Glass-based articles with improved stress profiles

Patent metadata

Field	Value
Publication number	US-11312657-B2
Application number	US-201916458583-A
Country	US
Kind code	B2
Filing date	Jul 1, 2019
Priority date	Jul 2, 2018
Publication date	Apr 26, 2022
Grant date	Apr 26, 2022

Abstract

Glass-based articles are manufactured by a unique ion exchange process that results in glass-based articles having improved stress profiles with higher stress values at moderate depths. A medium of the ion exchange process includes ions of two or more alkali metals of two or more alkali metal oxides in a base composition of a glass-based substrate in a ratio such that ions of each alkali metal are in chemical equilibrium with each of the respective alkali metals of the alkali metal oxides in the base glass composition.

First claim

What is claimed is:

1. A glass-based article comprising:
opposing first and second surfaces defining a thickness (t);
a central composition at the center of the glass-based article containing two alkali metal oxides;
a surface concentration of each of the two alkali metal oxides being non-zero at one or both of the first and second surfaces; and
a metal oxide, different from the two alkali metal oxides of the central composition, having a non-zero concentration that varies from the first surface to a depth of layer (DOL) with respect to the metal oxide;
wherein at a depth of about three times the DOL, a molar concentration of each of the two alkali metal oxides in the glass-based article is ±5% of a respective molar concentration of each of the two alkali metal oxides in the central composition of the glass-based article.

2. The glass-based article of claim 1 , wherein the glass-based article comprises an alkali-aluminosilicate, an alkali-containing borosilicate, an alkali-containing aluminoborosilicate, or an alkali-containing phosphosilicate.

3. The glass-based article of claim 1 , wherein the central composition comprises 1 mol % or less of the metal oxide different from the two alkali metal oxides of the central composition.

4. The glass-based article of claim 1 , wherein the metal oxide different from the two alkali metal oxides of the central composition is selected from the group consisting of: lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), francium (Fr), silver (Ag), gold (Au), copper (Cu), and combinations thereof.

5. The glass-based article of claim 1 , wherein the two alkali metal oxides of the central composition comprise lithium and sodium, and the metal oxide different from the two alkali metal oxides of the central composition is potassium.

6. A consumer electronic product comprising:
a housing having a front surface, a back surface, and side surfaces;
electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and
a cover disposed over the display;
wherein at least a portion of at least one of the housing and the cover comprises the glass-based article of one of claim 1 .

7. A glass-based article comprising:
opposing first and second surfaces defining a thickness (t);
a central composition at the center of the glass-based article containing two alkali metal oxides;
a surface concentration of each of the two alkali metal oxides being non-zero at one or both of the first and second surfaces;
a metal oxide, different from the two alkali metal oxides of the central composition, having a non-zero concentration that varies from the first and second surfaces to a depth of layer (DOL) of the metal oxide; and
a stress profile comprising:
a depth of compression (DOC) that is greater than or equal to 0.13·t;
a spike region extending from the first surface to a transition region;
the transition region extending to a tail region; and
the tail region extending to a center of the glass-based article;

wherein the transition region comprises a first compressive stress at greater than or equal to about 0.00625·t depth from the first surface of at least about 150 MPa, and a second compressive stress at greater than or equal to about 0.025·t depth from the first surface of at least about 120 MPa; and
at a depth of 20 micrometers or more a concentration of the metal oxide different from the two alkali metal oxides of the central composition is 0.3% by weight or more of all alkali metals in the glass-based article.

8. The glass-based article of claim 7 , wherein the first compressive stress is located between about 5 and 10 micrometers depth from the first surface and is in the range of about 150 MPa to about 300 MPa, and the second compressive stress is located between about 15 and 20 micrometers depth from the first surface and is in the range of about 120 MPa to about 240 MPa.

9. The glass-based article of claim 7 , wherein the glass-based article comprises an alkali-aluminosilicate, an alkali-containing borosilicate, an alkali-containing aluminoborosilicate, or an alkali-containing phosphosilicate.

10. The glass-based article of claim 7 , wherein the central composition comprises 1 mol % or less of the metal oxide different from the two alkali metal oxides of the central composition.

11. The glass-based article of claim 7 , wherein the metal oxide different from the two alkali metal oxides of the central composition is selected from the group consisting of: lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), francium (Fr), silver (Ag), gold (Au), copper (Cu), and combinations thereof.

12. The glass-based article of claim 7 , wherein all points of the stress profile located in the spike region comprise a tangent having an absolute value that is 20 MPa/micrometer or greater.

13. The glass-based article of claim 7 , wherein the two alkali metal oxides of the central composition comprise lithium and sodium, and the metal oxide different from the two alkali metal oxides of the central composition is potassium.

14. A glass-based article comprising:
opposing first and second surfaces defining a thickness (t);
a central composition at the center of the glass-based article containing lithium and one or more additional alkali metal oxides;
a surface concentration of each of the lithium and the one or more additional alkali metal oxides being non-zero at one or both of the first and second surfaces;
a metal oxide, different from lithium and the one or more additional alkali metal oxides of the central composition, having a non-zero concentration that varies from the first and second surfaces to a depth of layer (DOL) of the metal oxide;
a depth of compression (DOC) that is greater than or equal to about 0.13·t; and
a first compressive stress at from about 5 micrometers to 10 micrometers depth from the first surface is at least 150 MPa, and a second compressive stress at from about 15 micrometers to about 20 micrometers depth from the first surface is at least 120 MPa;
wherein at a depth of 20 micrometers or more a concentration of the metal oxide different from the lithium and the one or more additional alkali metal oxides of the central composition is 0.3% by weight or more of all alkali metals in the glass-based article.

15. The glass-based article of claim 14 , wherein the glass-based article comprises an alkali-aluminosilicate, an alkali-containing borosilicate, an alkali-containing aluminoborosilicate, or an alkali-containing phosphosilicate.

16. The glass-based article of claim 14 , wherein the central composition comprises 1 mol % or less of the metal oxide different from the lithium and the one or more additional alkali metal oxides of the central composition.

17. The glass-based article of claim 14 , wherein the metal oxide different from the lithium and the one or more additional alkali metal oxides of the central composition is selected from the group consisting of: sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), francium (Fr), silver (Ag), gold (Au), copper (Cu), and combinations thereof.

18. The glass-based article of claim 14 , wherein at a depth of 3 to 10 micrometers or more a concentration of the metal oxide different from the lithium and the one or more additional alkali metal oxides of the central composition is 5% by weight or more of all alkali metals in the glass-based article.

Assignees

• Corning Inc

Inventors

• Schneider Vitor Marino

Classifications

• C03C21/002 Primary

  to perform ion-exchange between alkali ions (C03C21/005 takes precedence) · CPC title

• C03C2201/50

  containing alkali metals · CPC title

• C03C3/097

  containing phosphorus, niobium or tantalum · CPC title

• C03C2204/00

  Glasses, glazes or enamels with special properties · CPC title

• C03C3/091

  containing aluminium · CPC title