Composition for heat-shrinkable tube and heat-shrinkable tube manufactured therefrom

Patent metadata

Field	Value
Publication number	US-11242454-B2
Application number	US-201816771508-A
Country	US
Kind code	B2
Filing date	Oct 26, 2018
Priority date	Dec 29, 2017
Publication date	Feb 8, 2022
Grant date	Feb 8, 2022

Abstract

Provided is a composition for a heat-shrinkable tube, comprising: a base resin; and a flame retardant, wherein the base resin comprises chlorinated polyolefin resin and polyolefin elastomer, wherein the chlorinated polyolefin resin comprises chlorine in an amount of 30 to 40% by weight based on the total weight thereof, and the polyolefin elastomer has a melting point of 95 to 120° C., and an amount of the chlorinated polyolefin resin is 40 to 60 parts by weight and an amount of the polyolefin elastomer is 20 to 40 parts by weight, based on 100 parts by weight of the base resin.

First claim

The invention claimed is:

1. A composition for a heat-shrinkable tube, comprising:
a base resin; and
a flame retardant,
wherein the base resin comprises chlorinated polyolefin resin and polyolefin elastomer,
wherein the chlorinated polyolefin resin comprises chlorine in an amount of 30 to 40% by weight based on the total weight thereof and has a Mooney viscosity (ML1+4, 121° C.) of 100 or more, and the polyolefin elastomer has a melting point of 95 to 120° C. and a melt viscosity of 1 dg/min or less, and
an amount of the chlorinated polyolefin resin is 40 to 60 parts by weight and an amount of the polyolefin elastomer is 20 to 40 parts by weight, based on 100 parts by weight of the base resin.

2. The composition for a heat-shrinkable tube of claim 1 , wherein the base resin further comprises ethylene vinyl acetate (EVA).

3. The composition for a heat-shrinkable tube of claim 2 , wherein the ethylene vinyl acetate (EVA) comprises vinyl acetate (VA) in an amount of 25 to 30% by weight based on the total weight thereof.

4. The composition for a heat-shrinkable tube of claim 1 , wherein the chlorinated polyolefin resin comprises a chlorinated polyethylene resin.

5. The composition for a heat-shrinkable tube of claim 1 , wherein the flame retardant comprises magnesium hydroxide (Mg(OH) 2 ), the surface of which is treated hydrophobically.

6. The composition for a heat-shrinkable tube of claim 5 , wherein an amount of the flame retardant is 15 to 40 parts by weight, based on 100 parts by weight of the base resin.

7. The composition for a heat-shrinkable tube of claim 1 , further comprising at least another additive selected from the group consisting of a flame retardant aid, an antioxidant, a crosslinking aid, a UV inhibitor, a processing aid, a heat stabilizer, a lubricant, an anti-blocking agent, an anti-static agent, wax, a coupling agent, and a pigment.

8. The composition for a heat-shrinkable tube of claim 7 , wherein the flame retardant aid comprises an antimony-based flame retardant aid and a bromine-based flame retardant aid,
wherein an amount of the antimony-based flame retardant aid and an amount of the bromine-based flame retardant aid are each 5 to 15 parts by weight, based on 100 parts by weight of the base resin.

9. A heat-shrinkable tube manufactured from the composition for a heat-shrinkable tube according to claim 1 .

Assignees

• Ls Cable & System Ltd

Inventors

• Kim Yu Min
• Kang Min Gyu
• Kim Whan Ki
• Kim Sang Hee

Classifications

• C08L2203/202

  use in electrical wires or wirecoating · CPC title

• C08K3/016

  Flame-proofing or flame-retarding additives · CPC title

• C08F8/20

  Halogenation · CPC title

• C08L23/286 Primary

  Chlorinated polyethylene · CPC title

• C08K9/00

  Use of pretreated ingredients · CPC title