Bitumen solid at ambient temperature

Patent metadata

Field	Value
Publication number	US-11292913-B2
Application number	US-201816606943-A
Country	US
Kind code	B2
Filing date	Apr 18, 2018
Priority date	Apr 21, 2017
Publication date	Apr 5, 2022
Grant date	Apr 5, 2022

Abstract

Granules of material usable as a road binder or as a sealing binder including a core and a coating layer, wherein: the core consists of a first composition including at least one material selected from: a bitumen base, a pitch, a clear binder, and the coating layer consists of a second composition which includes: at least one viscosifying compound selected from cellulose ethers, and at least one anticaking agent. Also, a method for producing granules of material that can be used as a road binder or as a sealing binder, and the use thereof as a road binder, in particular for the production of coated materials. Also, a method for producing coatings from granules of material that can be used as a road binder or as a sealing binder and to a method for transporting and/or storing and/or handling granules.

First claim

The invention claimed is:

1. Pellets of material that can be used as a road binder or as a sealing binder, comprising a core and a coating layer, wherein:
the core consists of a first composition comprising at least one material selected from the group consisting of: a bitumen base, a pitch and a clear binder, and
the coating layer consists of a second composition which comprises, relative to the total weight of the coating layer:
from 10% to 90% by weight of at least one viscosifying compound, selected from the group consisting of cellulose ethers, and
from 10% to 90% by weight of at least one anticaking agent, which is siliceous fines.

2. The pellets as claimed in claim 1 , wherein the cellulose ether is selected from the group consisting of: methylcellulose, ethylcellulose, hydroxymethylcellulose, hydroxyethylcellulose (HEC), hydroxypropylcellulose (HPC), hydroxyethylmethylcellulose (HEMC), hydroxypropylmethylcellulose (HPMC), hydroxybutylmethylcellulose (HBMC), carboxymethylcellulose (CMC), sodium carboxymethylcellulose (Na-CMC), carboxymethylsulfoethylcellulose, and hydroxyethylmethylcarboxymethylcellulose.

3. The pellets as claimed in claim 2 , wherein the cellulose ether is selected from the group consisting of: hydroxyethylmethylcellulose, hydroxypropylmethylcellulose and hydroxybutylmethylcellulose.

4. The pellets as claimed in claim 3 , wherein the cellulose ether is hydroxypropylmethylcellulose.

5. The pellets as claimed in claim 1 , wherein the first composition has a needle penetrability measured at 25° C. according to the standard EN 1426 of from 5 to 330 1/10 mm.

6. The pellets as claimed in claim 5 , wherein the first composition has a needle penetrability measured at 25° C. according to the standard EN 1426 of from 10 to 220 1/10 mm.

7. The pellets as claimed in claim 1 , wherein the first composition also comprises at least one chemical additive selected from the group consisting of: an organic compound, a paraffin, a polyphosphoric acid, an adhesion dopant, and mixtures thereof.

8. The pellets as claimed in claim 1 , wherein the coating layer is solid at a temperature greater than 60° C.

9. The pellets as claimed in claim 1 , wherein the coating layer has an average thickness greater than or equal to 20 μm.

10. A process for manufacturing pellets of material that can be used as a road binder or as a sealing binder, composed of a core and a core coating layer as claimed in claim 1 , this process comprising:
i) shaping the core from a first composition comprising at least one material selected from the group consisting of: a bitumen base, a pitch and a clear binder,
ii) coating the core on all or part of its surface with a second composition comprising (a) at least one viscosifying compound selected from the group consisting of cellulose ethers and (b) at least one anticaking agent.

11. The process as claimed in claim 10 , wherein the second composition is applied to the core of the pellets in a fluidized air bed device.

12. The pellets as claimed in claim 1 , which show stability on transportation or storage or handling at a temperature ranging from 20° C. to 100° C., for a period of greater than or equal to 2 months.

13. The pellets as claimed in claim 1 , which show stability on transportation or storage or handling at a temperature ranging from 20° C. to 80° C. for a period of greater than or equal to 3 months.

14. The pellets as claimed in claim 1 , which have a weight of between 0.1 g and 50 g.

15. A process for manufacturing bituminous mixes comprising at least one road binder and aggregates, the road binder being chosen from the pellets as claimed in claim 1 , this process comprising at least the steps of:
heating the aggregates to a temperature ranging from 100° C. to 180° C.,
mixing the aggregates with the road binder in a tank,
obtaining bituminous mixes.

16. The process as claimed in claim 15 wherein the process comprises the step of heating the aggregates to a temperature ranging from 120° C. to 160° C.

17. The process as claimed in claim 15 , which does not comprise a step of heating the road binder before it is mixed with the aggregates.

18. The process as claimed in claim 15 , wherein the step of mixing the aggregates with the road binder is performed with stirring, and stirring is then maintained for not more than 5 minutes.

Assignees

• Total Marketing Services

Inventors

• Colliat Romain
• Hung Yvong

Classifications

• E01C7/18

  of road-metal and bituminous binders {(for surface treatments except for penetration coverings, or for thin surface layers E01C7/353; bituminous mixtures C08L95/00)} · CPC title

• C08L1/284

  with hydroxylated hydrocarbon radicals · CPC title

• C10C3/14 Primary

  Solidifying, Disintegrating, e.g. granulating · CPC title

• C08L95/00 Primary

  Compositions of bituminous materials, e.g. asphalt, tar, pitch · CPC title

• C09D101/284

  with hydroxylated hydrocarbon radicals · CPC title