Fabrication of hydroxyapatite based hybrid sorbent media for removal of fluoride and other contaminants

Patent metadata

Field	Value
Publication number	US-11273427-B2
Application number	US-201916547998-A
Country	US
Kind code	B2
Filing date	Aug 22, 2019
Priority date	Aug 22, 2018
Publication date	Mar 15, 2022
Grant date	Mar 15, 2022

Abstract

Fabricating a hybrid sorbent media includes contacting a porous material with a first aqueous solution including phosphate ions to yield a first mixture, contacting the first mixture with a second aqueous solution comprising calcium ions to yield a second mixture, and adjusting a pH of the second mixture to form hydroxyapatite inside the porous media to yield the hybrid sorbent media.

First claim

What is claimed is:

1. A method of fabricating hybrid sorbent media, the method comprising:
contacting porous media defining pores with a first aqueous solution comprising phosphate ions to yield a first mixture;
contacting the first mixture with a second aqueous solution comprising calcium ions to yield a second mixture; and
adjusting a pH of the second mixture to initiate formation of hydroxyapatite on pore surfaces of the pores of the porous media to yield the hybrid sorbent media,
wherein the porous media is an ion-exchange resin, and contacting the porous media with the first aqueous solution, contacting the first mixture with the second aqueous solution, and adjusting the pH of the second mixture occur at room temperature.

2. The method of claim 1 , further comprising removing some of the first aqueous solution from the first mixture before contacting the first mixture with the second aqueous solution.

3. The method of claim 1 , further comprising aging the hybrid sorbent media to allow growth of hydroxyapatite nanoparticles inside the pores of the porous media.

4. The method of claim 3 , wherein aging comprises aging at room temperature for at least 24 hours.

5. The method of claim 1 , wherein the first aqueous solution comprises diammonium hydrogen phosphate, ammonium dihydrogen phosphate, di-sodium hydrogen phosphate, triethyl phosphate, phosphorus pentoxide, phosphoric acid, phosphonoacetic acid, or a combination thereof.

6. The method of claim 1 , wherein a volume ratio of the first aqueous solution to the porous media is about 2:1.

7. The method of claim 1 , wherein the first aqueous solution is saturated with phosphate at room temperature.

8. The method of claim 1 , wherein contacting the porous media with the first aqueous solution occurs for at least about 24 hours.

9. The method of claim 1 , wherein the second aqueous solution comprises calcium chloride dihydrate, calcium nitrate, calcium hydroxide, calcium acetate, or a combination thereof.

10. The method of claim 1 , wherein contacting the first mixture with the second aqueous solution occurs for at least about 24 hours.

11. The method of claim 1 , wherein adjusting the pH of the second mixture comprises adjusting the pH to an alkaline pH.

12. The method of claim 11 , wherein the alkaline pH is in a range of about 10 to about 12.

13. The method of claim 11 , wherein adjusting the pH of the second mixture comprises combining a basic solution with the second mixture, wherein the basic solution comprises ammonium hydroxide, sodium hydroxide, urea, or a combination thereof.

14. The method of claim 1 , wherein the hybrid sorbent media comprises at least 30 wt % hydroxyapatite per dry weight of the hybrid sorbent media.

15. The method of claim 14 , wherein the hybrid sorbent media is configured to remove fluoride from an aqueous solution.

16. The method of claim 15 , wherein the hybrid sorbent media is further configured to remove nitrate from the aqueous solution.

17. The method of claim 1 , wherein the hydroxyapatite nanoparticles are in the form of needles having a length up to about 100 nm.

Assignees

• Markovski Jasmina
• Hristovski Kiril D
• Univ Arizona State

Inventors

• Markovski Jasmina
• Hristovski Kiril D

Classifications

• B01J20/26

  Synthetic macromolecular compounds · CPC title

• C02F1/288

  using composite sorbents, e.g. coated, impregnated, multi-layered · CPC title

• B01J20/048 Primary

  containing phosphorus, e.g. phosphates, apatites, hydroxyapatites · CPC title

• B01J20/28026

  Particles within, immobilised, dispersed, entrapped in or on a matrix, e.g. a resin · CPC title

• B01J20/3085

  Chemical treatments not covered by groups B01J20/3007 - B01J20/3078 · CPC title