Monochromatic dental shaped article and blank for making dental restorations

Patent metadata

Field	Value
Publication number	US-11278381-B2
Application number	US-201816487360-A
Country	US
Kind code	B2
Filing date	Mar 15, 2018
Priority date	Mar 17, 2017
Publication date	Mar 22, 2022
Grant date	Mar 22, 2022

Abstract

Monochromatic dental shaped body, which has an opacity of from 70 to 78%, and a process for its production.

First claim

The invention claimed is:

1. Monochromatic dental shaped body comprising
a polymerized resin matrix,
a thickener comprising uncrosslinked polymer particles, and
at least one organic filler comprising crosslinked polymer particles having an average particle size (d50 value) of from 20 to 100 μm,
wherein the monochromatic dental shaped body has an opacity of from 72 to 76% and a color, determined according to the L*a*b color model corresponding to DIN EN ISO 11664-4, defined by an L value within the range of 75.5 to 86.0, an a value within the range of 3.4 to 9.5 and a b value within the range of 15.5 to 32.0, and wherein the monochromatic dental shaped body does neither contain inorganic filler nor organic-inorganic filler (composite filler) and does not have a layer structure.

2. Shaped body according to claim 1 ,
wherein the opacity is from 73 to 75%.

3. Shaped body according to claim 1 ,
wherein the polymeric resin matrix is formed by polymerization of a monomer or a mixture of monomers which is/are selected from monofunctional monomers, polyfunctional monomers or a mixture of mono- and polyfunctional monomers.

4. Shaped body according to claim 3 ,
wherein the monofunctional monomer(s) is/are selected from methyl methacrylate, ethyl methacrylate, 2-hydroxyethyl methacrylate, butyl methacrylate, benzyl methacrylate, tetrahydrofurfuryl methacrylate, isobornyl methacrylate, p-cumyl-phenoxyethylene glycol methacrylate (CMP-1E) and acetoxyacetylethyl methacrylate (AAEMA).

5. Shaped body according to claim 3 ,
wherein the polyfunctional monomer(s) is/are selected from bisphenol A dimethacrylate, 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropyl)phenyl]propane (bis-GMA; an addition product of methacrylic acid and bisphenol A diglycidyl ether), eth-oxy- or propoxylated bisphenol A dimethacrylate, 2-[4-(2-methacryloyloxyethoxy-ethoxy)phenyl]-2-[4-(2-methacryloyloxyethoxy)phenyl]propane), 2,2-bis[4-(2-meth-acryloxypropoxy)phenyl]propane, 1,6-bis-[2-methacryloyloxyethoxycarbonylamino]-2,2,4-trimethylhexane (UDMA; an addition product of 2-hydroxyethyl methacrylate and 2,2,4-trimethylhexamethylene diisocyanate), TMX-UDMA (an addition product of a mixture of HEMA and hydroxypropyl methacrylate (HPMA) with α,α,α′, α′-tetramethyl-m-xylylene diisocyanate (TMXDI)), di-, tri- or tetraethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetramethacrylate, glycerol di- or trimethacrylate, 1,4-butanediol dimethacrylate, 1,10-decanediol dimethacrylate (D 3 MA), 1,12-dodecanediol dimethacrylate and bis(3-methacryloyloxymethyl)tricyclo-[5.2.1.0 2,6 ]decane (DCP).

6. Shaped body according to claim 3 ,
wherein the polymeric resin matrix is formed by polymerization of a mixture of
methyl methacrylate,
at least one of UDMA and TMX-UDMA, and
ethylene glycol dimethacrylate.

7. Shaped body according to claim 1 ,
wherein the organic filler has a lower opacity than the resin matrix.

8. Shaped body according to claim 1 ,
wherein the thickener has an average particle size of from 10 to 60 μm and the at least one organic filler has an average particle size of from 20 to 60 μm.

9. Process of manufacturing the monochromatic shaped body of claim 1 for use as a blank for the production of dental restorations, which comprises curing the following mixture:
(1) 1 to 20 wt.-% polyfunctional radically polymerizable monomer(s),
(2) 10 to 60 wt.-% monofunctional radically polymerizable monomer(s),
(3) 0.01 to 5.0 wt.-% initiator for the radical polymerization,
(4) 20 to 70 wt.-% thickener comprising uncrosslinked polymer particles,
(5) 5 to 50 wt.-% organic filler comprising crosslinked polymer particles having an average particle size (d50 value) of from 20 to 100 μm, and optionally
(6) 0.1 to 5.0 wt.-% further additive(s), in each case relative to the total mass of the mixture, wherein the mixture does not contain inorganic filler and organic-inorganic filler (composite filler).

10. Process according to claim 9 , which comprises curing the following mixture:
(1) 2 to 10 wt.-% polyfunctional radically polymerizable monomer(s),
(2) 5 to 50 wt.-% monofunctional radically polymerizable monomer(s),
(3) 0.1 to 3.0 wt.-% initiator for the radical polymerization,
(4) 30 to 60 wt.-% thickener,
(5) 10 to 40 wt.-% organic filler and optionally
(6) 0.1 to 2.0 wt.-% further additive(s), in each case relative to the total mass of the mixture.

11. Process according to claim 9 , which comprises curing the following mixture:
(1) 3 to 8 wt.-% polyfunctional radically polymerizable monomer(s),
(2) 10 to 45 wt.-% monofunctional radically polymerizable monomer(s),
(3) 0.1 to 2.0 wt.-% initiator for the radical polymerization,
(4) 35 to 55 wt.-% thickener,
(5) 15 to 35 wt.-% organic filler and optionally
(6) 0.2 to 1.5 wt.-% further additive(s), in each case relative to the total mass of the mixture.

12. Shaped body according to claim 1 , further comprising at least one pigment as colorant.

13. Shaped body according to claim 12 , which contains 0.0002 to 1.0 wt.-% of at least one pigment, relative to the total mass of the shaped body.

14. Process of using the shaped body according to claim 1 for the production of artificial teeth or tooth segments.

15. Process according to claim 14 ,
wherein the artificial teeth or the tooth segments are produced by a cutting process.

16. Process according to claim 15 ,
wherein the artificial teeth or the tooth segments are produced by a CAD/CAM process.

17. Process for the production of a shaped body according to claim 1 , wherein
(a) a polymerizable mixture is provided, which contains radically and/or cationically polymerizable resin, the organic filler, the thickener and initiator for the radical and/or cationic polymerization,
(b) the mixture is coloured by the addition of colorants,
(c) the opacity of the mixture is optionally adjusted by the addition of pigment(s), and
(d) the mixture is shaped to form a shaped body and
(e) cured by radical and/or cationic polymerization.

18. Process according to claim 17 ,
wherein, in step (c), the opacity is adjusted by addition of TiO 2 white.

19. Process according to claim 17 ,
wherein the shaped body is shaped in step (d) by introducing the mixture into a casting mould by injection moulding followed by curing.

20. Process of manufacturing the monochromatic dental shaped body of claim 1 for use as a blank for the production of dental restorations, which comprises curing the following mixture:
(1) 15 to 70 wt.-% mono- and/or polyfunctional radically polymerizable monomer(s),
(2) 0.01 to 5.0 wt.-% photoinitiator for the radical, cationic or combined polymerization,
(3) 5 to 90 wt.-% organic filler(s) comprising crosslinked polymer particles having an average particle size (d50 value) of from 20 to 100 μm,
(4) a thickener comprising uncrosslinked polymer particles and optionally
(5) 0.1 to 5.0 wt.-% further additive(s), in each case relative to the total mass of the mixture, wherein the mixture does not contain inorganic filler and organic-inorganic filler (composite filler).

21. Process of manufacturing a dental restoration, comprising:
producing the monochromatic dental shaped body of claim 1 having the form of a blank for the production of a dental restoration, and
shaping the blank to a dental restoration by a cutting process.

Assignees

• Ivoclar Vivadent Ag

Inventors

• Hagenbuch Konrad
• Kerschbaumer Harald
• Gurschler Konrad
• Häfele Clemens Andreas
• Baaske Thomas

Classifications

• A61C2201/002

  using colour effect, e.g. for identification purposes · CPC title

• A61C13/0022

  Blanks or green, unfinished dental restoration parts · CPC title

• A61C13/082 Primary

  Cosmetic aspects, e.g. inlays; Determination of the colour (A61C19/10 takes precedence) · CPC title

• A61K6/887

  Compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• A61C13/0004

  Computer-assisted sizing or machining of dental prostheses · CPC title