Friction-activated adhesive formulations and application devices

Patent metadata

Field	Value
Publication number	US-11267997-B2
Application number	US-202016779709-A
Country	US
Kind code	B2
Filing date	Feb 3, 2020
Priority date	Dec 16, 2013
Publication date	Mar 8, 2022
Grant date	Mar 8, 2022

Abstract

A solid thermoplastic semi-crystalline friction-activated adhesive composition comprising the mixture of:
(a) from about 50 to about 100 parts by weight of a semi-crystalline adhesive polymer that comprises:
(1) crystalline monomer having an alkyl carbon length of at least 16 carbon atoms; (2) non-crystalline monomer having a homopolymer T g below about 80° C.; (3) waxy, soft monomer having an average pendant alkyl carbon length of at least 14 carbon atoms; (4) monomer having acid or base functionality; (5) functional or non-functional macromere having a T m from about 40 to about 120° C.;
(b) 0 to about 50 parts by weight of tackifier; (c) 0 to about 50 parts by weight of crystalline additive; (d) 0 to about 50 parts by weight of filler; (e) 0 to about 30 parts by weight of oil; and (f) 0 to about 50 parts by weight of one surfactant.

Also glue crayons and other application devices comprising such adhesive compositions.

First claim

What is claimed is:

1. A friction-activated adhesive composition comprising:
(a) from about 50 to about 100 parts by weight of a copolymer comprising the reaction product of the following monomers:
(i) about 5 to about 96 parts by weight per 100 parts by weight of a C n (meth)acrylic monomer having a pendant alkyl unit of at least 16 carbon atoms, wherein a homopolymer of the (meth)acrylic monomer having a pendant alkyl unit of at least 16 carbon atoms has a melting temperature of about 45° C. to about 68° C.,
(ii) about 12 to about 59 parts by weight per 100 parts by weight of a non-crystalline C n (meth)acrylic monomer, wherein a homopolymer of the non-crystalline C n (meth)acrylic monomer has a glass transition temperature of about 40° C. or less,
(iii) a waxy, soft C n (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms, wherein a homopolymer of the waxy, soft C n (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms has a melting temperature of about 25° C. to about 44° C., and
(iv) from about 0.5 to about 3 parts by weight per 100 parts by weight of an acidic comonomer comprising a carboxylic acid comprising from 3 to 12 carbon atoms and having from 1 to 4 carboxylic acid moieties; and

(b) a tackifier.

2. The friction-activated adhesive composition of claim 1 , wherein
the waxy, soft Cn (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms is present in the copolymer in an amount no more than 70 parts by weight per 100 parts.

3. The friction-activated adhesive composition of claim 1 , further comprising
(c) a macromer having a melting temperature of about 35° C. to about 70° C.

4. The composition of claim 3 , wherein the macromer is the reaction product of one or more prepolymers of octadecyl acrylate, behenyl acrylate, tetradecyl acrylate, hexadecyl methacrylate, octadecyl methacrylate, eicosyl acrylate, eicosyl methacrylate, and behenyl methacrylate.

5. The friction-activated adhesive composition of claim 1 , further comprising
(d) a crystalline additive.

6. The friction-activated adhesive composition of claim 5 , wherein the amount of crystalline additive is about 3% to about 50% by weight of the composition.

7. The friction-activated adhesive composition of claim 5 , wherein the crystalline additive comprises an alcohol with an n-alkyl chain length of at least 22 carbon atoms.

8. The friction-activated adhesive composition of claim 7 , wherein the crystalline additive has a melting point of about 50° C. or greater.

9. The friction-activated adhesive composition of claim 1 , wherein the composition comprises about 5 to about 40 parts by weight tackifier per 100 parts by weight of the adhesive composition.

10. The friction-activated adhesive composition of claim 1 , further comprising a surfactant.

11. The friction-activated adhesive composition of claim 1 , further comprising an oil.

12. A friction-activated adhesive application device comprising
an adhesive crayon comprising the composition of claim 1 ; and
a removable wrapper.

13. A method of using the friction-activated adhesive application device of claim 1 comprising rubbing the crayon onto a substrate to form a tacky adhesive deposit on the substrate.

14. The friction-activated adhesive composition of claim 1 , wherein the acidic comonomer comprises one or both of acrylic acid and methacrylic acid.

15. The friction-activated adhesive composition of claim 1 , wherein the friction-activated adhesive composition has a melting temperature above room temperature, resists flowing at temperatures up to about 50° C., and is melted by frictionally generated heat when formed into a crayon and rubbed on a substrate.

16. A friction-activated adhesive composition comprising:
(a) from about 50 to about 100 parts by weight of a copolymer comprising the reaction product of the following monomers
(i) about 5 to about 96 parts by weight per 100 parts by weight of a C n (meth)acrylic monomer having a pendant alkyl unit of at least 16 carbon atoms, wherein a homopolymer of the (meth)acrylic monomer having a pendant alkyl unit of at least 16 carbon atoms has a melting temperature of about 45° C. to about 68° C.,
(ii) about 12 to about 59 parts by weight per 100 parts by weight of a non-crystalline C n (meth)acrylic monomer, wherein a homopolymer of the non-crystalline C n (meth)acrylic monomer has a glass transition temperature of about 40° C. or less, and
(iii) a waxy, soft C n (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms, wherein a homopolymer of the waxy, soft C n (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms has a melting temperature of about 25° C. to about 44° C.;

(b) at least one tackifier, wherein the tackifier is present in an amount up to 50 parts by weight;
(c) 0 to about 50 parts by weight of at least one crystalline additive;
(d) 0 to about 30 parts by weight of at least one oil; and
(e) 0 to about 50 parts by weight of at least one surfactant.

17. The friction-activated adhesive composition of claim 16 , wherein
the waxy, soft Cn (meth)acrylic monomer having a pendant alkyl unit of at least 14 carbon atoms is present in the copolymer in an amount no more than 70 parts by weight per 100 parts.

18. The friction-activated adhesive composition of claim 16 , further comprising
(d) a macromer having a glass transition temperature of about 35° C. to about 70° C.

19. The composition of claim 18 , wherein the macromer is the reaction product of one or more prepolymers of octadecyl acrylate, behenyl acrylate, tetradecyl acrylate, hexadecyl methacrylate, octadecyl methacrylate, eicosyl acrylate, eicosyl methacrylate, and behenyl methacrylate.

20. The friction-activated adhesive composition of claim 16 , further comprising
(f) a crystalline additive.

21. The friction-activated adhesive composition of claim 16 , wherein the amount of the at least one crystalline additive is about 3% to about 50% by weight of the composition.

22. The friction-activated adhesive composition of claim 16 , wherein the crystalline additive comprises an alcohol with an n-alkyl chain length of at least 22 carbon atoms.

23. The friction-activated adhesive composition of claim 22 , wherein the crystalline additive has a melting point of about 50° C. or greater.

24. The friction-activated adhesive composition of claim 16 , wherein the composition comprises about 5 to about 40 parts by weight tackifier per 100 parts by weight of composition.

25. The friction-activated adhesive composition of claim 16 , further comprising a surfactant.

26. The friction-activated adhesive composition of claim 16 , further comprising an oil.

27. A friction-activated adhesive application device comprising
an adhesive crayon comprising the composition of claim 16 ; and
a removable wrapper.

28. A method of using the friction-activated adhesive application device of claim 16 comprising rubbing the crayon onto a substrate to form a tacky adhesive deposit on the substrate.

Assignees

• 3M Innovative Properties Co

Inventors

• June Stephen M
• Beveridge Nicole M
• Lu Ying-Yuh

Classifications

• C09J133/06 Primary

  of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical · CPC title

• C08F220/10

  Esters · CPC title

• C09J201/02 Primary

  characterised by the presence of specified groups {, e.g. terminal or pendant functional groups} · CPC title

• C08L33/06

  of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical · CPC title

• C09J9/005

  Glue sticks · CPC title