KR desulfurization stirring paddle casting material and preparation method therefor

Patent metadata

Field	Value
Publication number	US-11267764-B2
Application number	US-201816649395-A
Country	US
Kind code	B2
Filing date	Sep 7, 2018
Priority date	Sep 21, 2017
Publication date	Mar 8, 2022
Grant date	Mar 8, 2022

Abstract

Provided are a Kanbara Reactor (KR) desulfurization stirring paddle casting material and a preparation method therefor. The casting material consists of a base material and an additive; the base material consists of the following raw materials in weight percentages: M70 sintered mullite 60-80%, flint clay 5-20%, fine powder 5-20%, and pure calcium aluminate cement 1-5%. The percentages of each component of the additive based on the weight of the base material are as follows: water reducing agent 0.05-0.2%, and heat-resistant stainless steel fiber 1-5%. The main raw materials are M70 sintered mullite and a small amount of flint clay so as to ensure good thermal shock resistance; the medium temperature and high temperature strength are controlled at 100-180 MPa so as to ensure good erosion resistance; the content of Al2O3 in the casting material is 60-70% so as to ensure good corrosion resistance; the ratio of high temperature strength to medium temperature strength is controlled at 1-1.2, which further improves the thermal shock resistance and peeling resistance of the casting material, thereby extending the service life of the stirring paddle. The casting material is lower in cost and has a good practical furnace usage effect; in addition, a paddle blade has less chance of cracking and peeling, while a bottom portion of the stirring paddle is less eroded, thus the frequency of paddle blade repair is low, and service life is significantly improved.

First claim

What is claimed is:

1. A casting material for a stirring paddle for KR desulfurization, consisting of a base material of the casting material and additives,
wherein the base material of the casting material consists of the following ingredients by weight percentage: 60-80% of M70 sintered mullite, 5-20% of flint clay, 5-20% of micropowder, and 1-5% of pure calcium aluminate cement; and
wherein the additives consist of, by weight percentage based on the weight of the base material of the casting material: 0.05-0.2% of a water reducing agent, and 1-5% of a heat-resistant stainless steel fiber.

2. The casting material for a stirring paddle for KR desulfurization according to claim 1 , wherein the base material for the casting material has an Al 2 O 3 content of 60-70%.

3. The casting material for a stirring paddle for KR desulfurization according to claim 1 , wherein the M70 sintered mullite has an Al 2 O 3 content of 70% or more.

4. The casting material for a stirring paddle for KR desulfurization according to claim 1 , wherein the flint clay has an Al 2 O 3 content of 43% or more.

5. The casting material for a stirring paddle for KR desulfurization according to claim 1 , wherein the micropowder is a silica micropowder and/or an alumina micropowder.

6. The casting material for a stirring paddle for KR desulfurization according to claim 1 , wherein the pure calcium aluminate cement has an Al 2 O 3 content of 70% or more.

7. A method for preparing the casting material for a stirring paddle for KR desulfurization according to claim 1 comprising: weighing the base material of the casting material and the additives according to the proportions, and mixing uniformly.

8. The method according to claim 7 , wherein the base material for the casting material has an Al 2 O 3 content of 60-70%.

9. The method according to claim 7 , wherein the M70 sintered mullite has an Al 2 O 3 content of 70% or more.

10. The method according to claim 7 , wherein the flint clay has an Al 2 O 3 content of 43% or more.

11. The method according to claim 7 , wherein the micropowder is a silica micropowder and/or an alumina micropowder.

12. The method according to claim 7 , wherein the pure calcium aluminate cement has an Al 2 O 3 content of 70% or more.

Assignees

• Baoshan Iron & Steel

Inventors

• Yao Jingfu
• Gan Feifang
• Mou Jining
• Wang Tao

Classifications

• C21C1/02

  Dephosphorising or desulfurising · CPC title

• C04B2235/9676

  against molten metals such as steel or aluminium · CPC title

• C04B35/66 Primary

  Monolithic refractories or refractory mortars, including those whether or not containing clay {(making or repairing of linings F27D1/16)} · CPC title

• C04B35/76 Primary

  Fibres, filaments, whiskers, platelets, or the like · CPC title

• C04B35/185

  Mullite {3Al2O3-2SiO2} · CPC title