Optimized gamma-prime strengthened austenitic trip steel and designing methods of same

Patent metadata

Field	Value
Publication number	US-11242576-B2
Application number	US-201715483559-A
Country	US
Kind code	B2
Filing date	Apr 10, 2017
Priority date	Apr 8, 2016
Publication date	Feb 8, 2022
Grant date	Feb 8, 2022

Abstract

An optimized Gamma-prime (γ′) strengthened austenitic transformation induced plasticity (TRIP) steel comprises a composition designed and processed such that the optimized γ′ strengthened austenitic TRIP steel meets property objectives comprising a yield strength of 896 MPa (130 ksi), and an austenite stability designed to have Msσ(sh)=−40° C., wherein Msσ(sh) is a temperature for shear, and wherein the property objectives are design specifications of the optimized γ′ strengthened austenitic TRIP steel. The optimized γ′ strengthened austenitic TRIP steel is Blastalloy TRIP 130.

First claim

What is claimed is:

1. A gamma-prime (γ′) strengthened austenitic transformation induced plasticity (TRIP) steel, comprising:
a composition consisting essentially of nickel (Ni) in a range of 28.73-29.13 wt. %, titanium (Ti) in a range of 1.93-2.13 wt. %, aluminum (Al) in a range of 1.18-1.28 wt. %, chromium (Cr) in a range of 3.8-4.2 wt. %, molybdenum (Mo) in a range of 1.15-1.25 wt. %, vanadium (V) in a range of 0.2-0.4 wt. %, carbon (C) in a range of 0.005-0.015 wt. %, boron (B) in a range of 0.0075-0.0175 wt. %, and iron (Fe) in balance, the composition being processed to form the γ′ strengthened austenitic TRIP steel such that η grain boundary cellular precipitation is thermodynamically eliminated, a volume fraction and a radius of the γ′ precipitates are controlled by tempering time and temperature, and an antiphase boundary energy (APBE) is a function of the composition of the γ′ precipitates,
wherein said iron (Fe) is in a range essentially of 61.5775-62.9975 wt. %.

2. The γ′ strengthened austenitic TRIP steel of claim 1 , wherein weight fractions of Al and Ti are chosen to achieve desired strength and desired thermodynamic stability, and a weight fraction of Ni is chosen to achieve desired austenite stability.

3. The γ′ strengthened austenitic TRIP steel of claim 2 , wherein the weight fractions of Al, Ti, and Ni are chosen to be 1.23 wt. %, 2.03 wt. % and 28.93 wt. %, respectively.

4. The γ′ strengthened austenitic TRIP steel of claim 1 , wherein the tempering time is in a range of 5-120 hrs, and the temperature is in a range of 700-750° C.

5. The γ′ strengthened austenitic TRIP steel of claim 4 , wherein the tempering time is 20 hrs, and the temperature is 700° C., and wherein the γ′ strengthened austenitic TRIP steel has a yield strength of 852 MPa (123.5 ksi) and M s σ (sh) of −42° C. wherein M s σ (sh) is a temperature for shear.

6. The γ′ strengthened austenitic TRIP steel of claim 5 , wherein the γ′ strengthened austenitic TRIP steel further has a Young's Modulus of 257 GPa, an elongation of 26.5% on a 18.6 mm gauge length, an uniform elongation of 17.6%, and a true failure strain of 61.3%.

7. The γ′ strengthened austenitic TRIP steel of claim 1 , consisting essentially of 29.09 wt. % Ni, 2 wt. % Ti, 1.24 wt. % Al, 4.1 wt. % Cr, 1.22 wt. % Mo, 0.4 wt. % V, 0.013 wt. % C, 0.01 wt. % B, and Fe in balance.

Assignees

• Univ Northwestern

Inventors

• Wengrenovich Nicholas J
• Olson Gregory B

Classifications

• C22C38/54

  with boron · CPC title

• C21D7/13

  by hot working · CPC title

• C21D2211/004

  Dispersions; Precipitations · CPC title

• C21D6/004

  containing Cr and Ni · CPC title

• C22C38/06

  containing aluminium · CPC title