vinyl-based monomer, and an alkyl (meth)acrylate-based monomer to prepare a graft copolymer latex; and
adding an imidazole-based ionic compound to the graft copolymer latex and coagulating the same,
wherein the coagulation is performed at 93 to 97° C. for 5 to 20 minutes.

Assignees

• Lg Chemical Ltd

Inventors

• Park Sang Hoo
• Jang Seok Goo
• Ok Hye Jeong
• Kim Ho Hoon
• Shim Hyung Seop
• Choi Jeong Su
• Yoo Keun Hoon
• Lee Won Seok
• Lee Roo Da
• Lee Jong Ju

Classifications

• C08F2/06 Primary

  Organic solvent · CPC title

• C08F2/26

  anionic · CPC title

• C08F6/22

  Coagulation · CPC title

• C08K5/3445

  Five-membered rings · CPC title

• C08L33/064 Primary

  containing anhydride, COOH or COOM groups, with M being metal or onium-cation · CPC title